Glass fiber reinforced polyphenylene sulfide composite with high metal bonding strength and preparation method thereof

A technology of polyphenylene sulfide and polyphenylene sulfide resin, which is applied in the field of polyphenylene sulfide resin processing and preparation, can solve the problem that the low water absorption rate, consumption, physical dielectric property, weather resistance and other related properties of polyphenylene sulfide are not obtained. Effective improvement and other problems, to achieve the effect of good product quality, simple preparation method and excellent metal bonding strength

Active Publication Date: 2015-03-11
SILVER AGE ENG PLASTICS DONGGUAN
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Chinese invention patent (CN201310363040) discloses a polyphenylene sulfide composite material and its preparation method. The composition is added by adding different types of polyamide and polyphenylene sulfide Ether forms an alloy, which improves the processing type of polyphenylene sulfide and reduces the cost. Although a composition with good comprehensive mechanical properties is obtained, it is found

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber reinforced polyphenylene sulfide composite with high metal bonding strength and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] 81.2 parts by weight of polyphenylene sulfide resin, 13 parts by weight of ethylene-butyl acrylate-glycidyl methacrylate copolymer, 1.0 parts by weight of high molecular weight hindered amine light stabilizer, and 0.25 parts by weight of pentaerythritol Dodecyl thiopropyl ester (412S), 0.25 parts by weight of tris[2.4-di-tert-butylphenyl] phosphite, 0.3 parts by weight of pentaerythritol stearate; A auxiliary agent 4 parts by weight; in a high-speed mixer Press the above components at room temperature figure 1 The process route is evenly mixed and then produced in a twin-screw extruder. Processing conditions: material mixing speed: 500 rpm; zone one temperature: 200°C, zone two temperature: 270°C, zone three temperature: 260°C, zone four temperature: 260°C, zone five temperature: 230°C, six Zone temperature: 230℃, seven zone temperature: 230℃, eight zone temperature: 260℃, nine zone temperature: 280℃, host speed: 400 rpm.

Embodiment 2

[0054] 73.2 parts by weight of polyphenylene sulfide resin, 11 parts by weight of maleic anhydride-ethylene-octene copolymer, 0.8 parts by weight of low molecular weight stereo hindered amine light stabilizer, 0.25 parts by weight of 4,4' -[1,1'-biphenyl]diphosphonic acid-tetra[2,4-di-tert-butylphenyl] ester (PEPQ), 0.25 parts by weight of tris[2.4-di-tert-butylphenyl] Phosphate ester, 0.3 parts by weight of a mixture of stearic acid and calcium stearate; A auxiliary agent: 4 parts by weight; press the above components in a high-speed mixer at room temperature figure 1 The process route is uniformly mixed, and then produced in a twin-screw extruder. Continuous glass fiber is added from the middle of the twin-screw, and the glass fiber content is controlled to 10. Processing conditions: material mixing speed: 500 rpm; zone one temperature: 200°C, zone two temperature: 300°C, zone three temperature: 290°C, zone four temperature: 280°C, zone five temperature: 210°C, six Zone tempe...

Embodiment 3

[0056] 66.6 parts by weight of polyphenylene sulfide resin, 9 parts by weight of maleic anhydride-ethylene-octene copolymer, 0.6 parts by weight of benzotriazole ultraviolet absorber, 0.2 parts by weight of 4,4'-[1, 1'-Biphenyl]ylidene diphosphonic acid-tetra[2,4-di-tert-butylphenyl] ester (PEPQ), 0.2 parts by weight of tris[2.4-di-tert-butylphenyl] phosphite, 0.4 Parts by weight of montan wax; 3 parts by weight of A auxiliary; press the above components in a high-speed mixer at room temperature figure 1 The process route is uniformly mixed, and then produced in a twin-screw extruder. Continuous glass fiber is added from the middle of the twin-screw, and the glass fiber content is controlled to 20. The mixing speed of the materials is: 500 rpm; temperature in zone one: 200°C, temperature in zone two: 300°C, temperature in zone three: 290°C, temperature in zone four: 280°C, temperature in zone five: 210°C, temperature in zone six: 210℃, seven zone temperature: 210℃, eight zone t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the polyphenylene sulfide resin processing preparation field, and in particular relates to a glass fiber reinforced polyphenylene sulfide composite with high metal bonding strength and a preparation method thereof; the glass fiber reinforced polyphenylene sulfide composite comprises the following raw materials by weight: 51.7-81.2 parts of polyphenylene sulfide resin, 0-40 parts of continuous glass fiber; 5-13 parts of a toughening agent; 0.2-1 part of a weathering agent; 0.3-0.5 part of an antioxidant; 0.3-0.5 part of a lubricant and 2-4 parts of an additive A, the glass fiber reinforced polyphenylene sulfide composite not only has excellent weathering properties and excellent metal bonding strength, after metal bonding and anode oxidation treatment, the glass fiber reinforced polyphenylene sulfide composite may not discolor, the bonding strength decay is small, the glass fiber reinforced polyphenylene sulfide composite also has excellent weather resistance and low dielectric properties and loss factor, can satisfy the customer demand of different colors, and greatly improves the product appearance design freedom degree.

Description

technical field [0001] The invention relates to the field of polyphenylene sulfide resin processing and preparation, in particular to a glass fiber reinforced polyphenylene sulfide compound with high bonding strength with metal and a preparation method thereof. Background technique [0002] In recent years, with the diversification of people's demand for the appearance of electronic products, the appearance quality of electronic products is constantly changing. The single metal or plastic casing of electronic products can no longer meet the diversified market needs. Combined electronic product casings have become people's new favorite. At present, some of the more popular electronic product bodies on the market are the products of the combination technology of aluminum alloy surface treatment and resin polymer. [0003] Polyphenylene sulfide resin (PPS), also known as polyphenylene sulfide, PPS plastic is a light yellow, brown, high crystallinity, hard and brittle polymer. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L81/02C08L23/08C08K13/04C08K7/14C08K3/32C08K3/34B29C47/92B29C48/92
CPCB29C48/92B29C2948/9258B29C2948/92704C08K2201/003C08L81/02C08L2205/03C08L2205/035C08L23/0884C08K13/04C08K7/14C08K5/372C08K5/526C08K5/103C08K2003/321C08K3/34C08L35/00C08K5/5333C08K5/09C08K5/098C08L91/06
Inventor 李小辉傅轶唐昌伟
Owner SILVER AGE ENG PLASTICS DONGGUAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap