Polyester polycarboxylic acid early-strength water reducing agent

A polyester-based polycarboxylic acid and early-strength water-reducing agent technology, which is applied in the field of early-strength water-reducing agents, can solve the problems of slow development of concrete strength, shortened setting time, and single early-strength method

Inactive Publication Date: 2018-09-28
芜湖恒固混凝土材料有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the traditional polycarboxylate-based water reducer will delay the hydration of cement, the early strength of concrete will develop slowly, which limits its use in precast concrete and cold climates.
Patent application number 201310346345.8 discloses a high early strength polycarboxylate water reducer and its preparation method. The water reducer is made of methallyl polyoxyethylene ether, acrylamide, sodium methacrylate, Acrylic acid and acrylated alkanolamine and other monomers are polymerized under the action of initiators and chain transfer agents. This water reducer has problems such as single early strength mode, limited shortening of setting time, and no consideration of the impact on concrete thixotropy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester polycarboxylic acid early-strength water reducing agent
  • Polyester polycarboxylic acid early-strength water reducing agent

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] The present invention also provides a preparation method of the polyester polycarboxylate early-strength water reducer, the steps are as follows:

[0015] (1) Mixing sepiolite fiber, hexamethylolmelamine hexamethyl ether and pentaerythritol oleate in an aqueous medium at 120-150° C. for 0.5-1 hour to obtain modified sepiolite fiber;

[0016] (2) Mix methallyl alcohol polyoxyethylene ether, mono(meth)acrylate monomer, N-methylolacrylamide and unsaturated acid in a mixed solution of water and glycerin, and then add chain transfer agent, stirred at 70-110°C for 1.5-5h to obtain polyester polycarboxylic acid mother liquor;

[0017] (3) Add nano-titanium dioxide and modified sepiolite fiber to polyester polycarboxylic acid mother liquor, mix thoroughly, then add alkyl organic amine, sodium nitrite, defoamer, mix evenly, and obtain polyester polycarboxylate Carboxylic acid early strength superplasticizer.

[0018] The invention uses methallyl alcohol polyoxyethylene ether, ...

Embodiment 1

[0020] (1) Mix 2 g of sepiolite fiber, 1.5 g of hexamethylolmelamine hexamethyl ether and 1 g of pentaerythritol oleate in water for 1 hour at 125° C., centrifugally wash and dry to obtain modified sepiolite fiber;

[0021] (2) 60g methallyl alcohol polyoxyethylene ether, 25g polyethylene glycol polytetramethylene glycol mono(meth)acrylate, 5g N-methylolacrylamide and 1.5g maleic acid in 100g water and 25g Mix evenly in the mixed solution of glycerin, then add 0.5g of mercaptoacetic acid, and stir at 80°C for 2.5h to obtain a polyester polycarboxylic acid mother liquor;

[0022] (3) Mix 5 g of nano-silica and silane coupling agent KH550 in toluene evenly, and then reflux at 100° C. for 8 hours to obtain amino-modified silica with a surface amino content of 0.45 mmol / g;

[0023] (4) Add amino-modified silica and modified sepiolite fiber to the polyester polycarboxylic acid mother liquor, mix well, then add 6g triisopropanolamine, 15g sodium nitrite, 0.5g organosilicon disinfect...

Embodiment 2

[0025] (1) Mix 1g of sepiolite fiber, 1g of hexamethylolmelamine hexamethyl ether and 2g of pentaerythritol oleate in an aqueous medium at 150°C for 0.5h, centrifuge, wash and dry to obtain modified sepiolite fiber;

[0026] (2) Mix 20g methallyl alcohol polyoxyethylene ether, 28g propoxypolyethylene glycol polypropylene glycol mono(meth)acrylate, 6g N-methylolacrylamide and 1g maleic acid in water and 30g Mix evenly in the mixed solution of glycerin, then add 0.2g of mercaptoethanol, and stir at 110°C for 1.5h to obtain a polyester polycarboxylic acid mother liquor;

[0027] (3) Mix 6 g of nano-silica and silane coupling agent KH550 in toluene evenly, and then reflux at 100° C. for 8 hours to obtain amino-modified silica with a surface amino content of 0.45 mmol / g;

[0028](4) Add amino-modified silica and modified sepiolite fiber to polyester polycarboxylic acid mother liquor, mix well, then add 10g triethanolamine, 12g sodium nitrite, 1g polyether modified silicon defoamin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of early-strength water reducing agents, in particular to a polyester polycarboxylic acid early-strength water reducing agent. The polyester polycarboxylicacid early-strength water reducing agent is prepared from the following raw materials in parts by weight: 20 to 60 parts of VPEG, 15 to 30 parts of (methyl) monoacrylate monomer, 1 to 8 parts of nanometer titanium dioxide, 1 to 5 parts of sepiolite fiber, 0.5 to 2 parts of hexamethylol melamine hexamethyl ether, 0.5 to 2 parts of pentaerythritol oleate, 0.5 to 2 parts of unsaturated acid, 3 to 12parts of alkyl organic amine, 3 to 8 parts of N-hydroxymethyl acrylamide, 10 to 20 parts of sodium nitrite, 0.2 to 2 parts of a defoamer, 0.1 to 1 part of a chain transfer agent, and 20 to 30 parts of glycerin. The polyester polycarboxylic acid early-strength water reducing agent has the advantages that the air content of concrete is greatly reduced, the initial setting time and final setting time of the concrete are shortened, and the durability is improved.

Description

technical field [0001] The invention relates to the technical field of early-strength water-reducers, in particular to a polyester-based polycarboxylic acid early-strength water-reducer. Background technique [0002] Water reducing agent is an admixture that can reduce water consumption under the condition that the concrete slump is basically the same. In order to shorten the construction period, adding enhanced water reducer to concrete can not only improve the performance of concrete but also increase the early strength of concrete. Water reducers are divided into two types: organic and inorganic. Organic water reducers are in the category of water surface active agents. They have a better water reducing effect and can well reduce the interfacial energy between water, gas and solid, and play a role in lubrication and dispersion. However, it is weak to change the hydration reaction process of cement concrete; the inorganic water reducing agent mainly plays an early strengt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B24/42C04B24/26C08F283/06C08F220/58C04B103/30
CPCC04B40/0039C04B24/2694C04B2103/302C08F283/065C04B14/4643C04B14/06C04B24/122C04B22/085C04B24/42C08F220/58
Inventor 承忠富
Owner 芜湖恒固混凝土材料有限公司