Community low-voltage grid integrated distribution box and application thereof

A low-voltage power grid and distribution box technology, which is applied to electrical components, substation/switch layout details, etc., can solve problems such as poor mechanical properties, corrosion resistance, poor thermal conductivity, inability to discharge heat, and poor insulation performance, so as to improve resin Compatibility, reduced electrical conductivity, enhanced thermal stability and corrosion resistance effects

Inactive Publication Date: 2016-08-24
JUNAN POWER SUPPLY CO OF STATE GRID SHANDONG ELECTRIC POWER CO +1
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this kind of distribution box is that the insulation performance is not good, and it will cause serious safety hazards when the line is short-circuited, and the product is relatively heavy and inconvenient to install.
In recent years, plastic distribution box shells have been developed, which have good insulation properties and are light in weight, but have poor mechanical properties, corrosion resistance and thermal conductivity, and cannot withstand large impact forces, nor can they be placed in the distribution box. Discharge of the heat generated during power-on may easily cause high temperature in the distribution box and bring potential safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Community low-voltage grid integrated distribution box and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The community low-voltage power grid integrated distribution box, which includes a box body, and the box body is prepared from the following raw materials:

[0021] Perlite, sepiolite, borax, dolomite, brucite, activator, alumina, serine, methacryloxypropyltrimethoxysilane, polypropylene resin, graphite, nano silicon carbide, polyolefin elastomer body, polycarbonate, polyvinyl alcohol, isopropyl palmitate, tributyl phosphate, talc.

[0022] The box is prepared according to the following process:

[0023] 1) Add perlite and sepiolite to the crusher according to the mass ratio of 2:1 for crushing, and then grind to obtain a powder with a particle size of 200 mesh, which is the mixture A;

[0024] 2) Mix borax, dolomite, brucite and active agent evenly according to the mass ratio of 100:50:30:1, put them into the ball mill tank, the ball mill time is 6 hours, the ball mill speed is 800 rpm, and ball mill to powder The particle size is 200 mesh, and the mixture B is obtai...

Embodiment 2

[0030] The community low-voltage power grid integrated distribution box, which includes a box body, and the box body is prepared from the following raw materials:

[0031] Perlite, sepiolite, borax, dolomite, brucite, activator, alumina, serine, methacryloxypropyltrimethoxysilane, polypropylene resin, graphite, nano silicon carbide, polyolefin elastomer body, polycarbonate, polyvinyl alcohol, isopropyl palmitate, tributyl phosphate, talc.

[0032] The box is prepared according to the following process:

[0033] 1) Add perlite and sepiolite to the crusher according to the mass ratio of 2:1 for crushing, and then grind to obtain a powder with a particle size of 200 mesh, which is the mixture A;

[0034] 2) Mix borax, dolomite, brucite and active agent evenly according to the mass ratio of 100:50:30:1, put them into the ball mill tank, the ball mill time is 6 hours, the ball mill speed is 800 rpm, and ball mill to powder The particle size is 200 mesh, and the mixture B is obtai...

Embodiment 3

[0040] Box material performance test of the present invention:

[0041] 1. The box body material prepared in embodiment 1-2 is made standard test piece by test standard, carries out following performance test, and the results are shown in Table 1:

[0042] Table 1

[0043]

[0044] 2. Corrosion resistance test: Take salt solution as an example, soak the test material in 10% sodium chloride solution for 240 hours, and measure the main performance parameters, see Table 2:

[0045] Table 2

[0046] group Flame retardant Insulation performance retention rate (%) Tensile Strength Retention Rate (%) Elongation at break (%) Example 1 V0 98.2 97.6 99.1 Example 2 V0 98.9 97.8 99.3

[0047] Conclusion: The box prepared in Example 1-2 has good mechanical properties, insulation performance, corrosion resistance and flame retardancy, and can effectively prevent damage, electric shock and fire.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of power equipment and discloses a community low-voltage grid integrated distribution box. The community low-voltage grid integrated distribution box comprises a box body, and the box body is prepared from perlite, sepiolite, borax, dolomite, brucite, an activating agent, aluminum oxide, serine, methacryloxypropyltrimethoxysilane, polypropylene resin, graphite, nano silicon carbide, polyolefin elastomer, polycarbonate, polyvinyl alcohol, isopropyl palmitate, tributyl phosphate and talcum powder. The community low-voltage grid integrated distribution box is excellent in mechanical property, insulating property, corrosion resistance and flame retardation and effective in prevention of damages, electric shock and fire disasters.

Description

technical field [0001] The invention belongs to the field of electric equipment, and in particular relates to a community low-voltage power grid integrated distribution box and its application. Background technique [0002] The community low-voltage power grid connects various households and is related to people's quality of life, including components such as transmission cables, poles, and distribution boxes. The distribution box is the power distribution equipment used for power distribution, control, metering and cable connection in the power supply system. Generally, power supply bureaus and substations use high-voltage switchgear, and then the low-voltage side of the transformer is stepped down to lead to low-voltage The distribution box and the low-voltage distribution box are connected to each power distribution panel, control box, and switch box. Inside, some switches, circuit breakers, fuses, buttons, indicator lights, meters, wires and other protective devices are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/00C08L69/00C08L29/04C08L23/12C08K13/06C08K9/06C08K3/34C08K3/38C08K3/26C08K3/22C08K9/00C08K3/04H02B1/46
CPCC08L23/00C08K2201/003C08K2201/011C08K2201/014C08L2201/02C08L2201/08C08L2203/20C08L2205/035H02B1/46C08L69/00C08L29/04C08L23/12C08K13/06C08K9/06C08K3/34C08K2003/387C08K2003/265C08K2003/267C08K2003/2224C08K2003/2227C08K9/00C08K3/04
Inventor 陈琳孙运东
Owner JUNAN POWER SUPPLY CO OF STATE GRID SHANDONG ELECTRIC POWER CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products