Environment-friendly colored high-temperature super-wear-resistant super-hardness porcelain aggregate

A super wear-resistant and super-hard technology, applied in the field of high-quality aggregates, can solve problems such as poor bonding

Pending Publication Date: 2021-08-10
山东崯基新材料科技发展有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention proposes an environment-friendly colored high-temperature ultra-wear-resistant and super-hard porcelain aggregate to solve the problem that the porcelain aggregate is poorly bonded to special glue when used in the background technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The invention proposes an environment-friendly colored high-temperature ultra-wear-resistant and ultra-hard porcelain aggregate. The formula of its raw materials by weight is as follows: 0.00001 part of silicon dioxide, 0.0001 part of aluminum oxide, 0.0001 part of ferric oxide, and 0.0001 part of calcium oxide 0.0001 part of magnesium oxide, 0.0001 part of potassium oxide, 0.0001 part of sodium oxide, 0.0001 part of titanium dioxide, 0.00001 part of phosphorus pentoxide, 0.00001 part of manganese oxide, 0.00001 part of dichromium trioxide, 0.00001 part of zinc oxide, 0.00001 part of lead oxide, Zirconia 0.00001 part, barium oxide 0.00001 part, strontium oxide 0.00001 part, diboron trioxide 0.00001 part, fluorine 0.00001 part, lithium oxide 0.0001 part, chromium 0.00001 part, carbon 0.00001 part, sulfur 0.00001 part, nickel oxide 0.00001 part, cobalt oxide 0.00001 part, 0.00001 part of diarsenic trioxide, 0.00001 part of antimony trioxide.

[0016] The bulk density of t...

Embodiment 2

[0018] The present invention proposes an environment-friendly colored high-temperature ultra-wear-resistant ultra-hard porcelain aggregate. The formula of its raw materials by weight is as follows: 30 parts of silicon dioxide, 10 parts of aluminum oxide, 5 parts of ferric oxide, and 15 parts of calcium oxide. 15 parts of magnesium oxide, 15 parts of potassium oxide, 15 parts of sodium oxide, 30 parts of titanium dioxide, 5 parts of phosphorus pentoxide, 15 parts of manganese oxide, 5 parts of chromium oxide, 15 parts of zinc oxide, 15 parts of lead oxide, 15 parts of zirconia, 15 parts of barium oxide, 15 parts of strontium oxide, 5 parts of diboron trioxide, 5 parts of fluorine, 5 parts of lithium oxide, 5 parts of chromium, 5 parts of carbon, 5 parts of sulfur, 1 part of nickel oxide, cobalt oxide 1 part, 1 part of arsenic trioxide, 1 part of antimony trioxide.

[0019] The bulk density of this quality aggregate is 1-6000kg / m 3 . The density of the aggregate is 1-7000kg / m ...

Embodiment 3

[0021] The present invention proposes an environment-friendly colored high-temperature ultra-wear-resistant ultra-hard porcelain aggregate. The formula of its raw materials by weight is as follows: 45 parts of silicon dioxide, 25 parts of aluminum oxide, 15 parts of ferric oxide, and 35 parts of calcium oxide. 35 parts of magnesium oxide, 35 parts of potassium oxide, 35 parts of sodium oxide, 45 parts of titanium dioxide, 25 parts of phosphorus pentoxide, 35 parts of manganese oxide, 15 parts of chromium oxide, 35 parts of zinc oxide, 35 parts of lead oxide, 25 parts of zirconia, 25 parts of barium oxide, 20 parts of strontium oxide, 15 parts of boron trioxide, 15 parts of fluorine, 15 parts of lithium oxide, 15 parts of chromium, 15 parts of carbon, 15 parts of sulfur, 5 parts of nickel oxide, cobalt oxide 5 parts, 5 parts of arsenic trioxide, 5 parts of antimony trioxide.

[0022] The bulk density of this quality aggregate is 1-6000kg / m 3 . The density of the aggregate is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly colored high-temperature super-wear-resistant super-hardness porcelain aggregate. The formula comprises the following raw materials by weight: silicon dioxide, aluminum oxide, ferric oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide, phosphorus pentoxide, manganese oxide, chromic oxide, zinc oxide, lead oxide, zirconium oxide, barium oxide, strontium oxide, diboron trioxide, fluorine, lithium oxide, chromium, carbon, sulfur, nickel oxide, cobalt oxide, arsenic trioxide and antimony trioxide. The environment-friendly colored high-temperature super-wear-resistant super-hardness porcelain aggregate has greatly higher hardness, strength, plasticity, wear resistance, fire resistance temperature, skid resistance, firing calcination temperature, application range, weather resistance, adhesive force with glue and the like than the original product.

Description

technical field [0001] The invention relates to the technical field of bone materials, in particular to an environment-friendly colored high-temperature super wear-resistant super-hard porcelain bone material. Background technique [0002] The existing porcelain aggregates are poorly combined with special glue (because the surface of the product is very smooth, which will affect the adhesion with the glue), and the weather resistance is poor (because the material is simple and lacks chemical components). Therefore, We propose an environmentally friendly colored high-temperature ultra-wear-resistant ultra-hard porcelain aggregate. Contents of the invention [0003] The present invention proposes an environment-friendly, colored, high-temperature, ultra-wear-resistant, and super-hard porcelain aggregate to solve the problem that the porcelain aggregate is poorly bonded to the special glue when used in the background technology. [0004] The invention proposes an environment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14C04B35/46
CPCC04B35/14C04B35/46C04B2235/3217C04B2235/3418C04B2235/3272C04B2235/3208C04B2235/3206C04B2235/3201C04B2235/3232C04B2235/34C04B2235/3262C04B2235/3241C04B2235/3284C04B2235/3296C04B2235/3244C04B2235/3215C04B2235/3213C04B2235/3409C04B2235/3203C04B2235/42C04B2235/404C04B2235/422C04B2235/3279C04B2235/3275C04B2235/3294C04B2235/77C04B2235/9661
Inventor 孙瑞宵孙启江
Owner 山东崯基新材料科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap