Flame retardation and antibiosis fabric

A kind of antibacterial fabric and fabric technology, which is applied in the direction of fireproof coating, antifouling/underwater coating, coating, etc., can solve the problems of easy wrinkle and deformation, and achieve the effect of improving product performance and superior flame retardancy

Inactive Publication Date: 2016-10-12
李红玉
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, natural fabrics such as pure cotton, pure wool, pure silk, and pure hemp have been reduced to general fabrics because of their shortcomings such as easy to wrinkle and deform, and are rarely used as high-end clothing materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame retardation and antibiosis fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The flame-retardant and antibacterial fabric in this embodiment is bonded with a protective coating on the linen fabric, and the coating is composed of the following components in parts by mass: 18 parts of a-olefin elastomer, 16 parts of polymethyl methacrylate , 16 parts of isoprene rubber, 14 parts of tall oil fatty acid, 16 parts of butyl acetate, 16 parts of allyl sulfide, 14 parts of diethylene glycol ethyl ether, 16 parts of diethylene glycol butyl ether, 16 parts of propiconazole, 14 parts of sodium monofluorophosphate, 14 parts of dodecyl ethoxy sulfobetaine, 14 parts of dimethyl fumarate, 16 parts of cuprous chloride, 14 parts of metatitanic acid, 12 parts of silicon carbide fiber, benzene 16 parts of triethoxysilane, 14 parts of chromium oxide green, 12 parts of chromium chloride, 14 parts of barium chromate powder, 12 parts of sodium cellulose, 12 parts of trimethyl phosphate, 14 parts of polyacrylonitrile fiber, disalt 14 parts of basic lead stearate, 14 pa...

Embodiment 2

[0022] The flame-retardant and antibacterial fabric in this embodiment is bonded with a protective coating on the linen fabric, and the coating is composed of the following components in parts by mass: 20 parts of α-olefin elastomer, 18 parts of polymethyl methacrylate , 18 parts of isoprene rubber, 16 parts of tall oil fatty acid, 18 parts of butyl acetate, 18 parts of allyl sulfide, 16 parts of diethylene glycol ethyl ether, 18 parts of diethylene glycol butyl ether, 18 parts of propiconazole, 16 parts of sodium monofluorophosphate, 16 parts of dodecyl ethoxy sulfobetaine, 16 parts of dimethyl fumarate, 18 parts of cuprous chloride, 16 parts of metatitanic acid, 14 parts of silicon carbide fiber, benzene 18 parts of triethoxysilane, 16 parts of chromium oxide green, 14 parts of chromium chloride, 16 parts of barium chromate powder, 14 parts of sodium cellulose, 14 parts of trimethyl phosphate, 16 parts of polyacrylonitrile fiber, disalt 16 parts of basic lead stearate, 16 pa...

Embodiment 3

[0028] The flame-retardant and antibacterial fabric in this embodiment is bonded with a protective coating on the linen fabric, and the coating is composed of the following components in parts by mass: 22 parts of α-olefin elastomer, 20 parts of polymethyl methacrylate , 20 parts of isoprene rubber, 18 parts of tall oil fatty acid, 20 parts of butyl acetate, 20 parts of allyl sulfide, 18 parts of diethylene glycol ethyl ether, 20 parts of diethylene glycol butyl ether, 20 parts of propiconazole, 18 parts of sodium monofluorophosphate, 18 parts of dodecyl ethoxy sulfobetaine, 18 parts of dimethyl fumarate, 20 parts of cuprous chloride, 18 parts of metatitanic acid, 16 parts of silicon carbide fiber, benzene 20 parts of triethoxysilane, 18 parts of chromium oxide green, 16 parts of chromium chloride, 18 parts of barium chromate powder, 16 parts of sodium cellulose, 16 parts of trimethyl phosphate, 18 parts of polyacrylonitrile fiber, di-salt 18 parts of basic lead stearate, 18 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a flame retardation and antibiosis fabric. A gunny cloth fabric is bonded with a protection coating layer, and the coating layer comprises a-olefin elastomer, polymethyl methacrylate, isoprene rubber, tall oil fatty acid, butyl acetate, allyl sulfide, diethylene glycol diethyl ether, diethylene glycol butyl ether, propiconazole, sodium monofluorophosphate, dodecyl ethoxy sulfobetaine, dimethyl fumarate, cuprous chloride, metatitanic acid, silicon carbide fibers, phenyltriethoxysilane, chromium oxide green, chromium chloride, barium chromate powder, sodium cellulosate, trimethyl phosphate, polyacrylonitrile fibers, dibasic lead stearate, tris(butoxyethyl)phosphate, starch ether, vinyltris(beta-methoxyethoxy)silane, ethylamine, diethylenetriamine, alkylphenol polyoxyethylene and divinyl benzene. The flame retardation and antibiosis fabric has superior flame, acid-alkali, mildew and bacterium resistance, and improved performances.

Description

technical field [0001] The invention relates to a flame-retardant and antibacterial fabric, which belongs to the technical field of fabrics. Background technique [0002] Clothing is made of fabric, and fabric is the material used to make clothing. As one of the three elements of clothing, fabrics can not only interpret the style and characteristics of clothing, but also directly affect the color and shape of clothing. Showing its own noble perfection, soft to the touch. In the big world of clothing, the fabrics of clothing are varied and changing with each passing day. But generally speaking, high-quality and high-end fabrics mostly have the characteristics of comfortable wearing, sweat-absorbing and breathable, crisp drape, noble vision, and soft touch. Modern clothing worn on formal social occasions mostly uses high-quality blended fabrics. However, natural fabrics such as pure cotton, pure wool, pure silk, and pure hemp have been reduced to general fabrics due to the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D5/18C09D5/14C09D7/12D06N3/00D06N3/04
CPCC09D4/06C09D5/14C09D5/18C09D7/61C09D7/63C09D7/65C09D7/70D06N3/0002D06N3/04D06N2201/045
Inventor 不公告发明人
Owner 李红玉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap