A composite bed reactor and method for co-producing calcium carbide, gas and tar

A reactor and composite bed technology, applied in the field of composite bed reactors, can solve the problems of small particle raw material flow interference loss, high investment, high pollution, etc., and achieve the goal of less difficulty in design and construction, lower cost, and faster reaction rate Effect

Active Publication Date: 2016-05-04
BEIJING UNIV OF CHEM TECH
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The present invention aims to solve the problem of "high investment, high energy consumption and high pollution" in the production of calcium carbide. Through a lot of research and creative work, the inventor has developed a kind of product with simple structure and operation, high efficiency, low energy consumption and wide source of raw materials. The low-cost reactor and method for the co-production of calcium carbide, gas and tar not only solves the problem of contact between large particles of coke and calcium oxide or the problem of loss of small particles of raw materials due to air flow interference, but also realizes high temperature gas in the furnace. Direct and efficient heat exchange of raw materials to optimize heat utilization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A composite bed reactor and method for co-producing calcium carbide, gas and tar
  • A composite bed reactor and method for co-producing calcium carbide, gas and tar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A composite bed reactor for the co-production of calcium carbide, gas and tar, such as figure 1 shown. The reactor includes a hopper 1, a moving bed preheating chamber 2, a tar trap 3, a gas outlet 4, a rotary distributor 5, an oxygen heating chamber 6, an oxygen injection burner 7, a product molten pool 8, and a product outlet 9 and gate silo 10, etc., the hopper 1 has one, located on the top of the central axis of the reactor, the bottom of the hopper 1 is connected with the gate silo 10, the gate silo 10 is connected with the moving bed preheating chamber 2, and the moving bed preheating chamber A tar trap 3 is provided on the top side of the hot chamber 2, and a gas discharge port 4 is provided on the tar trap 3. A rotary distributor 5 is provided at the bottom of the moving bed preheating chamber 2, and the moving bed preheating chamber 2 passes through the rotary distributor. 5 communicates with the oxygen heating chamber 6, and the bottom of the oxygen heating c...

Embodiment 2

[0039] A method utilizing reactor coproduction calcium carbide, coal gas and tar described in embodiment 1, comprises the following steps:

[0040] A. Raw material molding: coal powder and calcium carbide slag (containing 90% calcium hydroxide) are used as raw materials, and the fixed carbon content in the coal powder is 70%, the volatile content is 22%, the ash content is 8%; the C content is 76 %. Grind and sieve the raw materials, select powder materials below 120 mesh, mix according to the ratio of C / Ca molar ratio of 16:1, stir evenly, and use a tablet machine to form columnar particles with a diameter of 30mm and a height of 40-60mm.

[0041] B. Raw material transportation and preheating: send the raw material particles obtained in the above step A to the hopper 1, and then transport them to the moving bed preheating chamber 2 through the gate silo 10, adjust the feeding speed and the motor speed of the rotary distributor 5, and then control the The speed at which the...

Embodiment 3

[0045] A method utilizing reactor coproduction calcium carbide, coal gas and tar described in embodiment 1, comprises the following steps:

[0046] A. Raw material granulation: Coke and calcium oxide are used as raw materials, wherein the C content in coke is about 90%, the ash content is about 8%, and the purity of calcium oxide is about 90%. Grind and sieve the raw materials, select the powder below 60 mesh, mix according to the ratio of C / Ca molar ratio of 9:1, mix well, spray and add water, and finally use a double-roll extrusion molding machine to form pellets with a particle size of 30mm.

[0047] B. Raw material transportation and preheating: send the raw material particles obtained in the above step A to the hopper 1, and then transport them to the moving bed preheating chamber 2 through the gate silo 10, adjust the feeding speed and the motor speed of the rotary distributor 5, and then control the The speed at which the granular raw materials move down in the moving...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface temperatureaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite bed reactor and a method for combined production of calcium carbide, gas and tar, and belongs to the field of calcium carbide production. The reactor comprises a hopper, a brake bunker, a moving bed preheating chamber, a tar collector, a gas outlet, a distributing device, an oxygen heat reaction chamber, oxygen spraying burners, a product molten pool and a product outlet, and the hopper is connected with the moving bed preheating chamber by the brake bunker, and the top side surface of the moving bed preheating chamber is provided with the tar collector, and the tar collector is provided with a gas outlet, and the moving bed preheating chamber bottom is provided with a distributing device, and the moving bed preheating chamber is communicated with an oxygen heat reaction chamber by a distributing device, and the oxygen heat reaction chamber bottom is connected with a product molten pool, and the upper portion of the connection between the oxygen heat reaction chamber and the product molten pool is provided with the oxygen spraying burner, and the middle bottom of the product molten pool is provided with a product outlet. The reactor of the invention has the advantages of simple structure and high efficiency, and large scale production is easy to realize, and the raw material is pelleted by powder form carbonaceous raw material and powder form calcium containing raw material, and the contact surface between raw materials is large, the reaction rate is fast, and reactor is convenient for reusing calcium carbide slags.

Description

technical field [0001] The invention relates to a composite bed reactor and method for co-producing calcium carbide, coal gas and tar, in particular to the molding of powdered carbon-containing raw materials and powdered calcium-containing raw materials, direct combustion of part of the carbon-containing raw materials for heating production of calcium carbide, combustion product gas and Calcium carbide furnace gas naturally rises to the upper part of the reactor to continuously exchange heat with the raw materials, and the hot gas is cooled and the raw materials are preheated and then reacted. Background technique [0002] Calcium carbide commonly known as calcium carbide (CaC 2 ), known as the mother of organic synthesis before the middle of the last century. At present, it is mainly used to produce a series of products such as vinyl chloride, vinyl acetate and acrylic acid. For example, about 70% of PVC (polyvinyl chloride) production in China originates from the calcium ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J8/08C01B31/32C10B53/04C10J3/66C01B32/942
Inventor 刘振宇刘清雅王仁醒屈一新李成岳刘辉
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com