Colored UV-light-curable paint

A technology for curing coatings and ultraviolet light, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of difficult wide application and high price, and achieve the effects of wide applicability, high curing activity, and stable storage

Active Publication Date: 2015-05-13
中山大桥化工企业集团中山智亨实业发展有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing colored UV-curable coatings usually use nano-transparent color paste, but it is difficult to be widely used because of its high price

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colored UV-light-curable paint
  • Colored UV-light-curable paint
  • Colored UV-light-curable paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1 (preparation of self-initiating resin HV-301B)

[0037] Into a 5000ml four-necked flask equipped with a condenser tube, a thermometer, an air duct, and a mechanical stirrer, pass dry air into it, start the stirrer, add 2661.6g of pentaerythritol triacrylate after 10 minutes, and dissolve 0.7g of it with 20.0g of butyl acetate P-methoxyphenol (MQ), 1.4g 2,6-di-tert-butyl-p-cresol (BHT), the above solution was added to the reaction kettle under stirring conditions, and 35.6g of 1,8-diazabicyclo[ 5.4.0] Undec-7-ene (DBU), was added dropwise to the reactor under stirring condition, and slowly heated up to 45°C; weighed 1000.0g acetylacetone, and used a constant pressure dropping funnel within 150-180min After the dropwise addition, wash the funnel with 30.0g of butyl acetate solvent, keep it warm at 45-55°C for 4h, add 20.0g of acrylic acid, and discharge the material. It is obtained from the initiation resin HV-301B. figure 1 , the resulting self-initiating r...

Embodiment 2

[0038] Embodiment 2 (preparation of transparent red paste)

[0039] The preparation method of transparent red paste comprises the following steps:

[0040] 1) Mix 13.56g xylene and 13.56g butyl acetate to obtain a mixed solvent;

[0041] 2) Pre-disperse 34.84g of self-initiating resin (B-12, HV-301B of Guangzhou Boxing with a mass ratio of 3:1), add 1.31g of dispersant (EFKA4010), 13.02g of mixed solvent in turn, and add 4.47g of g transparent red powder (DIC, model: R-185), mixes, obtains mixture;

[0042] 3) Grind the mixture at 35-40°C until the fineness is less than 5 μm, filter the material with a 5 μm filter bag, add 14.1 g of mixed solvent, and stir evenly to obtain a transparent red slurry.

[0043]The transparent red paste used in the following examples all adopts the transparent red paste prepared in this embodiment.

Embodiment 3

[0044] Embodiment 3 (colored ultraviolet light curing coating)

[0045] A colored ultraviolet light curing coating, the coating contains the following components by weight:

[0046] 38 parts of polyurethane acrylate (UV-7605B), 7.1 parts of polyurethane acrylate (UV1000), 30 parts of self-initiating resin (HV-301B), 3 parts of trimethylolpropane triacrylate, 5 parts of transparent red paste, FMT2. 0 part, 0.5 part of 1-hydroxycyclohexyl phenyl ketone (Irgacure184), mixed solvent (ratio by weight: toluene 20%, ethyl acetate 40%, propylene glycol butyl ether 10%, cyclohexane 20%, butanone 10 %) 20.2 parts, leveling agent (BYK333) 0.6 parts, leveling agent (BYK306) 0.2 parts, leveling agent (EFKA3777) 0.2 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Functional group degreeaaaaaaaaaa
Functional group degreeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a colored UV-light-curable paint comprising the components of, by weight: 40-80 parts of main resin, 2-8 parts of an active diluent, 0.1-5.0 parts of a transparent colorant, 2-4 parts of a photo-initiator, and 20-30 parts of a solvent. The main resin is composed of 40-80wt% of polyurethane acrylic ester and 20-60wt% of self-triggered UV-light-curable resin. The photo-initiator is at least one selected from an alpha-hydroxyketone photo-initiator, a phosphine oxide photo-initiator, and a titanocene photo-initiator. The transparent colorant is prepared from mixed and grinded materials of the self-triggered UV-light-curable resin as a carrier and a transparent toner. The colored UV-light-curable paint provided by the invention has advantages of excellent performance, high curing activity, high adhesion strength, good decorative effect, wide toning range, wide application range, and the like. The paint can cooperate with traditional primer paint, and electronic product film coating can be completed with a double-layer coating technology. Therefore, production cost of coating technologies can be reduced, environment pollution can be reduced, and product defective rate can be reduced.

Description

technical field [0001] The invention relates to an ultraviolet light curing paint, in particular to a colored ultraviolet light curing paint. Background technique [0002] Photocuring coating is a surface treatment technology in which a photoinitiator decomposes into free radicals or cations under the action of ultraviolet light, and then initiates unsaturated double bond polymerization to form a film. Compared with traditional solvent-based coatings, photocuring coatings can greatly reduce Environmental pollution and damage to human health caused by organic volatiles. At the same time, it also has a high crosslinking density. The paint film has excellent mechanical, chemical resistance, weather resistance and decorative properties, so it is widely used in electronic products. in the coating process. [0003] At present, the coating process of 3C electronic products usually uses traditional light-curing coatings for three-layer coating, which has the advantages of excellent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/14C09D7/12
Inventor 张博孙太荣于学亚林建明
Owner 中山大桥化工企业集团中山智亨实业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com