Method for preparing small-molecule oligomeric hyaluronic acid through enzyme method

A technology for oligomeric hyaluronic acid and enzymatic preparation, which is applied in the field of enzymatic preparation of small molecule oligomeric hyaluronic acid, can solve the problems of complex reaction conditions, influence of HA properties, and difficulty in product purification, and achieves easy purification, recovery and reaction. simple conditional effect

Active Publication Date: 2015-02-11
JIANGNAN UNIV
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the chemical degradation method introduces chemical reagents, the reaction conditions are complicated, it is easy to affect the properties of HA and bring difficulties to the purification of the product, and a large amount of industrial wastewater is generated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing small-molecule oligomeric hyaluronic acid through enzyme method
  • Method for preparing small-molecule oligomeric hyaluronic acid through enzyme method
  • Method for preparing small-molecule oligomeric hyaluronic acid through enzyme method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The expression of embodiment 1 hyaluronidase

[0025] The modified hyaluronidase gene sequence (SEQ ID NO.1) was fully chemically synthesized, digested and ligated to the expression vector pPIC9K to construct the recombinant plasmid pPIC9K-His-HaseA3887, transformed into E.coil DH5α, and extracted for sequencing verification. The recombinant plasmid was linearized by SalI and then electroporated into the expression host P. pastoris GS115, and the recombinant clone was verified to be correct by PCR.

[0026] Recombinant P. pastoris GS115 / pPIC9K-His-HaseA3887 clone was fermented and expressed. Single clones were inoculated in 5ml of YPD medium (yeast extract 10g / L, peptone 20g / L, glucose 20g / L), and cultured at 30°C and 200rpm for 16h. Transfer to 100ml induction expression medium BMGY (yeast extract 10g / L, peptone 20g / L, 3g / L K 2 HPO 4 , 11.8g / L KH 2 PO 4 , 10×YNB100ml / L (13.4g / L), 500×biotin 1mL (4×10 -4 g / L), glycerol 10mL), cultured to OD at 30℃200rpm 600 The v...

Embodiment 2

[0027] Purification and preparation of embodiment 2 recombinant hyaluronidase

[0028] After transcription and translation, the gene shown in SEQ ID NO.1 is fused with six consecutive histidine tags at the N-terminal of hyaluronidase. According to the principle of affinity chromatography, the tag can specifically bind to dextran nickel. Nickel dextran was first equilibrated with pH 6.0, 50mM phosphate buffer for 30min, then added the fermentation broth filtered through 0.45μm, incubated at 4°C for 2h, and then used the same buffer solution to prepare 0, 10, 20, 30, 40, 50mM imidazole buffer to elute impurities. Finally, the target protein was eluted with 500mM imidazole buffer. The target protein eluted with high concentration of imidazole was dialyzed overnight. A pure hyaluronidase protein with a single band is obtained, and the obtained pure hyaluronidase protein has hyaluronidase activity after determination.

Embodiment 3

[0029] Example 3 Preparation of oligomeric hyaluronic acid octasaccharide (HA-8) and decasaccharide (HA-10)

[0030] Hyaluronidase prepared in Example 2 (pure enzyme aqueous solution, enzyme activity 2.43 × 10 5 U / mL), for large molecular weight (10 4 -10 7kDa) hyaluronic acid for hydrolysis. Hyaluronic acid (HA) was prepared at 2mg / ml with 50mM citrate buffer, pH5.5. In the 1ml reaction system, add HA solution 0.8ml, enzyme solution 8μl, and the rest with citric acid buffer (pH6.0, 50mM) to make up to 1ml system, and react at 38°C for 4h. Immediately after the reaction was completed, the enzyme was inactivated in a boiling water bath. The reaction system was filtered with a 0.22 μm filter membrane, and the molecular weight of the product was analyzed by LCMS-IT-TOF mass spectrometer. The result is as figure 1 As shown, the mass spectrum peak that appeared at 17.5min on the mass spectrum total ion current peak has an M / Z of 766.22 in negative ion mode, which is [M-2H] af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention discloses an enzymatic method for preparing small molecular oligomeric hyaluronic acid, which belongs to the technical field of bioengineering. The present invention uses hyaluronidase derived from leeches to efficiently prepare oligomeric hyaluronic acid with specific small molecular weights such as tetrasaccharides, hexasaccharides, octasaccharides and decasaccharides by hydrolyzing high-molecular hyaluronic acid. The invention lays a certain foundation for efficient preparation of specific small molecule oligomeric hyaluronic acid, and is suitable for industrial production and application.

Description

technical field [0001] The invention relates to a method for enzymatically preparing small-molecule oligomeric hyaluronic acid, which belongs to the technical field of bioengineering. Background technique [0002] Hyaluronic acid (HA for short), commonly known as hyaluronic acid, is a repeating disaccharide unit composed of D-glucuronic acid and N-acetylglucosamine, through β(1-3) and β(1-4) It is a macromolecular viscous polysaccharide formed by alternating glycosidic bonds. It was first extracted from bovine glass bulb eyes by Meyer et al. in 1934. With its unique molecular structure and physical and chemical properties, hyaluronic acid shows a variety of important physiological functions in the body, such as lubricating joints, regulating the permeability of blood vessel walls, regulating protein, water and electrolyte diffusion and operation, and promoting wound healing. More importantly, hyaluronic acid has a special water-retaining effect and is the most moisturizing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C12P19/26
Inventor 陈坚堵国成康振李江华金鹏
Owner JIANGNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap