PVC (polyvinyl chloride) edge seal adhesive and preparation method thereof

A technology of edge banding and adhesive, which is applied in the field of pigments to achieve the effects of low product cost, high bonding strength and strong adhesion

Inactive Publication Date: 2019-06-18
广东绿洲化工有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, aiming at the shortage of hot melt adhesives and solvent-based edge banding adhesives, the present invention provides a PVC edge banding adhesive, which overcomes the problems existing in existing edge banding adhesives, and has high bonding strength and excellent aging resistance. , easy to use, environmentally friendly and pollution-free

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] In weight percentage, the PVC edge banding adhesive of the present embodiment comprises:

[0040] 40% deionized water, 1.2% anionic emulsifier, 0.3% reactive emulsifier, 0.1% buffer, 3.3% stabilizer, 2.2% crosslinking agent, 0.3% initiator, 22% Acrylic monomer, 25.5% vinyl acetate, 0.72% internal plasticizing monomer, 5% modified tackifying resin emulsion, 0.06% wetting agent W469, 0.15% film-forming aid.

[0041] Wherein, the anionic emulsifier is Dowfax 2A1 (dodecyl diphenyl ether disulfonic acid sodium salt); the reactive emulsifier is sodium vinyl sulfonate; the buffering agent is that the mass concentration is 5% sodium bicarbonate aqueous solution; the initiator It is an aqueous potassium persulfate solution with a mass concentration of 5%; the stabilizer is sodium polymethacrylate; the crosslinking agent is acrylamide; the acrylic monomer is butyl acrylate; the internal plasticizing monomer is dibutyl fumarate; The modified tackifying resin emulsion is modified ...

Embodiment 2

[0050] In weight percentage, the PVC edge banding adhesive of the present embodiment comprises:

[0051] 38% deionized water, 1.0% anionic emulsifier, 0.2% reactive emulsifier, 0.1% buffer, 2.8% stabilizer, 3.3% crosslinking agent, 0.25% initiator, 20% Butyl acrylate, 5% ethyl acrylate, 22% vinyl acetate, 0.94% internal plasticizing monomer, 7% modified tackifying resin emulsion, 0.07% wetting agent Deqian W469, 0.15% Coalescing aids.

[0052] Wherein, the anionic nonionic emulsifier is Dowfax 2A1 (dodecyl diphenyl ether disulfonic acid sodium salt); the reactive emulsifier is sodium propenyl sulfonate; the buffering agent is an aqueous sodium bicarbonate solution with a mass concentration of 5%; The initiator is an aqueous solution of potassium persulfate with a mass concentration of 5%; the stabilizer is sodium hydroxyethyl cellulose; the crosslinking agent is N-methylol acrylamide; the acrylic monomer is a mixture of butyl acrylate and ethyl acrylate The internal plastici...

Embodiment 3

[0056] In weight percentage, the PVC edge banding adhesive of the present embodiment comprises:

[0057] 45% deionized water, 1.0% anionic emulsifier, 0.25% reactive emulsifier, 0.2% buffer, 2.8% stabilizer, 3.3% crosslinking agent, 0.25% initiator, 20% Butyl acrylate, 4% isooctyl acrylate, 26% vinyl acetate, 1% internal plasticizing monomer, 3.5% modified tackifying resin emulsion, 0.08% wetting agent Deqian W469, 0.15% film-forming aids.

[0058] Wherein, the anionic emulsifier is Dowfax 2A1 (dodecyl diphenyl ether disulfonic acid sodium salt); the reactive emulsifier is sodium acrylamido sulfonate; the buffering agent is an aqueous solution of sodium bicarbonate whose mass concentration is 5%; The agent is an aqueous solution of potassium persulfate with a mass concentration of 5%; the stabilizer is sodium polymethacrylate; the crosslinking agent is methacrylamide; the acrylic monomer is a mixed monomer of butyl acrylate and isooctyl acrylate; The plastic monomer is di-n-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses PVC (polyvinyl chloride) edge seal adhesive, made from, by weight, 38-48% of deionized water, 0.8-2% of an anionic emulsifier, 0.1-0.2% of a reactive emulsifier, 0.1-0.2% of abuffer agent, 2.5-4.5% of a stabilizer, 1.5-3.5% of a crosslinking agent, 0.2-0.5% of an initiator, 20-28% of an acrylic monomer, 20-30% of vinyl acetate, 0.5-1% of an internal plasticization monomer,3-10% of modified tackifying resin emulsion, 0.05-0.1% of a wetting agent, and 0.1-0.3% of a film-forming aid. In addition, the invention also discloses a preparation method of the PVC edge seal adhesive. The PVC edge seal adhesive is convenient to use, can cure at normal temperature, has high adhesive strength and good aging resistance, is free of organic solvents and formaldehydes and is nontoxic and environmentally friendly.

Description

technical field [0001] The present invention relates to a kind of pigment, especially relates to the pigment with natural fluidity used in fine arts, moreover, the present invention also relates to the preparation method of this pigment. Background technique [0002] With the rapid improvement of people's living standards, the demand for panels in building decoration and furniture manufacturing is increasing. Traditional solid wood boards can no longer meet the needs of social and economic development due to factors such as limited forest resources and limitations in the use of boards. As a representative of new boards, man-made boards are characterized by low production costs, high utilization of wood, and excellent board strength. It has been widely used in furniture manufacturing and architectural decoration. The internal material structure of wood-based panels is quite different from that of solid wood. Generally, after cutting, the surface is rough and uneven, and is e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D131/04C09D11/08C08F218/08C08F220/18C08F220/56C08F222/14C08F220/58C08F228/02
Inventor 郑秀明丁建平
Owner 广东绿洲化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com