Graphene-oxide-modified polypropylene composite material

A graphene modification and composite material technology, applied in the field of polypropylene materials, can solve the problem that the strength, heat resistance, flame retardancy and stability cannot meet the needs of the society, poor dimensional stability, and poor thermal stability To achieve the effects of improving thermal stability and impact resistance, promoting char formation rate, improving stability and weather resistance

Inactive Publication Date: 2016-06-15
ANHUI LANTONG TECH CO LTD
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional polypropylene has low mechanical strength, low oxygen index, is easy to burn, has poor thermal stability, and poor dimensional stability. The existing polypropylene composite materials have low strength, heat resistance, flame retardancy and stability often fail to meet the needs of society

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017]A kind of graphene oxide modified polypropylene composite material proposed by the present invention, its raw material comprises the following components by weight: 60 parts of graphene oxide modified polypropylene, 20 parts of EPDM rubber, butadiene-acrylonitrile 1 part of copolymer, 10.3 parts of silane coupling agent KH-150.5 parts, 0.5 parts of silane coupling agent KH-6020.2 parts, 2 parts of zinc borate, 12 parts of magnesium hydroxide, 1 part of pentaerythritol, epoxy resin 3 parts of soybean oil, 1.5 parts of tricresyl phosphate, 0.3 parts of pentaerythritol stearate, 5 parts of yttrium oxide, 5 parts of nano-mica powder, 15 parts of talc powder, 1 part of micro-silica powder, dimethicone (3,4-dimethyl Base) 1.5 parts of benzyl sorbitol, 0.1 parts of 2,2'-methylenebis(4,6-di-tert-butylphenyl) sodium phosphate, 0.5 parts of ethylene-octene copolymer, 2-hydroxy-4 - 0.1 part of n-octyloxybenzophenone.

Embodiment 2

[0019] A kind of graphene oxide modified polypropylene composite material proposed by the present invention, its raw material comprises the following components by weight: graphene oxide modified polypropylene 100 parts, EPDM rubber 5 parts, butadiene-acrylonitrile 5 parts of copolymer, 0.1 parts of silane coupling agent KH-5700, 10 parts of zinc borate, 2 parts of magnesium hydroxide, 3.5 parts of pentaerythritol, 12 parts of epoxy soybean oil, 0.3 parts of tricresyl phosphate, 1.5 parts of pentaerythritol stearate , 1 part of yttrium oxide, 15 parts of nano mica powder, 2 parts of talc powder, 2.5 parts of microsilica powder, 0.2 part of di(3,4-dimethyl)benzyl sorbitol, 2,2'-methylene 0.5 parts of sodium bis(4,6-di-tert-butylphenyl)phosphate, 0.1 parts of ethylene-octene copolymer, and 0.5 parts of 2-hydroxy-4-n-octyloxybenzophenone;

[0020] Wherein, the graphene oxide modified polypropylene is prepared according to the following process: 100 parts of polypropylene, 10 part...

Embodiment 3

[0022] A kind of graphene oxide modified polypropylene composite material proposed by the present invention, its raw material comprises the following components by weight: graphene oxide modified polypropylene 80 parts, EPDM rubber 14 parts, butadiene-acrylonitrile 3 parts of copolymer, 0.8 parts of silane coupling agent Si-42, 7 parts of zinc borate, 10 parts of magnesium hydroxide, 2 parts of pentaerythritol, 10 parts of epoxy soybean oil, 0.9 parts of tricresyl phosphate, 1.1 parts of pentaerythritol stearate , 3.5 parts of yttrium oxide, 11 parts of nano-mica powder, 7 parts of talc powder, 2.3 parts of micro-silica powder, 0.9 parts of di(3,4-dimethyl)benzyl sorbitol, 2,2'-methylene 0.4 parts of bis(4,6-di-tert-butylphenyl)sodium phosphate, 0.3 parts of ethylene-octene copolymer, 0.43 parts of 2-hydroxy-4-n-octyloxybenzophenone;

[0023] Wherein, the graphene oxide modified polypropylene is prepared according to the following process: 100 parts of polypropylene, 25 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a graphene-oxide-modified polypropylene composite material which is prepared from graphene-oxide-modified polypropylene, ethylene propylene diene monomer rubber, a butadiene-acrylonitrile copolymer, a silane coupling agent, zinc borate, magnesium hydroxide, pentaerythritol, epoxy soybean oil, tritolyl phosphate, pentaerythritol stearate, yttrium oxide, nano mica powder, talcum powder, silicon micropowder, 1,3,2,4-di(3,4-dimethylbenzylidene)sorbitol, an ethylene-octylene copolymer and 2-hydroxy-4-n-octyloxy diphenyl ketone. The graphene-oxide-modified polypropylene composite material has the advantages of high strength, excellent heat resistance, excellent flame retardancy and favorable heat stability.

Description

technical field [0001] The invention relates to the technical field of polypropylene materials, in particular to a graphene oxide modified polypropylene composite material. Background technique [0002] As a thermoplastic resin with excellent comprehensive performance, polypropylene (PP) has the advantages of abundant raw material sources, good mechanical properties, low density and good chemical stability. At present, it is widely used in chemical industry, construction, electric power, automobile, machinery, textile, medical , packaging and building materials and furniture industries have been widely used. However, traditional polypropylene has low mechanical strength, low oxygen index, is easy to burn, has poor thermal stability, and poor dimensional stability. The existing polypropylene composite materials have low strength, heat resistance, flame retardancy and stability Often cannot meet the needs of society. In order to overcome and improve the defects of polypropyl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/16C08L9/02C08L91/00C08L23/08C08L13/00C08K13/02C08K3/04C08K3/38C08K3/22C08K5/053C08K5/523C08K5/103C08K3/34C08K3/36
CPCC08L23/12C08K2201/011C08K2201/014C08L2201/02C08L2201/04C08L2201/08C08L2205/035C08L2205/24C08L23/16C08L9/02C08L91/00C08L23/0815C08L13/00C08K13/02C08K3/04C08K2003/387C08K2003/2224C08K5/053C08K5/523C08K5/103C08K2003/221C08K3/34C08K3/36
Inventor 谭中全
Owner ANHUI LANTONG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap