Preparation method of aluminum-based silicon carbide

An aluminum-based silicon carbide and slurry technology, which is applied in metal processing equipment, transportation and packaging, etc., can solve the problems of many restrictions, uneven material, low product density, etc., to improve sintering performance, reduce sintering temperature, composition evenly distributed effect

Active Publication Date: 2017-08-04
李大海
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the patent CN102618740A, a method for preparing silicon carbide aluminum matrix composite materials by powder metallurgy is reported. This method has cumbersome process, low production efficiency, high cost, and the obtained product has low density, uneven material, low mechanical properties, and is not easy to form. Shortcomings such as thin walls; In the patent CN103160702A, a method for in-situ composite preparation of silicon carbide particle-reinforced aluminum-based composite materials is disclosed. After mechanical mixing, in-situ generation of silicon carbide powder reinforced aluminum matrix composites in the vacuum sintering process has many limitations, high cost, unsuitable for large-scale production, high raw material requirements, and cumbersome processes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of aluminum-based silicon carbide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A preparation method of aluminum-based silicon carbide:

[0052] 1) Preparation of SiC / Al slurry:

[0053]First, according to SiC micropowder 50wt%, 7wt% plasticizer, 3wt% dispersant, 10% and 40wt% water ratio, the SiC slurry with a solid content of 50% is prepared, wherein the plasticizer is polyethylene glycol, The dispersant is polymethacrylic acid amine; the average particle size of SiC micropowder is 7 microns;

[0054] Then add aluminum powder according to the mass ratio of SiC:Al=1:1, the average particle size of aluminum powder is 13 microns, ball mill for 16 hours, and mix uniformly to obtain SiC / Al slurry.

[0055] 2) Tape casting:

[0056] After vacuum defoaming the SiC / Al slurry obtained in step 1), add 1% of the ammonium persulfate initiator and 2% of the acrylamide monomer by weight of the slurry, mix evenly, and cast to obtain SiC / Al Al cast film.

[0057] 3) Bisque firing the cast film at 300°C to obtain a SiC / Al biscuit;

[0058] 4) Vacuum sinterin...

Embodiment 2

[0060] A preparation method of aluminum-based silicon carbide:

[0061] 1) Preparation of SiC / Al slurry:

[0062] First according to SiC micropowder 55wt%, the plasticizer of 10wt%, the dispersant of 1wt% and the water ratio of 34wt% prepare the SiC slurry that solid content is 55%, wherein plasticizer is by polyvinylpyrrolidone: polyvinyl alcohol: Glycerin=1:1:2 volume ratio composition, dispersant is ammonium citrate; SiC micropowder average particle size is 10 microns;

[0063] Then add aluminum powder and magnesium powder according to the mass ratio of SiC: Al: Mg=2: 1: 0.4, wherein the average particle diameter of aluminum powder is 20 microns, the average particle diameter of magnesium powder is 16 microns, ball milling 20h, mix uniformly, obtain SiC / Al paste.

[0064] 2) Tape casting:

[0065] After vacuum defoaming the SiC / Al slurry obtained in step 1), add 3% of the ammonium persulfate initiator and 4% of the acrylamide monomer by weight of the slurry, mix evenly, ...

Embodiment 3

[0069] A preparation method of aluminum-based silicon carbide:

[0070] 1) Preparation of SiC / Al slurry:

[0071] First according to SiC micropowder 60wt%, the plasticizer of 2wt%, the dispersant of 5wt% and the water ratio of 33wt% are prepared to obtain the SiC slurry that solid content is 60%, wherein plasticizer is by polyethylene glycol: glycerin=1 : 1 volume ratio, the dispersant is ammonium polyacrylate; the average particle diameter of the SiC micropowder is 3 microns;

[0072] Then add aluminum powder and magnesium powder according to the mass ratio of SiC: Al: Mg=1.5: 1: 0.37, wherein the average particle diameter of aluminum powder is 5 microns, the average particle diameter of magnesium powder is 5 microns, ball milling 10h, mix uniformly, A SiC / Al slurry was obtained.

[0073] 2) Tape casting:

[0074] After vacuum defoaming the SiC / Al slurry obtained in step 1), add 2% of the ammonium persulfate initiator and 3% of the acrylamide monomer by weight of the slurr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A method for preparing aluminum-based silicon carbide, comprising steps: step 1, preparing SiC / Al slurry, using SiC micropowder to prepare SiC slurry, then adding aluminum powder and magnesium powder in proportion and mixing them uniformly; step 2, casting Forming, after defoaming the SiC / Al slurry, adding 1-3% of the initiator and 2-4% of the monomer by the total weight of the SiC / Al slurry, mixing evenly, and casting to obtain a SiC / Al cast film; Step 3, bisque firing of the cast film, bisque firing of the cast film obtained in step 2 to obtain a SiC / Al biscuit; step 4, vacuum sintering, sintering the SiC / Al biscuit in a vacuum state to obtain an aluminum-based carbonized silicon. The invention prepares the aluminum-based aluminum nitride by adopting the gel casting method, and the obtained product has uniform distribution of components, low porosity and high thermal conductivity, and the sintering performance is improved and the sintering temperature is lowered by introducing magnesium powder. The process involved in the invention is simple, and the energy consumption is less.

Description

technical field [0001] The invention relates to the technical field of manufacturing heat dissipation materials for light-emitting diodes, and more specifically relates to a method for preparing aluminum-based silicon carbide. Background technique [0002] With the leap of LED manufacturing technology and the higher performance requirements of devices, newer and higher requirements are put forward for packaging materials, and traditional materials are no longer suitable for the packaging of high power density devices. The aluminum, copper, kovar materials or semiconductor materials used in large quantities in the past cannot meet the requirements of good thermal conductivity and lightness, and the cost is high, which can no longer meet the needs of the existing high power density, which makes the thermal management of electronic devices an important issue. bottleneck. [0003] If the thermal management of electronic devices is not well resolved, it will lead to thermal fail...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/05C22C29/06C22C30/00C22C32/00
CPCC22C1/051C22C29/06C22C30/00C22C32/0052B22F3/1003B22F2998/10B22F1/10B22F3/22
Inventor 李大海彭建勋李钰
Owner 李大海