Preparation method of elastic damping SBS material

An elastic and powder technology, applied in the field of the preparation of elastic shock-absorbing SBS materials, can solve the problems of the strength and elastic properties not meeting the requirements for use, the organic matrix is ​​difficult to disperse uniformly, and the elastic properties are not ideal, etc., to prevent the reaction rate from being too fast. , Increase elasticity, prevent the effect of agglomeration

Pending Publication Date: 2017-04-19
GUANGXI TEACHERS EDUCATION UNIV
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

SBS composite materials can be used as elastic shock-absorbing materials, but their strength and elastic properties are not up to the requirements of use. In the industry, inorganic reinforcing phases are often filled to improve their performance, but the surface of the inorganic filling phase is hydrophilic and oleophobic. Large energy and easy agglomeration between particles make it difficult to disperse uniformly in the organic matrix and the binding force with the matrix is ​​weak, resulting in poor strength of the material and unsatisfactory elastic properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of elastic damping SBS material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A preparation method of elastic shock-absorbing SBS material, comprising the following steps:

[0026] Step 1. Add calcium lactate and sodium lauryl sulfate to water, stir for 1 hour at a temperature of 40°C and a stirring rate of 600r / min, then add glucose and sodium carbonate, and then add water at a temperature of 100°C and a stirring rate of 600r / min. at 200r / min, stirred for 8h, cooled, and centrifuged to obtain a precipitate; the precipitate was successively washed with an aqueous ethanol solution with a gradually decreasing volume fraction, then washed with distilled water, dried, and ground to obtain the first powder; in step 1, calcium lactate, The mass ratio of water, sodium lauryl sulfate, glucose, and sodium carbonate is 1:5:0.1:0.1:3;

[0027] Step 2: Add yttrium nitrate, neodymium oxide, hydroxypropyl methylcellulose, polyethylene glycol, and sodium polyacrylate to the first powder, mix and stir evenly, place in a heating furnace for sintering in sequence,...

Embodiment 2

[0040] A preparation method of elastic shock-absorbing SBS material, comprising the following steps:

[0041] Step 1. Add calcium lactate and sodium lauryl sulfate to water, stir for 1.5 hours at a temperature of 50°C and a stirring rate of 800r / min, then add glucose and sodium carbonate, and stir at a temperature of 120°C The speed is 350r / min, stirred for 10h, cooled, and centrifuged to obtain the precipitate; the precipitate is washed successively with ethanol aqueous solution with gradually decreasing volume fraction, then washed with distilled water, dried, and ground to obtain the first powder; in step 1, calcium lactate , water, sodium lauryl sulfate, glucose, and sodium carbonate have a mass ratio of 1:7:0.15:0.3:4;

[0042] Step 2: Add yttrium nitrate, neodymium oxide, hydroxypropyl methylcellulose, polyethylene glycol, and sodium polyacrylate to the first powder, mix and stir evenly, place in a heating furnace for sintering in sequence, and then grind to obtain the f...

Embodiment 3

[0055] A preparation method of elastic shock-absorbing SBS material, comprising the following steps:

[0056] Step 1. Add calcium lactate and sodium lauryl sulfate into water, stir for 2 hours at a temperature of 60°C and a stirring rate of 1000r / min, then add glucose and sodium carbonate, and then add water at a temperature of 140°C and a stirring rate of 1000r / min. 500r / min, stirred for 12h, cooled, and centrifuged to obtain a precipitate; the precipitate was washed successively with an aqueous ethanol solution with a gradually decreasing volume fraction, then washed with distilled water, dried, and ground to obtain the first powder; the calcium lactate, water , the mass ratio of sodium lauryl sulfate, glucose, sodium carbonate is 1:10:0.2:0.5:5;

[0057] Step 2: Add yttrium nitrate, neodymium oxide, hydroxypropyl methylcellulose, polyethylene glycol, and sodium polyacrylate to the first powder, mix and stir evenly, place in a heating furnace for sintering in sequence, and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of an elastic damping SBS material, comprising the following steps: Step 1, carrying out a reaction between calcium lactate, lauryl sodium sulfate, water, glucose and sodium carbonate, centrifuging, washing, and drying to obtain first powder; Step 2, adding yttrium nitrate, neodymium oxide, hydroxypropyl methyl cellulose, polyethylene glycol and sodium polyacrylate into the first powder, uniformly mixing, and sintering to obtain second powder; Step 3, adding glycol, water, linoleic acid, sodium dodecyl benzene sulfonate, styrene and potassium sulphate into the second powder, reacting, filtering, and grinding so as to obtain third powder; Step 4, uniformly mixing SBS, the third powder, polystyrene, ultrahigh molecular weight polyethylene, carbon black, terpene resin, lanthanum oxide, cerium oxide, zirconium oxide, polyetheretherketone resin, oxidized polyethlene wax, macadamia shell powder, metallocene polyethylene and bamboo fiber, and mixing to obtain the elastic damping SBS material. The SBS material has advantages of high strength and good elasticity.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a preparation method of an elastic shock-absorbing SBS material. Background technique [0002] Styrene-butadiene-styrene block copolymer (SBS) is a tri-block copolymer of styrene and butadiene as monomers, which has the characteristics of plastic and rubber, and is called "third-generation synthetic rubber". Similar to styrene-butadiene rubber, SBS can be in contact with water, weak acid, alkali, etc. It has excellent tensile strength, large surface friction coefficient, good low-temperature performance, and good processing performance. It has become the most consumed thermoplastic elastomer at present. SBS composite materials can be used as elastic shock-absorbing materials, but their strength and elastic properties are not up to the requirements of use. In the industry, inorganic reinforcing phases are often filled to improve their performance, but the surface of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L25/06C08L23/06C08L61/16C08L23/30C08L99/00C08L97/02C08K13/06C08K9/10C08K7/24C08K3/22C08K3/04
CPCC08L53/02C08L2205/025C08L2205/035C08L2205/16C08L2207/068
Inventor 刘钰馨
Owner GUANGXI TEACHERS EDUCATION UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap