Synthetic latex glove

A technology for synthesizing latex and gloves, which can be applied to gloves, protective clothing, clothing, etc. It can solve the problems of butyl latex instability, difficulty in film formation, and demulsification, so as to achieve strong operability in processing technology and ensure the performance of film formation process , Easy to wear and comfortable effect

Pending Publication Date: 2020-09-25
山东利尔新材股份有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, butyl latex is unstable, difficult to form a film, has poor processing stability, and is prone to precipitation and demulsification after adding compounding agents. Therefore, the application technology of butyl latex at home and abroad has been developed for decades, but its film-forming technology still remains unable to industrialize

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthetic latex glove
  • Synthetic latex glove
  • Synthetic latex glove

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of synthetic latex glove, described glove is prepared from the latex composition of following mass parts:

[0036] Natural latex: 30

[0037] Butyl latex: 70

[0038] Casein: 1

[0039] Sulfur: 1.7

[0040] Potassium hydroxide: 1.0

[0041] Accelerator TETD:3

[0042] Accelerator Thiourea: 1.5

[0043] Accelerator PX:0.5

[0044] Zinc Oxide: 5

[0045] Antiager 264: 0.5

[0046] Carbon black: 10

[0047] Gum Arabic: 5

[0048] Talc: 20

[0049] Clay: 0.5

[0050] Water glass: 0.2

[0051] Sodium carboxymethyl cellulose: 0.5

[0052] The manufacturing process of synthetic latex gloves of the present invention, described specific preparation method comprises the steps:

[0053] 1) preparation: mix and prepare natural rubber latex and butyl latex according to the mass parts;

[0054] 2) Pre-vulcanization: Add casein, potassium hydroxide, sulfur, accelerator TETD, accelerator thiourea, accelerator PX, zinc oxide, anti-aging agent 264, carbon black, gum...

Embodiment 2

[0065] A kind of synthetic latex glove, described glove is prepared from the latex composition of following mass parts:

[0066] Natural latex: 20

[0067] Butyl latex: 80

[0068] Casein: 1

[0069] Sulfur: 1.5

[0070] Potassium hydroxide: 1.0

[0071] Accelerator TMTD: 2.5

[0072] Accelerator TETD: 1.5

[0073] Accelerator ZDC: 0.5

[0074] Zinc Oxide: 5

[0075] Antiaging agent A: 0.5

[0076] Fast Yellow: 10

[0077] Diatomaceous earth: 30

[0078] Water glass: 0.2

[0079] Sodium carboxymethyl cellulose: 0.5

[0080] Pectin: 1

[0081] Agar: 3

[0082] Enzyme treated starch: 5

[0083] The manufacturing process of synthetic latex gloves of the present invention, described specific preparation method comprises the steps:

[0084] 1) preparation: mix and prepare natural rubber latex and butyl latex according to the mass parts;

[0085] 2) Pre-vulcanization: add casein, potassium hydroxide, sulfur, accelerator TMTD, accelerator TETD, accelerator ZDC, zinc o...

Embodiment 3

[0096] A kind of synthetic latex glove, described glove is prepared from the latex composition of following mass parts:

[0097] Natural latex: 50

[0098] Butyl latex: 50

[0099] Casein: 1

[0100] Sulfur: 1.8

[0101] Potassium hydroxide: 0.5

[0102] Accelerator TMTD: 3

[0103] Accelerator TETD: 1

[0104] Accelerator PX: 1

[0105] Zinc Oxide: 5

[0106] Antiager 4010: 0.5

[0107] Modified Cellulose: 2

[0108] Propylene Glycol Alginate: 2

[0109] Carbon black: 0.05

[0110] White carbon black: 0.05

[0111] Water glass: 0.2

[0112] Sodium carboxymethyl cellulose: 0.5

[0113] The manufacturing process of synthetic latex gloves of the present invention, described specific preparation method comprises the steps:

[0114] 1) preparation: mix and prepare natural rubber latex and butyl latex according to the mass parts;

[0115] 2) Pre-vulcanization: add casein, potassium hydroxide, sulfur, accelerator TMTD, accelerator TETD, accelerator PX, zinc oxide, ant...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a synthetic latex glove and a preparation method thereof. The synthetic latex glove is prepared from the following substances: 1-100 parts of a film-forming substance, 0.5 to 10parts of casein, 0.5 to 4 parts of sulfur, 0.5 to 5 parts of an accelerant, 0.5 to 8 parts of zinc oxide, 0.1 to 5 parts of an anti-aging agent, 0.1 to 1 part of pigment, 0.1 to 1 part of potassium hydroxide, 0.1 to 1 part of water glass, 0.1 to 10 parts of a thickening agent, 0.1 to 30 parts of an inorganic filler and 0.1 to 1 part of sodium carboxymethyl cellulose. The invention further discloses a preparation method of the synthetic latex glove. Compared with the prior art, the synthetic latex glove of the invention has the beneficial effects of excellent hot air aging resistance, excellent water permeation resistance, excellent air tightness, excellent mechanical properties, excellent sulfuric acid solution resistance and excellent sodium hydroxide solution resistance. The invention particularly provides a latex formula with aging resistance, air permeation resistance and water permeation resistance and the latex glove prepared from the latex formula. The latex glove is multi-layer and soft, ageing-resistant, air-permeation-resistant and water-permeation-resistant, fits with a hand curve in shape, and is convenient and comfortable to wear and produced by adopting a standard dipping production line.

Description

technical field [0001] The invention belongs to the field of rubber gloves, and in particular relates to a composite latex formula resistant to aging and medium penetration and a glove preparation technology thereof. Background technique [0002] Most of the original industrial or labor protection gloves are made of leather, such as pigskin or cowhide. This kind of gloves is made of hard material, which is not conducive to the bending of laborers' fingers, and is used in some places that require flexible fingers. [0003] With the rapid development of manufacturing technology and materials, especially the development of rubber and composite materials, more and more new varieties have been discovered. According to the material of the gloves, industrial or labor protection gloves can be divided into rubber, steel wire, leather and knitted thread labor protection gloves. Rubber gloves are mainly used in the process of electrician and cleaning because of their anti-corrosion, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/22C08L7/02C08L89/00C08L1/28C08K13/02C08K3/06C08K3/22C08K3/34C08K5/40C08K5/39C08K5/405C08J5/02A41D19/015
CPCC08L23/22C08L7/02C08J5/02A41D19/0055C08L2205/035C08K2003/2296C08J2323/22C08J2407/02C08J2307/02C08L89/005C08L1/286C08K13/02C08K3/06C08K3/22C08K3/34C08K5/40C08K5/39C08K5/405
Inventor 王长水宋峰于迅郭丽云于振
Owner 山东利尔新材股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com