Antibacterial polystyrene modified material and preparation method thereof

A technology of polystyrene and modified materials, which is applied in metal material coating technology, ion implantation plating, coating, etc., can solve difficult problems, achieve effective utilization, good combination effect, and improve light stability and the effect of abrasion resistance

Inactive Publication Date: 2013-07-17
KINGFA SCI & TECH CO LTD
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the huge surface energy of nano-powders, there is a strong "cohesion" in them. At the same time, the compatibility of inorganic nano-powders with different types of organic polymer materia

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial polystyrene modified material and preparation method thereof
  • Antibacterial polystyrene modified material and preparation method thereof
  • Antibacterial polystyrene modified material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Using high-speed pre-mixing and dispersing one-time extrusion process, 76 parts of polystyrene, 1 part of nano-titanium dioxide particles, 2 parts of nano-silver particles, 6 parts of ethylene-propylene rubber as a dispersion modifier, and two parts of styrene-butyl acrylate 10 parts of graft-modified ethylene-propylene rubber, 5 parts of nano-apatite whiskers, 0.01 parts of antioxidant, and 5 parts of processing aids are dispersed and mixed by a high-speed mixer; melted, mixed and extruded by a twin-screw extruder Take out, cool, dry and cut into pellets.

[0029] The above-mentioned granules are injection-molded into plates by an injection molding machine, placed overnight under natural conditions, and then the plates are placed in an oxygen-containing gas atmosphere, and pure titanium is used as a target material, and the plasma sputtering process is performed using an existing plasma coating machine , in the plasma sputtering process, the radio frequency power is 30...

Embodiment 2

[0032] The high-speed premixing and dispersing extrusion process of Example 1 is used to granulate. The parts by weight of each component are: 80 parts of polystyrene, 0.5 part of nano-titanium dioxide particles, 1 part of nano-silver particles, and 3 parts of α-olefin oligomers. 6 parts, 6 parts of styrene-butyl acrylate binary graft modified ethylene-propylene rubber, 3 parts of nano-apatite whiskers, 0.1 part of antioxidant, and 0.1 part of processing aid.

[0033] The above-mentioned pellets are blown into containers by a blow molding machine, placed overnight under natural conditions, and then the container is placed in an oxygen-containing gas atmosphere, pure titanium is used as a target, and plasma sputtering is performed using an existing plasma coating machine In the plasma sputtering process, the radio frequency power is 50w, the bias voltage is 60V, and the sputtering time is 4 minutes.

[0034] After sputtering, the thickness of the titanium dioxide film on the su...

Embodiment 3

[0036] The high-speed premixing and dispersing primary extrusion process of Example 1 is used to granulate, and the parts by weight of each component are: 83 parts of polystyrene, 0.8 part of nano-titanium dioxide particles, 1.5 parts of nano-silver particles, and 5 parts of α-olefin oligomers. 8 parts, 8 parts of styrene-butyl acrylate binary graft modified ethylene-propylene rubber, 5 parts of nano-apatite whiskers, 1 part of antioxidant, and 3 parts of processing aid.

[0037] The above-mentioned pellets are injection-molded into pipes by injection molding machine, placed overnight under natural conditions, and then the pipes are placed in an oxygen-containing gas atmosphere, pure titanium is used as the target material, and the plasma sputtering process is performed using an existing plasma coating machine , in the plasma sputtering process, the radio frequency power is 100w, the bias voltage is 80V, and the sputtering time is 8 minutes.

[0038] After sputtering, the thickn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an antibacterial polystyrene modified material and a preparation method thereof. The polystyrene material comprises polystyrene, nanometer titanium dioxide particles, nanometer silver particles, a dispersing modified agent, a styrene butyl acrylate binary grafting modified ethylene-propylene rubber, nano hydroxyapatite whisker, an antioxidant and a processing aid; and after forming, the surface of the material is provided with a nanometer titanium dioxide film formed by a plasma sputtering process. The polystyrene modified material provided by the invention has good mechanical properties and continuous antibacterial effect, and can prevent the agglomeration of the nanometer material and effectively improve the light stability.

Description

technical field [0001] The invention relates to a polystyrene modified material, in particular to an antibacterial polystyrene modified material and a preparation method thereof. Background technique [0002] Polystyrene is a non-toxic, odorless, colorless transparent particle, a glass-like brittle material, and one of the most widely used synthetic resins today. This traditional polystyrene product has extremely high transparency, the light transmittance can reach more than 90%, good electrical insulation performance, easy coloring, good processing fluidity, good rigidity, good chemical corrosion resistance, and low price. , but this traditional polystyrene has many shortcomings, such as brittleness, low impact strength, and prone to stress cracking, which greatly limit the application range of polystyrene. At present, in order to solve the shortcomings of traditional polystyrene, it is mainly improved by blending it with rubber or copolymerizing it with other resins. Alt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L51/00C08L51/06C08K13/04C08K3/22C08K3/08C08K7/04C08K3/32C23C14/08C23C14/34
Inventor 叶丹滢袁绍彦刘奇祥吴博石鑫
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap