Carbon nanotube composite chromium plating solution and electroplating method

A carbon nanotube composite and carbon nanotube technology, applied in electrolytic coatings, coatings, etc., can solve the problems of low hardness of the coating, insufficient friction resistance, and restrictions on the large-scale application of chromium electroplating, and achieve the effect of improving the quality of the coating

Inactive Publication Date: 2015-05-13
WUXI XUEJIANG ENVIRONMENT ENG EQUIP
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, chromium-based electroplating is difficult to achieve nanocomposite electroplating due to the limitation of various technical factors.
In order to make up for defects such as low chromium hardness, alloy metal elements or non-metallic elements are often added to the electroplating solution. Although the quality of the coating is improved to a certain extent, there are still problems such as low hardness of the coating, insufficient friction resistance, and poor corrosion resistance. Ideal technical defects, these seriously restrict the large-scale application of chrome plating in industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon nanotube composite chromium plating solution and electroplating method
  • Carbon nanotube composite chromium plating solution and electroplating method
  • Carbon nanotube composite chromium plating solution and electroplating method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] (1) Preparation of nano-dispersion. Using self-made carbon nanotubes that have been cleaned of impurities, the preparation method of carbon nanotubes and the specific process of removing impurities have been described above, and will not be repeated here. Add the fatty alkyl methyl halide and alkylbenzene sulfonate into the three-necked flask to dissolve and then stir with a mixer at low speed for several minutes. Then, transfer it to a large beaker and install the GR-I shear disperser of Chengdu Xindu Yongtong Machinery Factory, add the powder of carbon nanotubes into the three-necked flask, and adjust the speed of the shear disperser to 300-500rpm , the shear dispersion time is 5-10 minutes, then the rotation speed is adjusted to 1500-2000 rpm, and the shear dispersion time is 10-15 minutes to obtain the nano slurry. The average particle size of the nano-dispersion was tested by a Mastersizer 2000 laser particle size analyzer from Malvern.

[0033] (2) Weigh the mas...

Embodiment 1

[0039] The formula of carbon nanotube composite chromium electroplating solution is as follows:

[0040]

[0041] In the nano-dispersion liquid preparation, the rotating speed of low-speed shear dispersion is 300rpm, and the time of low-speed shear dispersion is 5min; the rotational speed of high-speed shear dispersion is 1500rpm, and the time of high-speed shear dispersion is 10min; the ultrasonic dispersion power is 600W, The time of ultrasonic dispersion is 6min, and the average particle size of carbon nanometer in the prepared dispersion is 30nm; the plating process conditions: the pulse width of single pulse square wave current is 1ms, the duty cycle is 30%, and the average current density is 4A / dm 2 ; The pH is 2.5, the temperature is 25°C, and the electroplating time is 120min.

Embodiment 2

[0043] The formula of carbon nanotube composite chromium electroplating solution is as follows:

[0044]

[0045] In the nano-dispersion liquid preparation, the rotating speed of low-speed shear dispersion is 500rpm, and the time of low-speed shear dispersion is 10min; the rotational speed of high-speed shear dispersion is 2000rpm, and the time of high-speed shear dispersion is 15min; the ultrasonic dispersion power is 1000W, The time of ultrasonic dispersion is 3min, and the average particle size of carbon nanometer in the prepared dispersion is 40nm; the plating process conditions: the pulse width of single pulse square wave current is 1ms, the duty ratio is 25%, and the average current density is 5A / dm 2 ; The pH is 3, the temperature is 30°C, and the electroplating time is 100min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a carbon nanotube composite chromium plating solution and an electroplating method. The carbon nanotube composite chromium plating solution comprises the following components by content: 150-210g / L chromic chloride hexahydrate, 120-140g / L citrate, 40-60g / L oxalate, 60-90g / L urea, 10-20g / L formic acid, 90-120g / L ammonium bromide, 8-18g / L carbon nanotube, 0.3-0.6g / L fatty alkyl methyl halide salt and 0.1-0.2g / L alkylbenzene sulfonate. The plating solution contains carbon nanotube, due to self rigidity of carbon nanotube, the hardness and wear resistance of a plating layer are increased; on one hand, permeation of a corrosion solution can be prevented by filling the aperture of a plating layer and winding the metal crystal grain surface by carbon nanotube, on the other hand, a minisize primary battery is formed by nano WC and the alloy metal microcrystal, passivation of chromium can be promoted, and corrosion resistance is increased.

Description

technical field [0001] The invention relates to the technical field of chromium electroplating technology, in particular to a carbon nanotube composite chromium electroplating solution and an electroplating method. Background technique [0002] Cr is a silver-white metal with a slight bluish tint. It is easily passivated in the air, and the surface is covered with an oxide film. It has good corrosion resistance, is stable in the atmosphere, and can maintain its luster for a long time; , Sulfide, carbonate solution and organic acid are very stable. Cr has high hardness, small friction coefficient, good wear resistance, corrosion resistance and heat resistance. The Cr coating has the advantages of bright surface, high hardness, and corrosion resistance. It is a good protective and decorative coating, and is widely used in many fields such as automobiles and aerospace. However, the Cr coating will become soft at higher temperatures, and the hardness value begins to decrease a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/06C25D15/00C25D5/18
CPCC25D3/06C25D5/18C25D15/00
Inventor 曾雄燕
Owner WUXI XUEJIANG ENVIRONMENT ENG EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com