Nitrogen-boron-doped porous carbon for electrode of supercapacitor and preparation method of nitrogen-boron-doped porous carbon

A technology of supercapacitor and porous carbon, applied in hybrid capacitor electrodes, chemical instruments and methods, inorganic chemistry, etc., can solve the problems of unsuitable supercapacitor electrode materials, low electrochemical activity, etc., and achieve broad market application prospects, high ratio Capacitance, easy incubation and harvesting effects

Active Publication Date: 2017-08-04
ANHUI UNIVERSITY
View PDF13 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] For example, the patent application number 201510611801.6 discloses a method for preparing a super porous carbon material with persimmon peel, using persimmon peel as a raw material, carbonized and activated to make porous carbon, the specific surface area is 1186 square meters per gram, but the electric capacity of the material Low chemical activity, not suitable as supercapacitor electrode material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nitrogen-boron-doped porous carbon for electrode of supercapacitor and preparation method of nitrogen-boron-doped porous carbon
  • Nitrogen-boron-doped porous carbon for electrode of supercapacitor and preparation method of nitrogen-boron-doped porous carbon
  • Nitrogen-boron-doped porous carbon for electrode of supercapacitor and preparation method of nitrogen-boron-doped porous carbon

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] (1) intercept the reed stalk, peel it, dry it, adopt a tissue masher to pre-crumble it, use deionized water as a dispersant, and adopt a planetary ball mill to further ball-mill the pre-broken reed stalk, and the rotating speed is 500 rpm Minutes, ball milling time is 24 hours.

[0048] (2) The slurry after ball milling was centrifuged at a speed of 5000 rpm, and the sediment was alternately washed three times with deionized water and absolute ethanol, and dried at 50 degrees Celsius to obtain pretreated reed stalk powder.

[0049] (3) Weigh reed stalk powder, urea ammonium nitrogen fertilizer (nitrogen ≥ 30%, China Salt Anhui Hongsifang Co., Ltd.), boron fertilizer (sodium borate ≥ 99%, boron-containing ≥15%, Anhui Nongwang Agricultural Science and Technology Development Co., Ltd.) was dispersed in deionized water, heated at 160 degrees Celsius for 12 hours in a hydrothermal reaction kettle, and the precipitate was repeatedly washed alternately with deionized water and...

Embodiment 2

[0059] (1) intercept the reed stalk, peel it, dry it, adopt a tissue masher to pre-crumble it, use deionized water as a dispersant, and adopt a planetary ball mill to further ball-mill the pre-broken reed stalk, and the rotating speed is 500 rpm Minutes, ball milling time is 24 hours.

[0060] (2) The slurry after ball milling was centrifuged at a speed of 5000 rpm, and the sediment was alternately washed three times with deionized water and absolute ethanol, and dried at 50 degrees Celsius to obtain pretreated reed stalk powder.

[0061] (3) Take reed stalk powder, nitrogen fertilizer, boron fertilizer, and potassium hydroxide according to the mass ratio of 1:2:2:3, add an appropriate amount of deionized water to the system after mixing, continue to stir until it becomes a paste, and after 50 Dry at °C, transfer to a tube furnace, pass an argon atmosphere, first raise the temperature to 300 °C at a rate of 2 °C / min and keep it warm for 1 hour, then raise the temperature to 70...

Embodiment 3

[0065] (1) Plane the fresh and alive reed that contains root hair, cultivate after 15 days in the nitrogenous fertilizer that contains 5% mass ratio and the boron fertilizer mixed solution of 5% mass ratio, intercept reed stalk, peel, adopt tissue masher to its For pre-crushing, deionized water is used as a dispersant, and the pre-broken reed stalks are further ball-milled with a planetary ball mill at a speed of 500 rpm, and the ball-milling time is 24 hours.

[0066] (2) The slurry after ball milling was centrifuged at a speed of 5000 rpm, and the sediment was alternately washed three times with deionized water and absolute ethanol, and dried at 50 degrees Celsius to obtain pretreated reed stalk powder.

[0067] (3) Weigh the reed stalk powder and potassium hydroxide according to the mass ratio of 1:3, mix them evenly, add an appropriate amount of deionized water to the system, continue to stir until it becomes a paste, dry it at 50 degrees Celsius, and transfer it to a tube ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses nitrogen-boron-doped porous carbon for an electrode of a supercapacitor and a preparation method of the nitrogen-boron-doped porous carbon, belonging to the technical field of energy source materials and application. The porous carbon is prepared from natural reed stalks as a carbon source by respectively taking a nitrogen fertilizer and a boron fertilizer as a nitrogen source and a boron source through a carbonization activation process. The prepared nitrogen-boron-doped porous carbon has a hierarchical three-dimensional pore structure containing micropores and mesopores, the main aperture distribution is 1-5 nanometers, the specific surface area is 1400m<2> / g-1700m<2> / g, the doped nitrogen atomic ratio is 6%-8%, and the doped boron atomic ratio is 2%-4%; and when the porous carbon is used as an electrode material of the supercapacitor, the specific capacitance of the porous carbon at a current density of 1A / g is 225F / g-250F / g, the preserved capacitance is higher than 95% after 5000 circulating charge-discharge processes, and the energy density at a power density of 1W / kg is 30Wh / kg-35Wh / kg.

Description

technical field [0001] The invention belongs to the technical field of energy materials and applications, and in particular relates to a nitrogen- and boron-doped porous carbon used for supercapacitor electrodes and a preparation method thereof. Background technique [0002] Porous carbon has become the preferred electrode material for supercapacitors due to its advantages such as large specific surface area, adjustable pore structure, good chemical stability and low cost. Porous carbon electrodes in supercapacitors mainly form an electric double layer at the electrode / electrolyte interface to store energy. Therefore, activated carbon materials for efficient energy storage should have a large specific surface area that is conducive to charge accumulation and facilitate electrolyte wetting and rapid ion migration. the pore structure. The study found that the heteroatom-doped porous carbon has better electrochemical performance than the traditional porous carbon. [0003] Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/348C01B32/318H01G11/26H01G11/34
CPCC01P2004/03C01P2004/04C01P2006/12C01P2006/17C01P2006/40H01G11/26H01G11/34Y02E60/13
Inventor 毕红祝煜张翔
Owner ANHUI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com