A latex paint, water-based technology, applied in the direction of latex paint, coating, etc., can solve the problems of not paying attention to indoor environmental pollution, easy yellowing of the paint film, poor air permeability, etc. Excellent performance and strong adhesion

Inactive Publication Date: 2003-08-13
陈伟常 +1
View PDF1 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But at present, the known various interior wall decorative paints, most of them lay particular stress on the requirements of decoration, and do not pay attention to the problem of indoor environmental pollution in the home. A kind of architectural coating, which mainly uses the chlorine partial emulsion in the formula to form a poor air permeability and water impermeable film during the coating process, thereby preventing radon gas from escaping and preventing water from oozing out, and has a certain anti-radon effect. However, it does not have the function of preventing benzene, xylene, formaldehyde, etc., and because the emulsion polymerization monomer used contains polyvinylidene chloride, the paint film is prone to yellowing, chalking and foaming

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] The equipment and preparation process used in the preparation and detection of embodiment 1 are as follows:

[0057] Instruments and equipment: reaction kettle, high-speed dispersing machine, sand mill, radon measuring instrument, scrub resistance instrument, stirring tank, viscometer, fineness meter, radon exhalation rate standard device, radon exhalation rate measuring instrument, benzene and xylene, formaldehyde Standard device for precipitation rate, chromatograph, etc.;

[0058] Process flow:

[0059] A) The reaction mixing temperature is about 40 degrees;

[0060]B) Put component 1 into the reactor according to the amount first, then gradually add components 2, 3, 4, and 5, and mix and stir for 30 minutes at first slowly and then quickly;

[0061] C) Add components 6, 7, 8, 9, and stir at high speed for 30 minutes;

[0062] D) Add components 10, 11, 12, 13 and stir slowly for 30 minutes;

[0063] E) Take it out and put it into a sand mill to grind for about 60...

Embodiment 2

[0066] Embodiment 2, its component and parts by weight are:

[0067] 1. Water 320

[0068] 2. Hydroxyethyl fiber 2.6

[0069] 3. Dispersant SN-Dispersant-5040 3.2

[0070] 4. Defoamer SN-154 3.5

[0071] 5. Leveling agent NOPCO OSX TM 2000EXP 3

[0072] 6. Light calcium carbonate 125

[0073] 7. Titanium dioxide 175

[0074] 8. Bentonite 45

[0075] 9. Talc powder 125

[0076] 10. Ethylene glycol 6.5

[0077] 11. Film-forming aid dimethyl phthalate 3.5

[0078] 12. PVDF-acrylate copolymer and

[0079] Blend of vinyl acetate-acrylate copolymer emulsions 375

[0080] 13. GK-98 preservative

[0081] (Trihydroxyethyl-s-triazine) 3.2

[0082] The mixture of described PVDF-acrylate copolymer and vinyl acetate-acrylate copolymer emulsion is that the weight ratio of PVDF-acrylate copolymer and vinyl acetate-acrylate copolymer emulsion is 5: 95, adopts common method to mix uniformly and become.

[0083] Preparation used equipment and preparation process are as emb...

Embodiment 3

[0084] Embodiment 3, its component and parts by weight are as follows:

[0085] 1. Water 310

[0086] 2. Hydroxyethyl Fiber 2.4

[0087] 3. Dispersant SN-Dispersant-5040 and

[0088] Mixture of FC-109 3.1

[0089] 4. Defoamer SN-154 3.2

[0090] 5. Leveling agent NOPCO OSX TM 2000EXP 2.8

[0091] 6. Light calcium carbonate 128

[0092] 7. Titanium dioxide 190

[0093] 8. Bentonite 48

[0094] 9. Talc powder 140

[0095] 10. Ethylene glycol 6.2

[0096] 11. Film-forming aid dimethyl phthalate 3.2

[0097] 12. PVDF-acrylate copolymer and

[0098] Blend of vinyl acetate-acrylate copolymer emulsions 380

[0099] 13. GK-98 preservative

[0100] (effective chemical component trihydroxyethyl-s-triazine) 2.7

[0101] The mixture of described PVDF-acrylate copolymer and vinyl acetate-acrylate copolymer emulsion is that the weight ratio of PVDF-acrylate copolymer and vinyl acetate-acrylate copolymer emulsion is 5: 95, adopts common method to mix uniformly and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A radon-screening water emulsoid paint used as decorative paint for preventing radon, benzene, xylene and formaldehyde from being educed from wall and adsorbing them contains water, hydroxyethyl cellulose, disperser, defoaming agent, levelling agent, light calcium carbonate, titanium oxide, bentone, talc powder, ethanediol, film forming agent, PVDF-acrylate copolymer and vinyl acetate-acrylate copolymer emulsion, and antibacterial mildew-proof agent.

Description

Technical field [0001] The invention relates to a chemical coating, in particular to a water-based radon-proof latex paint used for home interior wall decoration. Background technique [0002] With the improvement of people's living standards, people pay more and more attention to the problem of indoor environmental pollution in the home, and the main pollution factors that cause indoor pollution in the home are radon, benzene, xylene, formaldehyde, etc. Radon gas is a colorless, odorless radioactive gas, and benzene, xylene, formaldehyde, etc. are also chemical poisons harmful to the human body. They may exist in building materials such as bricks, gravel, concrete, prefabricated components, plywood, etc., and migrate from them by thermal motion and convection of atoms or molecules, from the interior of the substrate to the surface of the substrate and then to the air In the environment, when the concentration of these harmful gases accumulates and gradually increases, it w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/02C09D131/04
Inventor 陈伟常
Owner 陈伟常
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap