Biodegradable composite film for fresh-keeping packaging of edible fungi and preparation method thereof

A biodegradable, fresh-keeping packaging technology, used in coatings, hyaluronic acid coatings, alginic acid coatings, etc., can solve problems such as adverse effects, chemical reagent residues, harmful gases in plastic films, and achieve extended storage and shelf life. Reduces water loss and weight loss, inhibits respiration and post-growth effects

Active Publication Date: 2021-04-16
上海大觉包装制品有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although methods such as vacuum cooling, controlled atmosphere refrigeration, and irradiation fresh-keeping have certain effects, they are not suitable for promotion and use because of high equipment costs, huge initial investment, and cumbersome operations; After it is placed on the shelf and stored at room temperature, the above-mentioned corruption and deterioration problems will still occur in a short period of time
The chemical preservation method is cheap, but there is a problem of chemical reagent residue, which has adverse effects on the human body and the environment and hidden safety hazards, and is gradually abandoned by people.
Coating film preservation is a kind of natural sugar, protein, lipid, etc. as the main raw materials, which are coated on the surface of edible fungi by spraying, dipping, etc., and after drying, an imperceptible transparent edible film layer is formed. Bacteria play a fresh-keeping method with an antiseptic effect; coating preservation has a certain preservation effect on edible fungi with large and plump mushroom bodies, but for small and dense edible fungi such as Flammulina velutipes and tea tree mushrooms, coating preservation is inconvenient to operate and Large dosage, uneconomical, poor effect
[0005] Now the shelf life of edible mushrooms is commonly used for freshness preservation. The plastic wrap is generally made of refractory plastic film materials such as polyethylene, polyvinyl chloride or polyvinylidene chloride. Although it is light in weight and cheap, the plastic film is easy to produce Harmful gas, peculiar smell, and easy to cause white pollution. Its extensive use has caused great harm to people's living environment. The existing plastic plastic wrap packaging edible fungus is not a green and environmentally friendly packaging method.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biodegradable composite film for fresh-keeping packaging of edible fungi and preparation method thereof
  • Biodegradable composite film for fresh-keeping packaging of edible fungi and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The biodegradable composite film for fresh-keeping packaging of edible fungi of this embodiment is prepared by the following method:

[0038] 1) Basement membrane pretreatment: take a polylactic acid film with a thickness of 25 μm as the basement membrane, immerse the basement membrane in a polyethyleneimine solution with a concentration of 1.0 g / L for 3 hours for amination, take it out, and wash it with deionized water And carry out blast drying at 45°C, then immerse in dilute hydrochloric acid with a mass concentration of 4.5% for 3min to acidify, take it out, wash with deionized water, and carry out blast drying at 45°C to obtain the modified base membrane;

[0039] 2) get chitosan and be dissolved in acetic acid aqueous solution (the mass concentration of acetic acid is 1.0%) and make the chitosan solution that concentration is 3.8g / L; Step 1) gained modified base film is completely submerged in gained chitosan In the solution for 9 minutes, after taking it out, wa...

Embodiment 2

[0043] The biodegradable composite film for fresh-keeping packaging of edible fungi of this embodiment is prepared by the following method:

[0044] 1) Basement membrane pretreatment: take a polylactic acid film with a thickness of 25 μm as the basement membrane, immerse the basement membrane in a polyethyleneimine solution with a concentration of 2.0 g / L for 2.5 hours for amination, take it out, and wash it with deionized water After cleaning, carry out blast drying at 45°C, then immerse in dilute hydrochloric acid with a mass concentration of 4.0%% for 4 minutes to acidify, then take it out, wash with deionized water, and carry out blast drying at 45°C. sexual basement membrane;

[0045] 2) get chitosan and be dissolved in acetic acid aqueous solution (the mass concentration of acetic acid is 1.0%) and make the chitosan solution that concentration is 3.5g / L; Step 1) gained modified base film is completely submerged in gained chitosan In the solution for 10 minutes, after ta...

Embodiment 3

[0049] The biodegradable composite film for fresh-keeping packaging of edible fungi of this embodiment is prepared by the following method:

[0050] 1) Basement membrane pretreatment: Take a polylactic acid film with a thickness of 25 μm as the basement membrane, immerse the basement membrane in a polyethyleneimine solution with a concentration of 1.5g / L for 2.5h for amination, take it out, and wash it with deionized water After cleaning, carry out blast drying at 45°C, then immerse in dilute hydrochloric acid with a mass concentration of 5.0% for 2 minutes for acidification, take it out, wash with deionized water, and carry out blast drying at 45°C to obtain modified basement membrane;

[0051] 2) get chitosan and be dissolved in acetic acid aqueous solution (the mass concentration of acetic acid is 1.0%) and make the chitosan solution that concentration is 4.0g / L; Step 1) gained modified base film is completely submerged in gained chitosan In the solution for 8 minutes, aft...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a biodegradable composite film for fresh-keeping packaging of edible fungi and a preparation method thereof. The composite film is prepared by the following method: 1) taking a polylactic acid film as a base film, and immersing the base film in a polyethyleneimine solution amination, after washing and drying, immerse in dilute hydrochloric acid for acidification, wash and dry to obtain a modified base film; 2) immerse the obtained modified base film in the obtained chitosan solution, wash and dry to obtain the first Composite film; 3) dissolving sodium alginate, calcium chloride and cinnamic acid in water to make a coating solution; 4) uniformly coating the obtained coating solution on one side of the first composite film, and drying to form a coating layer, that is have to. The obtained biodegradable composite film is used for fresh-keeping packaging of edible fungi, which can delay the respiration and post-ripening effect of edible fungi, reduce the rate of browning and weight loss, effectively preserve the freshness of edible fungi, and greatly extend the storage period and Normal temperature shelf life, suitable for promotion and use.

Description

technical field [0001] The invention belongs to the technical field of fresh-keeping packaging of edible fungi, in particular to a biodegradable composite film for fresh-keeping packaging of edible fungi, and also relates to a preparation method of the biodegradable composite film for fresh-keeping packaging of edible fungi. Background technique [0002] Edible fungi, also known as mushrooms, have fleshy or gelatinous fruiting bodies, and are large edible fungi; common edible fungi include shiitake mushrooms, oyster mushrooms, Agaricus bisporus, Flammulina velutipes, Pleurotus eryngii, fungus, white fungus, etc. Edible fungi are rich in protein and amino acids, the content is several times to dozens of times that of ordinary vegetables and fruits, and its amino acid composition is relatively comprehensive. Most mushrooms contain eight kinds of amino acids necessary for the human body, and also contain various vitamins and various Mineral elements with physiological activity....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/048C08J5/18C09D105/08C09D105/04C08L67/04
CPCC08J5/18C08J7/042C08J2367/04C08J2405/04C08J2405/08
Inventor 吴雅婧熊露璐吴雅琳魏科峰
Owner 上海大觉包装制品有限公司