Functional floor heating floor made of alloy materials and preparation method thereof

A functional, floor heating technology, applied in the field of building decoration materials, can solve the problems of complicated preparation process, the geothermal floor does not have fire-retardant and flame-retardant properties, and is easy to catch fire and burn, and achieves simple preparation process, good floor heating conductivity, and thermal efficiency utilization. high rate effect

Active Publication Date: 2014-01-29
安徽圣源橡塑科技有限公司
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Composite flooring is composed of multiple layers with different functions pressed and compounded by bonding technology. The preparation process is complicated, and there are disadvantages such as high energy consumption and environmental pollution; During the process, it is easy to release a certain amount of formaldehyde by heat, which is harmful to human health; during the long-term use of traditional geothermal flooring, mold will be formed on the floor surface due to dust and dirt, which will affect human health; traditional geothermal flooring, such as The long-term use of composite PVC floor will cause warping and deformation due to long-term heating use; the thermal conductivity of composite floors such as wooden floor and bamboo floor is relatively low, between 0.17-0.34w / (m*k), and the relative energy consumption is relatively long-term use; The traditional geothermal floor does not have the characteristics of fire and flame retardancy, it is easy to catch fire, and there is a safety hazard; the surface of the traditional geothermal floor has the worst wear resistance, and it is easy to form scratches after long-term use, which will affect the appearance of the floor surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Functional floor heating floor made of alloy materials and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A floor heating floor made of functional alloy materials, comprising a vacuum-coated reflective layer 4, a PVC-based polymer alloy composite material layer 3, a co-extruded composite decorative layer 2, and a UV-treated transparent antibacterial and wear-resistant layer 1 sequentially laminated from bottom to top;

[0043] Wherein, primer layer 3 comprises the component of following weight fraction:

[0044] PVC resin 100 parts

[0045] ABS resin (747S) 30 parts

[0046] Active fine calcium carbonate (1250 mesh) 80 parts

[0047] Calcium zinc composite stabilizer 5.0 parts

[0048] Flame retardant 7 parts

[0049] Processing aid ACR401 2 parts

[0050] 8 copies of CPE

[0051] Semi-refined paraffin wax 0.6 parts

[0052] 0.5 parts of stearic acid

[0053] Wherein, the main base material of the decoration layer 2 is ASA (acrylonitrile-styrene-acrylate copolymer).

[0054] Wherein, the UV coating used in the UV-treated transparent antibacteria...

Embodiment 2

[0063] A floor heating floor made of functional alloy materials, comprising a vacuum-coated reflective layer 4, a PVC-based polymer alloy composite material layer 3, a co-extruded composite decorative layer 2, and a UV-treated transparent antibacterial and wear-resistant layer 1 sequentially laminated from bottom to top;

[0064] Wherein, primer layer 3 comprises the component of following weight fraction:

[0065] PVC resin 100 parts

[0066] Glutarimide copolymer 20 parts

[0067] Active fine calcium carbonate (1250 mesh) 100 parts

[0068] Calcium zinc composite stabilizer 5.0 parts

[0069] Flame retardant 7 parts

[0070] Processing aid ACR401 2 parts

[0071] 12 copies of MBS

[0072] Semi-refined paraffin wax 0.6 parts

[0073] 0.5 parts of stearic acid

[0074] Wherein, the main base material of the decoration layer 2 is ASA (acrylonitrile-styrene-acrylate copolymer).

[0075] Wherein, the UV coating used in the UV-treated transp...

Embodiment 3

[0084] A floor heating floor made of functional sub-alloy materials, comprising a positive air coating layer 4, a PVC-based polymer alloy composite material layer 3, a co-extruded composite decorative layer 2, and a UV-treated transparent antibacterial and wear-resistant layer 1 sequentially laminated from bottom to top;

[0085] Wherein, primer layer 3 comprises the component of following weight fraction:

[0086] PVC resin 100 parts

[0087] Heat-resistant α-methylstyrene-acrylonitrile copolymer 15 parts

[0088] Active fine calcium carbonate (1250 mesh) 100 parts

[0089] Calcium zinc composite stabilizer 5.0 parts

[0090] Flame retardant 7 parts

[0091] Processing aid ACR401 2 parts

[0092] 9 copies of MBS

[0093] Semi-refined paraffin wax 0.6 parts

[0094] 0.5 parts of stearic acid

[0095] Wherein, the main body of the base material of the decoration layer 2 is PMMA (polymethyl methacrylate).

[0096] Wherein, the UV coating us...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a functional floor heating floor made of alloy materials and a preparation method thereof. The floor heating floor is structurally characterized by being of a four-layer composite structure, wherein the bottom layer is a vacuum coating reflective layer; a backing material layer is arranged on the reflective layer and made of polyvinyl chloride (PVC)-based polymer alloy composite materials; a coextru-lamination decorative layer is arranged on the backing material layer; the backing material layer and the decorative layer are integrally formed to an integral structure through a co-extrusion extrusion process; the top layer is an ultraviolet (UV) processing transparent antibacterial wear-resisting layer. The invention further discloses a method for preparing the functional floor heating floor. The method comprises the following steps of (1) blending and preparing of the backing material layer; (2) online coextru-lamination of the decorative layer and the backing material layer; (3) online embossing processing of the surface of the decorative layer; (4) vacuum coating of the surface of a board; (5) UV antibacterial wear-resisting processing of the surface layer. The method is simple in process progress. The floor heating floor prepared by the method is good in floor heating conductivity, dimension stability, antifouling and environment-friendly performance and using durability.

Description

technical field [0001] The invention relates to the field of building decoration materials, in particular to a floor heating floor made of functional alloy material and a preparation method thereof. Background technique [0002] At present, the floors traditionally selected as floor heating systems are mostly composite floors, such as composite PVC floors, solid wood composite floors, laminated floor-grade bamboo and wood floors, etc. Composite flooring is composed of multiple layers with different functions pressed and compounded by bonding technology. The preparation process is complicated, and there are disadvantages such as high energy consumption and environmental pollution; During the process, it is easy to release a certain amount of formaldehyde by heat, which is harmful to human health; during the long-term use of traditional geothermal flooring, mold will be formed on the floor surface due to dust and dirt, which will affect human health; traditional geothermal f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/02E04F15/06E04F15/10B32B33/00B32B27/30B32B27/18B32B27/20B32B15/082B32B37/02C08L27/06C08K13/06C08K9/00C08K3/26C09D5/14B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704B29C2948/92895
Inventor 王新志李明王磊张中巨
Owner 安徽圣源橡塑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products