High-performance aluminum/carbon composite electrode foil and preparation method thereof

A technology of carbon composite and electrode foil, which is applied in the direction of capacitor electrodes, electrode carriers/current collectors, circuits, etc., can solve the problems of poor compatibility, insufficient conductivity and stability, etc., to overcome poor compatibility, The effect of increasing the surface area and improving the binding force

Active Publication Date: 2012-04-25
宇东箔材科技南通有限公司
View PDF10 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The high-performance aluminum/carbon composite electrode foil made by the present invention does not rely on adhesives to bond the carbon layer, but relies on the amorphous carbon layer formed in situ on the surface of the conductive graphite particles to connect the conductive graphite particles and the aluminum foil matrix into one body, The combination of crystalline graphite a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance aluminum/carbon composite electrode foil and preparation method thereof
  • High-performance aluminum/carbon composite electrode foil and preparation method thereof
  • High-performance aluminum/carbon composite electrode foil and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0032] Example 1 1 part by weight of polyvinylidene fluoride, 98.5 parts by weight of graphite powder with an average particle size of 25 microns, and 0.5 part by weight of silane coupling agent are uniformly dispersed in a solvent (N-methylpyrrolidone) to obtain a slurry with a solid content of 5%. The slurry was dipped and coated on both sides of a corroded aluminum foil with a thickness of 50 μm, and the thickness of the carbon layer on one side was 50 μm after drying. Place the pole piece in N 2 Maintain the atmosphere at 350°C for 48h.

Example Embodiment

[0033] Example 2 Mix 6 parts by weight of polytetrafluoroethylene emulsion (water-based emulsion with 50% polytetrafluoroethylene content), 96 parts by weight of graphite powder with an average particle size of 15 microns, and 1 part by weight of titanate coupling agent in a solvent (dimethyl carbonate). ) Is uniformly dispersed to obtain a slurry with a solid content of 10%. The slurry is dipped and coated on both sides of a corroded aluminum foil with a thickness of 50 μm. After drying, the carbon layer has a single-sided thickness of 35 μm. Place the pole piece in N 2 Keep the atmosphere at 380°C for 40h.

Example Embodiment

[0034] Example 3 5 parts by weight of epoxy resin, 94.5 parts by weight of graphite with an average particle size of 20 microns and 0.5 parts by weight of titanate coupling agent are uniformly mixed and dispersed in a solvent (propylene glycol methyl ether) to obtain a slurry with a solid content of 20%. The slurry was coated on both sides of a corroded aluminum foil with a thickness of 50 μm by a knife coating method, and the thickness of the carbon layer on one side was 45 μm after drying. Place the pole piece in N 2 Keep the atmosphere at 400°C for 36h.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Purityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-performance aluminum/carbon composite electrode foil and a preparation method thereof. The high-performance aluminum/carbon composite electrode foil comprises a substrate aluminum foil and a carbon-containing layer formed on the surface of the aluminum foil, wherein the carbon-containing layer comprises graphite particles and an amorphous carbon layer, wherein the graphite particles have high electrical conductivity; the amorphous carbon layer is coated on the periphery of the graphite particles and is connected with an aluminum foil substrate to conduct graphite particles; and an interdiffusion layer with a certain depth is formed between the aluminum foil substrate and the carbon-containing layer. The preparation method for the high-performance aluminum/carbon composite electrode foil is characterized by comprising the following steps of: blending graphite powder, organic resin and an active additive in an organic solvent to prepare slurry; coating the slurring on the aluminum foil; and performing heat treatment under the condition of isolating oxygen after drying the slurry. The preparation method is simple in process and low in cost; and the prepared electrode foil has high-temperature stability, extremely low internal resistance, good sealing performance and wide application prospect.

Description

technical field [0001] The invention relates to an aluminum / carbon composite electrode foil and a preparation method thereof. Specifically, the invention relates to a method for manufacturing an aluminum / carbon composite electrode foil that can be used as an electrode material or an electrode collector material for devices such as aluminum electrolytic capacitors, supercapacitors, and lithium-ion batteries, and belongs to the field of energy materials. Background technique [0002] Commonly used energy storage devices such as capacitors and batteries have high capacity and low internal resistance performance requirements in order to ensure their performance, so as to obtain greater energy storage and output efficiency. The main structure of energy storage devices such as capacitors (batteries) is anode / dielectric material (electrolyte) / cathode / collector. Electrode materials have an extremely significant impact on the capacity and internal resistance of energy storage device...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01G9/04H01G9/045H01M4/66
CPCY02E60/12Y02E60/10
Inventor 李荐黄祖琼陈卫东姚建军杨振江
Owner 宇东箔材科技南通有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products