Liquid rubber modified nitrile rubber cable material

A technology of nitrile rubber and liquid rubber, which is applied in the direction of rubber insulators and organic insulators, can solve the problems of short service life of cable materials, aging resistance, elasticity and toughness that cannot meet the requirements of society, and threaten the safety of life and property. Good aging resistance, excellent elasticity and toughness, and long service life

Inactive Publication Date: 2015-05-13
无为县茂林电缆材料有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of the economy, there are strict requirements on the performance of cables. The aging resistance, elasticity and toughness of traditional nitrile rubber cable materials cannot meet the requirements of the society, resulting in a short service life of the cable materials, which brings great harm to the actual use. Therefore, it is necessary to improve the existing nitrile rubber cable materials to meet the diverse requirements of the cable market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The liquid rubber modified nitrile rubber cable material of the present invention, its raw material comprises the following components by weight: 95 parts of nitrile rubber, 5 parts of liquid isoprene rubber, 12 parts of benzoxazine resin, superfine acrylic acid 5 parts of ester rubber powder, 8 parts of silicone polyurethane oligomer, 12 parts of white carbon black, 20 parts of hydrotalcite, 10 parts of four needle-shaped zinc oxide whiskers, 35 parts of nano silicon dioxide, 0.8 parts of zinc oxide, methyl 1.5 parts of zinc acrylate, 0.3 parts of zinc gluconate, 4.5 parts of stearic acid, 0.8 parts of sulfur, 1 part of N, N'-m-phenylene bismaleimide, 0.9 parts of triallyl isocyanurate , 3 parts of styrene-ethylene-butadiene block copolymer, 2.5 parts of propylene glycol sebacate polyester, 0.8 parts of glyceryl distearate, 2.5 parts of zinc stearate, 1 part of calcium stearate, vinyl 5 parts of triethoxysilane, 0.5 parts of accelerator, and 3 parts of anti-aging agent...

Embodiment 2

[0016]The liquid rubber modified nitrile rubber cable material of the present invention, its raw material comprises the following components by weight: 85 parts of nitrile rubber, 15 parts of liquid isoprene rubber, 3 parts of benzoxazine resin, superfine acrylic acid 13 parts of ester rubber powder, 2 parts of silicone polyurethane oligomer, 30 parts of white carbon black, 5 parts of hydrotalcite, 20 parts of tetraacicular zinc oxide whiskers, 10 parts of nano silicon dioxide, 2.0 parts of zinc oxide, methyl 0.5 parts of zinc acrylate, 0.8 parts of zinc gluconate, 2.5 parts of stearic acid, 2.0 parts of sulfur, 2.5 parts of N, N'-m-phenylene bismaleimide, 0.2 parts of triallyl isocyanurate , 10 parts of styrene-ethylene-butadiene block copolymer, 1 part of propylene glycol sebacate polyester, 2 parts of glyceryl distearate, 1 part of zinc stearate, 2 parts of calcium stearate, vinyl 2 parts of triethoxysilane, 1.8 parts of accelerator, and 1 part of anti-aging agent.

Embodiment 3

[0018] The liquid rubber modified nitrile rubber cable material of the present invention, its raw material comprises the following components by weight: 88 parts of nitrile rubber, 12 parts of liquid isoprene rubber, 7 parts of benzoxazine resin, superfine acrylic acid 11 parts of ester rubber powder, 5.6 parts of silicone polyurethane oligomer, 26 parts of white carbon black, 8 parts of hydrotalcite, 18 parts of tetraacicular zinc oxide whiskers, 22 parts of nano silicon dioxide, 1.6 parts of zinc oxide, methyl 0.9 parts of zinc acrylate, 0.63 parts of zinc gluconate, 3.2 parts of stearic acid, 1.7 parts of sulfur, 2.0 parts of N,N'-m-phenylene bismaleimide, 0.56 parts of triallyl isocyanurate , 8 parts of styrene-ethylene-butadiene block copolymer, 2.0 parts of propylene glycol sebacate, 1.4 parts of glyceryl distearate, 2.1 parts of zinc stearate, 1.6 parts of calcium stearate, vinyl 2.7 parts of triethoxysilane, 1.4 parts of accelerator, and 1.9 parts of anti-aging agent. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a liquid rubber modified nitrile rubber cable material. The liquid rubber modified nitrile rubber cable material comprises raw materials as follows: nitrile rubber, liquid isoprene rubber, benzoxazine resin, superfine acrylate rubber powder, an organic silicon polyurethane oligomer, silica, hydrotalcite, tetrapod-shaped zinc oxide whiskers, nanosilicon dioxide, zinc oxide, zinc methacrylate, zinc gluconate, stearic acid, sulfur, N, N'-M-phenylene dimaleimide, triallyl isocyanurate, styreneic bock copolymers, propanediol sebacate polyester, glycerol distearates, zinc stearate, calcium stearate, ethenyl triethoxysilane, an accelerant and an anti-aging agent. The liquid rubber modified nitrile rubber cable material has high strength, excellent elasticity and rigidity, good ageing resistance and long service life.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a liquid rubber modified nitrile rubber cable material. Background technique [0002] Nitrile rubber is prepared by emulsion polymerization of butadiene and acrylonitrile. It has high oil resistance, abrasion resistance, good heat resistance and strong adhesion. It has been widely used in cable materials. With the development of the economy, there are strict requirements on the performance of cables. The aging resistance, elasticity and toughness of traditional nitrile rubber cable materials cannot meet the requirements of the society, resulting in a short service life of the cable materials, which brings great harm to the actual use. Therefore, it is necessary to improve the existing nitrile rubber cable materials to meet the diverse requirements of the cable market. Contents of the invention [0003] The invention provides a liquid rubber modified nitrile rubber cabl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L9/00C08L79/04C08L33/04C08L75/04C08L53/02C08K13/04C08K3/36C08K3/26C08K7/08C08K5/103C08K5/098C08K5/5425H01B3/28
CPCC08L9/02C08K2201/011C08K2201/014C08L2203/202C08L2205/035H01B3/28
Inventor 叶显林
Owner 无为县茂林电缆材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com