Anti-abrasion denitration catalyst and preparation method thereof

A denitration catalyst and anti-wear technology, applied in catalyst activation/preparation, chemical instruments and methods, physical/chemical process catalysts, etc., can solve the problems of unstable activity, poor wear resistance, unbalanced active centers, etc. Stabilize, improve water resistance, reduce oxidation effect

Inactive Publication Date: 2017-09-19
PETROCHINA CO LTD
View PDF9 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The main purpose of the present invention is to provide an anti-wear denitrification catalyst and its preparation method to overcome the defects of unbalanced active centers, poor wear resistance and unstable activity of denitrification catalysts in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-abrasion denitration catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] will contain TiO 2 500g of titanyl sulfate is dissolved in the sulfuric acid solution, and the 3 22.5g of ammonium molybdate, as P 2 o 5 4.5g of phosphoric acid, 4.5g of magnesium nitrate solution as MgO to form a TiO-containing 2 It is a 35g / L mixed solution. After stirring for 2 hours, gradually add ammonia water to adjust the pH value to 9.5. After the precipitation is complete, filter and wash; then use deionized water to make a slurry with a water content of 50%, and add V 2 o 5 A total of 12.5g of ammonium metavanadate solution, stirred for 1.5h, dried, roasted at 550°C for 8h, and then ground into a powder with a particle size of less than 20μm; the powder was mixed with MoO 3 A total of 7.5g of ammonium molybdate, 4g of stearic acid, 3g of polyethylene oxide and deionized water are used to make a paste with a water content of 30%, adjust the pH value to 8.5 with ammonia water, add 5g of nano silicon dioxide, 4.5g of silicon dioxide after stirring Limestone,...

Embodiment 2

[0067] will contain TiO 2 500g of titanyl sulfate is dissolved in the sulfuric acid solution, and the 3 22.5g of ammonium molybdate, as P 2 o 5 4.0g of phosphoric acid, 4.0g of magnesium nitrate solution as MgO to form a TiO-containing 2 It is a 30g / L mixed solution. After stirring for 1.5h, gradually add ammonia water to adjust the pH value to 10. After the precipitation is complete, filter and wash; then use deionized water to make a slurry with a water content of 50% from the washed material, and add V 2 o 5 A total of 10g of ammonium metavanadate solution, stirred for 1.5h, dried, roasted at 550°C for 8h, and then ground into a powder with a particle size of less than 30μm; the powder was mixed with MoO 3The ammonium molybdate of 7.5g, 3.5g stearic acid, 3.5g polyoxyethylene and deionized water are made the paste body containing water 32%, adjust pH value to 8.0 with ammoniacal liquor, add 4.5g nano silicon dioxide, 4g wollastonite, 17.5g glass fiber, 4g carboxymethy...

Embodiment 3

[0071] will contain TiO 2 500g of titanyl sulfate is dissolved in the sulfuric acid solution, and the 3 20g of ammonium molybdate, as P 2 o 5 3.5g of phosphoric acid, 3.5g of magnesium nitrate solution as MgO to form TiO-containing 2 It is a 30g / L mixed solution. After stirring for 1.0h, gradually add ammonia water to adjust the pH value to 9. After the precipitation is complete, filter and wash; then use deionized water to make a slurry with a water content of 45%, and add V 2 o 5 A total of 9g of ammonium metavanadate solution, stirred for 1.0h, dried, roasted at 550°C for 8h, and then ground into a powder with a particle size of less than 15μm; the powder was mixed with MoO 3 Ammonium molybdate of 5g, 3.0g stearic acid, 3.0g polyoxyethylene and deionized water are made into a paste with a water content of 28%, and the pH value is adjusted to 8.2 with ammonia water, and after stirring, add 3.5g nano silicon dioxide, 3.5 g wollastonite, 22.5g glass fiber, 3g carboxymeth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-abrasion denitration catalyst and a preparation method thereof. The preparation method comprises the following steps of dissolving titanium source precursors into acid to form a solution; respectively dissolving molybdenum source precursors, phosphorus source precursors and magnesium source precursors to form solutions; uniformly mixing the solutions; regulating the pH value; performing precipitation, filtering and washing; then adding deionized water; preparing the materials into slurry; adding a vanadium source precursor solution; after uniform mixing, directly performing drying and roasting; grinding the materials into powder; next, adding extrusion auxiliary agents, a solution formed by the molybdenum source precursors and pore forming agents; adding water during the stirring to obtain paste; regulating the pH value; adding nanometer silicon dioxide, wollastonite, glass fiber and bonding agents; performing uniform mixing; extruding honeycomb-shaped blanks by an extruding machine; performing drying and roasting; then, obtaining a finished product. The prepared anti-abrasion denitration catalyst can overcome the defects of unstable activity, poor anti-abrasion performance and activity center unbalance of a denitration catalyst in flue gas in the prior art.

Description

technical field [0001] The invention relates to an anti-wear denitration catalyst and a preparation method thereof, in particular to a denitration catalyst resistant to uneven deposition of vanadium in flue gas and a preparation method thereof, which belongs to the technical field of new inorganic materials. Background technique [0002] Nitrogen oxides (NO x ) is one of the main air pollutants, and the emission requirements are becoming increasingly stringent. my country's "Twelfth Five-Year Plan" Comprehensive Work Plan for Energy Conservation and Emission Reduction stipulates that by 2015, the total national nitrogen oxide emissions will drop by 10% compared with 2010. In September 2011, the Ministry of Environmental Protection promulgated GB13223-2001 "Emission Standards of Air Pollutants for Thermal Power Plants", which made stricter requirements on the NOx emission concentration of thermal power plants: it stipulates that the coal-fired boilers newly built, expanded a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/199
CPCB01J27/199B01J37/0009B01J37/03B01J37/04B01J35/56
Inventor 巫树锋贾媛媛刘光利唐中华王军杨岳梁宝锋李晶蕊李常青谷丽芬
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com