Flame-retardant composite material and preparation method thereof

A technology of flame retardant composite materials and flame retardants, applied in the field of materials

Inactive Publication Date: 2015-02-25
SUZHOU NETABHAPE COMPOSITE MATERIALS
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen from this that this scheme is a flame retardant system composed of resin, flame retardant and nano-oxide powder. Because different resins can also cause instability, the flame retardancy of the composite is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A flame-retardant composite material, comprising the following components in parts by mass:

[0023] 30 parts of modified silicone resin, 10 parts of silicon carbide ceramic powder, 5 parts of calcined kaolin, 5 parts of molybdenum dibutyldithiocarbamate, 5 parts of ammonium polyphosphate flame retardant, 3 parts of silane coupling agent, peroxide 3 parts of benzoyl curing agent and 12 parts of water.

[0024] Among them, the silicon carbide ceramic powder is prepared by hot pressing sintering method, with an average particle size of 3um.

[0025] According to the preparation method provided by the present invention, the above-mentioned flame-retardant composite material is prepared, and the steps are as follows:

[0026] (1) Mix silicon carbide ceramic powder, calcined kaolin, molybdenum dibutyldithiocarbamate and flame retardant, grind them, and mix them uniformly to make a mixed powder material;

[0027] (2) Add the curing agent, silane coupling agent and water int...

Embodiment 2

[0030] A flame-retardant composite material, comprising the following components in parts by mass:

[0031] 50 parts of modified silicone resin, 20 parts of silicon carbide ceramic powder, 10 parts of calcined kaolin, 15 parts of molybdenum dibutyldithiocarbamate, 10 parts of melamine cyanurate flame retardant, 8 parts of silane coupling agent, peroxide 6 parts of benzoyl curing agent and 28 parts of water.

[0032] Among them, the silicon carbide ceramic powder is prepared by hot pressing sintering method, with an average particle size of 3um.

[0033] According to the preparation method provided by the present invention, the above-mentioned flame-retardant composite material is prepared, and the steps are as follows:

[0034] (1) Mix silicon carbide ceramic powder, calcined kaolin, molybdenum dibutyldithiocarbamate and flame retardant, grind them, and mix them uniformly to make a mixed powder material;

[0035] (2) Add the curing agent, silane coupling agent and water into...

Embodiment 3

[0038] A flame-retardant composite material, comprising the following components in parts by mass:

[0039] 45 parts of modified silicone resin, 15 parts of silicon carbide ceramic powder, 7 parts of calcined kaolin, 10 parts of molybdenum dibutyldithiocarbamate, 7 parts of zinc borate flame retardant, 6 parts of silane coupling agent, benzene peroxide 5 parts of formyl curing agent and 18 parts of water.

[0040] Among them, the silicon carbide ceramic powder is prepared by hot pressing sintering method, with an average particle size of 3um.

[0041] According to the preparation method provided by the present invention, the above-mentioned flame-retardant composite material is prepared, and the steps are as follows:

[0042] (1) Mix silicon carbide ceramic powder, calcined kaolin, molybdenum dibutyldithiocarbamate and flame retardant, grind them, and mix them uniformly to make a mixed powder material;

[0043] (2) Add the curing agent, silane coupling agent and water into t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a flame-retardant composite material and a preparation method thereof, relating to the technical field of materials. The composition material comprises the following compositions in parts by mass: 30-50 parts of modified organosilicon resin, 10-20 parts of silicon carbide ceramics, 5-10 parts of forged kaolin, 5-15 parts of molybdenum dibutyldithiocarbamate, 5-10 parts of flame retardant, 3-8 parts of silane coupling agent, 3-6 parts of curing agent and 12-28 parts of water. The flame-retardant composite material is a resin-ceramic flame-retardant material, not only is excellent flame-retardant, but also has better mechanical performance, is excellent in high-temperature-resistant corrosion-resistant and anti-oxidization property, and the flame retardance property of the material can be effectively guaranteed.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a flame-retardant composite material and a preparation method of the composite material. Background technique [0002] Flame retardant materials are materials that can inhibit or delay combustion but are not easy to burn themselves. Ceramic materials are a class of inorganic non-metallic materials made of natural or synthetic compounds through shaping and high-temperature sintering. It has the advantages of high melting point, high hardness, high wear resistance and oxidation resistance. Therefore, ceramics are also an excellent flame retardant material. [0003] Resin flame retardant coating material is a material with wide application prospects at present. It can better protect the substrate by using the high temperature resistance and excellent curing performance of the resin. Moreover, adding a proper flame retardant to the resin will have a better flame reta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08K13/02C08K3/34C08K5/39C08K3/32C08K3/38C08K5/3492C08K5/14
Inventor 刘莉王爽刘晓东
Owner SUZHOU NETABHAPE COMPOSITE MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap