Environment-friendly antibacterial cable material and preparation method thereof

A cable and environmental protection technology, applied in the field of environmental protection antibacterial cable materials and their preparation, can solve the problems of cable surface corrosion and damage, waste of manpower and material resources, difficult cable maintenance, etc., to improve stability, inhibit bacterial growth, and be suitable for popularization and use. Effect

Inactive Publication Date: 2019-09-20
ANHUI CABLE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Nowadays, for aesthetic requirements, many cables are often buried underground and in walls, and the buried cables are difficult to repair after damage, the replacement is complicated, and waste of manpower and material resources. Therefore, in order to prevent cable damage, the requirements for cable materials are also extremely high. Cable materials must have Good weather resistance, not easy to damage, and because a large number of bacteria will often breed in the ground and walls without treatment for a long time, and the reproduction and growth of bacteria will cause corrosion and damage to the surface of the cable, so an effective antibacterial and oxidation resistant cable has been developed. The cable material is a major direction at this stage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly antibacterial cable material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An environment-friendly antibacterial cable material, the environment-friendly antibacterial cable material is made of the following raw materials in parts by weight: 26 parts of polyvinyl chloride resin, 16 parts of EPDM rubber, 10 parts of nitrile rubber, 14 parts of PVC resin, 12 parts 4 parts of alkyl mercaptan, 2 parts of hexamethylphosphoric triamide, 2 parts of acetylene carbon black, 2 parts of activated carbon, 1 part of diatomaceous earth, 2 parts of ethylene-butyl acrylate-glycidyl methacrylate, amino triethylene 1 part of methylphosphonic acid, 1 part of n-butyl titanate, 1 part of crosslinking agent, 1 part of flame retardant, and 1 part of vulcanizing agent.

[0027] The crosslinking agent is a mixture of dicumyl peroxide, ethyl orthosilicate, and p-toluenesulfonyl chloride in a mass ratio of 3:2:1; the flame retardant is triphenyl phosphate, decabromodiphenyl ether, A mixture of zinc borate and antimony trioxide in a mass ratio of 2:2:1:1; the vulcanizing...

Embodiment 2

[0036] An environment-friendly antibacterial cable material, the environment-friendly antibacterial cable material is made of the following raw materials in parts by weight: 30 parts of polyvinyl chloride resin, 18 parts of EPDM rubber, 14 parts of nitrile rubber, 16 parts of PVC resin, 12 parts 5 parts of alkyl mercaptan, 3 parts of hexamethylphosphoric triamide, 4 parts of acetylene carbon black, 3 parts of activated carbon, 3 parts of diatomaceous earth, 4 parts of ethylene-butyl acrylate-glycidyl methacrylate, amino triethylene 3 parts of methylphosphonic acid, 2 parts of n-butyl titanate, 2 parts of crosslinking agent, 3 parts of flame retardant, and 1.6 parts of vulcanizing agent.

[0037] The crosslinking agent is a mixture of dicumyl peroxide, ethyl orthosilicate, and p-toluenesulfonyl chloride in a mass ratio of 3:2:1; the flame retardant is triphenyl phosphate, decabromodiphenyl ether, A mixture of zinc borate and antimony trioxide in a mass ratio of 2:2:1:1; the vul...

Embodiment 3

[0046] An environment-friendly antibacterial cable material, the environment-friendly antibacterial cable material is made of the following raw materials in parts by weight: 28 parts of polyvinyl chloride resin, 17 parts of EPDM rubber, 12 parts of nitrile rubber, 15 parts of PVC resin, 12 parts 4.5 parts of alkyl mercaptan, 2.5 parts of hexamethylphosphoric triamide, 3 parts of acetylene carbon black, 2.5 parts of activated carbon, 2 parts of diatomaceous earth, 3 parts of ethylene-butyl acrylate-glycidyl methacrylate, amino triethylene 2 parts of methylphosphonic acid, 1.5 parts of n-butyl titanate, 1.5 parts of crosslinking agent, 2 parts of flame retardant, and 1.3 parts of vulcanizing agent.

[0047] The crosslinking agent is a mixture of dicumyl peroxide, ethyl orthosilicate, and p-toluenesulfonyl chloride in a mass ratio of 3:2:1; the flame retardant is triphenyl phosphate, decabromodiphenyl ether, A mixture of zinc borate and antimony trioxide in a mass ratio of 2:2:1:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an environment-friendly antibacterial cable material and a preparation method thereof, and relates to the technical field of cable processing. The environment-friendly antibacterial cable material comprises, by weight, 26-30 parts of polyvinyl chloride resin, 16-18 parts of ethylene-propylene-diene monomer rubber, 10-14 parts of nitrile rubber, 14-16 parts of PVC resin, 4-5 parts of lauryl mercaptan, 2-3 parts of hexamethylphosphoric triamide, 2-4 parts of acetylene black, 2-3 parts of activated carbon, 1-3 parts of diatomaceous earth, 2-4 parts of ethylene-butyl acrylate-glycidyl methacrylate, 1-3 parts of amino trimethylene phosphonic acid, 1-2 parts of n-butyl titanate, 1-2 parts of crosslinking agents, 1-3 parts of flame retardants and 1-1.6 parts of vulcanizing agents. The environment-friendly antibacterial cable material and the preparation method thereof have the advantages that the defects of the prior art are overcome, the anti-oxidation and anti-corrosion performance of the product is improved, multiple substances are added to effectively inhibit breeding and growth of bacteria, a long-lasting antibacterial effect is achieved, pollutants are avoided, and the cable material is safe, environmentally friendly and suitable for promotion and application.

Description

technical field [0001] The invention relates to the technical field of cable processing, in particular to an environment-friendly and antibacterial cable material and a preparation method thereof. Background technique [0002] Cable electric cable; power cable, usually a rope-like cable twisted by several or several groups of wires, at least two in each group, each group of wires is insulated from each other, and often twisted around a center, the whole The outside is covered with a highly insulating covering. As a supporting industry of the power industry, one of the pillar industries of the national economy, the wire and cable industry plays an extremely important role and position in the national economy. [0003] Nowadays, for aesthetic requirements, many cables are often buried underground and in walls, and the buried cables are difficult to repair after damage, the replacement is complicated, and waste of manpower and material resources. Therefore, in order to prevent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/16C08L9/02C08L23/08C08K13/04C08K5/372C08K5/5399C08K3/04C08K7/24C08K7/26C08K5/5317
CPCC08L27/06C08L2201/08C08L2203/202C08L2205/025C08L2205/035C08L23/16C08L9/02C08L23/0884C08K13/04C08K5/372C08K5/5399C08K3/04C08K7/24C08K7/26C08K5/5317
Inventor 夏候东周俊宰学龙韩俊宝徐晓丽朱元忠陈安鹏陶恒莹
Owner ANHUI CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap