A kind of conjugated polymer containing difluoronaphthothiophenedione electron-withdrawing unit and its synthesis method and application

A technology of conjugated polymer and synthesis method, applied in the field of polymers, can solve problems such as less material, and achieve the effects of high mobility, good solution processing performance, and excellent optoelectronic performance

Active Publication Date: 2021-08-10
SOUTH CHINA UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, although there are many kinds of organic conjugated polymer materials, there are relatively few materials with wide absorption and high carrier mobility. In order to achieve more efficient photoelectric conversion efficiency, it is very important to develop new high-performance donor polymer materials. Significance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of conjugated polymer containing difluoronaphthothiophenedione electron-withdrawing unit and its synthesis method and application
  • A kind of conjugated polymer containing difluoronaphthothiophenedione electron-withdrawing unit and its synthesis method and application
  • A kind of conjugated polymer containing difluoronaphthothiophenedione electron-withdrawing unit and its synthesis method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1,3-bis(2-ethylhexyl)-6,7-difluoro-5,8-bis(thiophen-2-yl)naphtho[2,3-c]thiophene-4,9-dione preparation:

[0035] (1) Under nitrogen protection, add 4,5-difluorophthalic acid 1 (4.04g, 20mmol) and a drop of N,N-dimethylformamide (DMF) into a 100mL two-necked round-bottomed flask, Oxalyl chloride (10 mL), and then add 20 mL of anhydrous dichloromethane as a solvent, and stir at room temperature for 12 hours. 2,5-bis(2-ethylhexyl)thiophene 2 (6.17 g, 20 mmol), AlCl 3 (10.67g, 80mmol), it was moved to 0°C under an ice-water bath and stirred for 30 minutes, then placed at room temperature and stirred for 3 hours. Post-processing: the reaction mixture was extracted with dilute hydrochloric acid aqueous solution and chloroform to obtain an organic phase, which was put into a one-port bottle and mixed with silica gel powder for rotary evaporation, and then purified with a silica gel column (petroleum ether: dichloromethane was selected as eluent). 4:1 (v / v)), the product 3 w...

Embodiment 2

[0042] 1,3-bis(2-ethylhexyl)-6,7-difluoro-5,8-bis(5-bromothien-2-yl)naphtho[2,3-c]thiophene-4,9 - Preparation of diketones (M1):

[0043] In a 100 mL single-necked bottle, compound 6 (0.69 g, 1 mmol) was dissolved in a mixed solvent of chloroform (30 mL) and acetic acid (30 mL), and the volume ratio of chloroform and acetic acid was 1:1. Then the one-necked flask was placed in an ice bath, and when the temperature of the reaction solution dropped to about 0°C, N-bromosuccinimide NBS (0.38 g, 2 mmol) was added batch by batch, and the reaction was stirred at room temperature for 8 hours. Post-processing: Pour the reaction solution into water, extract with dichloromethane, wash the organic layer with saturated aqueous sodium chloride solution, and dry over anhydrous magnesium sulfate. After distillation under reduced pressure, the crude product was purified by silica gel column (petroleum ether was selected as the eluent) to obtain the yellow solid product M1 (1,3-bis(2-ethylhex...

Embodiment 3

[0046] Preparation of PFPT-BDT

[0047] In the water-oxygen automatic control glove box, compound M1 (1,3-bis(2-ethylhexyl)-6,7-difluoro-5,8-bis(5-bromothiophen-2-yl)naphthol [2,3-c]thiophene-4,9-dione) (79.7mg, 0.10mmol), compound M2 (4,8-bis(5-(2-ethylhexyl)thiophen-2-yl)benzene And[1,2-b:4,5-b']dithiophene-2,6-diyl)bis(trimethyltin) (90.5mg, 0.10mmol) and catalyst tetrakistriphenylphosphine palladium (5.86mg , 0.005mmol) was added to a 10mL microwave tube, anhydrous xylene (2.5mL) was added to dissolve, and the silica gel cap was sealed. Place the microwave tube in the microwave reactor, set the temperature program: 80°C for 2 minutes, 120°C for 2 minutes, 160°C for 2 minutes, and finally 200°C for 45 minutes. In 200mL methanol, carry out Soxhlet extraction successively with methanol, acetone, n-hexane, dichloromethane and chloroform, then add the aqueous solution of sodium diethyldithiocarbamate trihydrate (225mg, 1mmol , 100mL water), stirred at 60°C for 8 hours, remov...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
energy conversion efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a conjugated polymer containing difluoronaphthothiophenedione electron-withdrawing units, a synthesis method and an application thereof, and belongs to the field of polymers applied to optoelectronic materials and devices. The conjugated polymer prepared in the present invention adopts a benzoheterocyclic structure substituted by difluorine, and the fluorine atom forms a non-bonding interaction with the electron-donating unit, which enhances the transport of carriers in the planar and rigid main chain structure, which is beneficial to obtain high mobility. And this type of conjugated polymer has a wide optical bandgap, suitable for matching with narrow bandgap small molecule acceptors to achieve complementary absorption spectra, so it can be used to make polymer light-emitting diode devices, polymer field-effect transistors and polymer solar energy active layer of the battery.

Description

technical field [0001] The invention relates to the field of polymers applied to optoelectronic materials and devices, in particular to a conjugated polymer containing difluoronaphthothiophenedione electron-withdrawing units. Background technique [0002] With the development of human society, the reserves of traditional non-renewable energy sources such as coal, oil and natural gas are decreasing day by day, and it is urgent to seek new energy sources for sustainable development. As a kind of green renewable energy, solar energy is inexhaustible and inexhaustible. As one of the important means to solve energy problems, organic solar cells have the advantages of easy-to-obtain materials, light weight, flexibility, and large-area preparation of thin-film devices, and have attracted widespread attention from scientists. There are many kinds of materials for the active layer of organic solar cells, their chemical structures are easy to modify, their preparation and purificatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G61/12
Inventor 应磊李康黄飞曹镛
Owner SOUTH CHINA UNIV OF TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com