High-stability solvent type plastic paint

A high-stability technology for plastic coatings, applied in anti-corrosion coatings, fire-resistant coatings, epoxy resin coatings, etc., can solve the problems of poor stability of plastic coatings, and achieve excellent chemical resistance, ethanol wiping resistance, and high film strength. Effect

Inactive Publication Date: 2017-07-07
德阳森华新材料科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is the problem of poor stability of traditional plastic coatings, and the purpose is to provide high-stability solvent-based plastic coatings to solve the problem of coating stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The high-stability solvent-based plastic coating of the present invention comprises the following components in mass ratio:

[0020] 10-20% acrylic resin, 55-60% phenolic epoxy acrylic resin, 20%-30% organic solvent, 2-5% polyurethane thickener, 2-5% organic bentonite, dispersant 5-10%, 10 -15% stabilizer, 10-15% tertiary vinyl resin;

[0021] The stabilizer comprises the following components: diglycidyl ether, calcium ricinoleate, barium oleate, phenyltriethyl phosphite,

[0022] 2-hydroxy-4-methoxybenzophenone, color retention agent. The organic solvent comprises one or more of butanone, methyl isobutyl ketone, ethylene glycol butyl ether, propylene glycol butyl ether, and acetone. The high-stability solvent-based plastic coating also includes 0.5-1% leveling agent by mass ratio, and the leveling agent is polyether-modified polydimethylsilane. Leveling agents improve the leveling properties of coatings.

[0023] Among the present invention, acrylic resin and pheno...

Embodiment 2

[0025] Based on embodiment 1, described high-stability solvent-based plastic coating also comprises diluent, and described diluent comprises following component: white electric oil, Virahol, isobutanol, ethyl acetate, methyl isobutyl Alkanol ammonium salt solutions of ketones, n-butyl acetate, diacetone alcohol, propylene glycol butyl ether and unsaturated acid carboxylic acid esters. Before the plastic coating is used, it needs to be diluted with a diluent; the alkanol ammonium salt solution of the unsaturated acid carboxylate is an auxiliary agent to increase the conductivity of the electrostatic spray coating, and the diluent of the present invention is composed of an organic solvent and an increase in the conductivity of the coating. The composition of additives, not only has excellent chemical resistance, but also is resistant to ethanol wiping, and is very suitable for electrostatic spraying.

Embodiment 3

[0027] Based on the above-mentioned examples, the described high-stability solvent-based plastic paint includes the following components by mass ratio: 10% acrylic resin, 60% novolac epoxy acrylic resin, 30% organic solvent, 3% polyurethane thickener, 2% organic bentonite, 8% dispersant, 15% stabilizer, 15% tertiary vinegar resin. The present invention optimizes the component content of the paint.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-stability solvent type plastic paint. The high-stability solvent type plastic paint is prepared from, by mass, 10-20% of acrylic resin, 55-60% of phenolic epoxy acrylic resin, 20-30% of organic solvent, 2-5% of polyurethane thickener, 2-5% of organobentonite, 5-10% of dispersant, 10-15% of stabilizer and 10-15% of vinisol cooh; the stabilizer comprises diglycidyl ether, calcium ricinoleate, barium oleate, phenyl triethyl phosphate, 2-hydroxy-4-methoxy-diphenyl ketone and a color retaining agent. A series of other additives high in stability are added and combined with the stabilizer mainly having the stabilizing effect to comprehensively improve the stability of the paint from the respects of light resistance, high temperature resistance, chemical corrosion resistance, sedimentary stability and anti-volatilization performance, it is ensured that the paint is high in flowability and adhesion property, and a film formed by the paint is high in strength, uniform in color and long in service life.

Description

technical field [0001] The invention relates to a plastic coating, in particular to a high-stability solvent-based plastic coating. Background technique [0002] Engineering plastics have developed rapidly in recent years, providing various industries with a wider range of choices for plastic substrates, and at the same time putting forward stricter requirements for plastic coatings. Traditional plastic coatings have a relatively narrow application area, are limited to one or two substrates, and have poor comprehensive performance. [0003] PVC, PE, PP, PS, ABS and other plastics will change color and reduce strength under the action of heat, light, oxygen and other factors. Unless the structure of the polymer itself is changed, this aging phenomenon cannot be prevented. Therefore, After coating, the coating itself has the properties of heat resistance, light resistance, and oxidation resistance; various coatings are composed of film-forming substances (various resins), sol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/10C09D133/00C09D5/08C09D5/46C09D7/12C09D7/00C09D7/06C09D7/47
CPCC08L2201/08C08L2205/035C09D5/08C09D5/18C09D7/20C09D7/43C09D7/47C09D7/62C09D7/63C09D163/10C08L33/00C08L75/04C08L27/06C08K13/06C08K3/346C08K5/1515C08K5/098C08K5/526
Inventor 钟华军柏建波吴继忠
Owner 德阳森华新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com