Polyvinyl chloride cable material resistant to heat and shock

A polyvinyl chloride cable and polyvinyl chloride technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problem of limiting the use of polyvinyl chloride cable materials, poor thermal stability, high brittleness of polyvinyl chloride, etc. problems, to achieve the effects of reducing the rate of thermal weight loss, inhibiting catalytic degradation, and enhancing the pinning effect

Inactive Publication Date: 2016-11-16
ANHUI ELECTRIC GRP SHARES
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, polyvinyl chloride has the defects of high brittleness, poor impact resistance, and its thermal stability is not very ideal, which limits the use of polyvinyl chloride cable materials and makes it have the defect of short service life in the process of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A heat-resistant and impact-resistant polyvinyl chloride cable material proposed by the present invention, its raw materials include by weight: 60 parts of polyvinyl chloride, 10 parts of polyurethane, 20 parts of bisphenol A polycarbonate, 5 parts of polybutylene succinate 10 parts of bis(2-ethylbutyrate) triethylene glycol, 1 part of epoxy octyl stearate, 12 parts of montmorillonite, 4 parts of ammonium heptamolybdate, 25 parts of kaolin, 0.5 parts of aluminum hydroxide 8 parts of basic magnesium sulfate whiskers, 0.01 parts of antioxidant, 2.5 parts of 1-amino-4-methylpiperazine, 2 parts of trimethylolpropane trimethacrylate, 2 parts of bis-ferrocenyl acetylene 8 parts, heat stabilizer 8 parts;

[0017] Wherein, the heat stabilizer consists of 20 parts by weight of rhenium complex, 3 parts by weight of cerium carbonate, 8 parts by weight of tribasic lead sulfate, 12 parts by weight of bisphenol A diglycidyl ether, 2 parts by weight of cyclic Butyl oxystearate, 20 pa...

Embodiment 2

[0019] A heat-resistant and impact-resistant polyvinyl chloride cable material proposed by the present invention, its raw materials include by weight: 40 parts of polyvinyl chloride, 25 parts of polyurethane, 5 parts of bisphenol A polycarbonate, 15 parts of polybutylene succinate 2 parts, 2 parts of ethylene glycol tri(2-ethylbutyrate), 8 parts of epoxy octyl stearate, 3 parts of montmorillonite, 13 parts of ammonium heptamolybdate, 10 parts of kaolin, 1.3 parts of aluminum hydroxide 1 part, 2 parts of basic magnesium sulfate whiskers, 1 part of antioxidant, 0.5 part of 1-amino-4-methylpiperazine, 1 part of trimethylolpropane trimethacrylate, 8 parts of bis-ferrocenyl acetylene 3 parts, heat stabilizer 3 parts;

[0020] Wherein, the heat stabilizer consists of 5 parts by weight of rhenium complex, 15 parts by weight of cerium carbonate, 8 parts by weight of tribasic lead sulfate, 3 parts by weight of bisphenol A diglycidyl ether, 15 parts by weight of cyclic Butyl oxystearat...

Embodiment 3

[0022] A heat-resistant and impact-resistant polyvinyl chloride cable material proposed by the present invention, its raw materials include by weight: 52 parts of polyvinyl chloride, 16 parts of polyurethane, 17 parts of bisphenol A polycarbonate, and 12 parts of polybutylene succinate. 4.5 parts of bis(2-ethylbutyrate) triethylene glycol, 4 parts of epoxy octyl stearate, 5.8 parts of montmorillonite, 10 parts of ammonium heptamolybdate, 16 parts of kaolin, 1.1 parts of aluminum hydroxide 4.6 parts of basic magnesium sulfate whiskers, 0.3 parts of antioxidant 246, 0.4 parts of antioxidant BHT, 1.3 parts of 1-amino-4-methylpiperazine, 1.68 parts of trimethylolpropane trimethacrylate , 4.9 parts of bis-ferrocenyl acetylene, 6.2 parts of heat stabilizer;

[0023] Wherein, the heat stabilizer consists of 11 parts by weight of rhenium complex, 10 parts by weight of cerium carbonate, 3.2 parts by weight of tribasic lead sulfate, 7 parts by weight of bisphenol A diglycidyl ether, 8 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyvinyl chloride cable material resistant to heat and shock. The polyvinyl chloride cable material resistant to heat and shock is prepared from polyvinyl chloride, polyurethane, bisphenol-A polycarbonate, poly (tetramethylene succinate), di (2-ethylbutanoic acid) triuret gylcol ester, 2-ethylhexyl epoxystearate, montmorillonite, ammonium heptamolybdate, kaolin, aluminum hydroxide, magnesium hydroxide whisker, antioxidant, 1-azyl-4-methyl piperazine, tri methylol propane tri methacrylate, bisferrocene-base acetylene and a heat stabilizer. The heat stabilizer is prepared through mixing of rhenium complex, cerous carbonate, tribasic lead sulfate, bisphenol A diglycidyl ether, epoxy butyl stearate, lanthanum stearate, glyzinc, aceticacid,2,2',2''-[(octylstannylidyne)tris(thio)]tris-,triisooctylester, mannitol and 2,5-diphenyl-1,3,4-oxadiazole. The polyvinyl chloride cable material has high strength, heat resistance and shock resistance, is resistant to bending and torsion, and has a long service life.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a heat-resistant and shock-resistant polyvinyl chloride cable material. Background technique [0002] With the rapid development of the global economy, the requirements for the quality and performance of wires and cables in various fields are getting higher and higher. Polyvinyl chloride is widely used in wires and cables due to its flame retardant, oil resistance, corona resistance, chemical corrosion resistance, good water resistance and processability. However, polyvinyl chloride has the defects of high brittleness and poor impact resistance, and its thermal stability is not very ideal, which limits the use of polyvinyl chloride cable materials and makes it have the defect of short service life in the process of use. Contents of the invention [0003] Based on the technical problems in the background technology, the present invention proposes a heat-resistant and sh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L75/04C08L69/00C08L67/02C08K13/04C08K7/08C08K5/1515C08K3/34C08K3/22H01B3/44
CPCC08L27/06C08K2201/014C08L2201/08C08L2203/202C08L2205/035H01B3/443C08L75/04C08L69/00C08L67/02C08K13/04C08K7/08C08K5/1515C08K3/346C08K2003/2227
Inventor 徐国锋赵建军吴建杰黄海琴吴松如朱家俊郑有松周家云
Owner ANHUI ELECTRIC GRP SHARES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap