Silk fine matt ceramic brick and preparation method thereof

A technology of ceramic tiles and ceramic tiles, which is applied in the direction of ceramic molding machines, ceramic material production, manufacturing tools, etc., can solve the problems that are not conducive to the richness of pattern decoration, yellowing of the glaze surface, complicated manufacturing methods, etc., and achieve broad firing range, reduce the difficulty of production, and reduce the consumption of glaze

Active Publication Date: 2022-03-25
JIANGXI HEMEI CERAMICS +4
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its weak point is: manufacturing method is relatively complicated
In addition, the glaze contains titanium dioxide, which is easy to make the glaze of the product yellow, which is not conducive to the decorative richness of the pattern.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silk fine matt ceramic brick and preparation method thereof
  • Silk fine matt ceramic brick and preparation method thereof
  • Silk fine matt ceramic brick and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0051] The present invention will be described in further detail below in conjunction with embodiment:

[0052] The silk fine and matt ceramic tile blank is composed of the following components:

[0053]

[0054] In this embodiment, the edging and polishing waste residues are selected from one or more of the following: SiO 2 , Al 2 O 3 , CaO, K 2 O, Na 2 O, MgO, MgCl 2 , SiC; the water content of the edging and polishing waste residue is 32-36%.

[0055] The edging and polishing waste residues mainly come from the solid waste residues produced by flocculation, precipitation and pressure filtration after a series of processes such as grinding, polishing, edging, and chamfering in the later stage of cold processing of ceramic tiles. These solid waste residues contain ceramic tiles. Polished or ground fines - blanks, glazes, ground fines from grinding heads, etc.; the recycled waste blanks are mud blanks (unfired) ), which can be reused for green body mud slurry through...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to fine silky matt ceramic tiles and a preparation method thereof. The ceramic brick blank is composed of the following components: nepheline powder: 10% to 15%; high carbon mud: 5% to 10%; low carbon mud: 20% to 25%; medium and high carbon mud: 10% to 15%; recycled waste Blank: 5% to 10%; potassium sodium stone powder: 5% to 10%; paving albite powder: 20% to 25%; waste porcelain powder: 5% to 10%; desulfurization waste residue: 0 to 7%; edging and polishing Waste residue: 20% to 30%; liquid debonding agent: 0.3% to 1.0%; liquid enhancer: 0.2% to 0.8%. Preparation process: green body raw material batching and ball milling → spray drying → aging → green body pressing molding → drying → blank throwing → water spraying → glaze → pattern decoration → firing.

Description

technical field [0001] The invention relates to the field of ceramic production, in particular to a silk fine and matt ceramic tile and a preparation method thereof. Background technique [0002] CN201710408570.8 discloses a raw material matte glaze, a preparation method and application thereof, and the purpose of which is to solve the problems of rough hand feeling, unstable corrosion resistance and poor color development of inkjet ink of matte glaze series products. The technical scheme: the preparation method of the raw material matte glaze comprises the steps of: taking 1-5 parts by mass of zinc oxide, 15-35 parts of barium carbonate, 15-30 parts of potassium feldspar, and 10-30 parts of albite 15 parts, 0-10 parts of dolomite, 3-10 parts of kaolin, 4-15 parts of quartz and 4-15 parts of calcium phosphate, then add sodium tripolyphosphate and carboxymethyl cellulose, and then add 50-70 parts of water, Ball mill to pass through a 325-mesh sieve, and stale for more than 2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/132C04B33/13C04B33/04C03C8/14C03C8/02C03C8/04C03C8/08C04B41/86
CPCC04B33/1324C04B33/132C04B33/131C04B33/1305C04B33/04C03C8/14C03C8/02C03C8/04C03C8/08C04B41/86C04B41/5022C04B2235/6567Y02P40/60C03C8/06C03C8/22C03C3/087C03C3/093C03C3/097C04B33/34C04B33/1321C04B33/1328C04B35/62655C04B2235/3472C04B2235/3481C04B33/1315C04B2111/80C04B41/4539B28B3/02B28B11/044B28B11/243C03C2205/00C04B33/30C04B41/009C04B41/522C04B41/89C04B2235/3463C04B2235/349C04B2235/448C04B2235/604
Inventor 古战文王彦君邓江文肖惠银杨权潘超宪王永强刘学斌蒋俊军王俊
Owner JIANGXI HEMEI CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap