Anti-cracking heat-preserving wall construction material and preparation method thereof

A technology for building materials and thermal insulation walls, applied in the field of building materials, can solve problems such as easy cracking and durability of plastering mortar, and achieve the effects of improving interface compatibility, improving thermal insulation, and reducing folding ratio

Active Publication Date: 2016-11-16
MAANSHAN TIANJINYUN PAINT IND
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Based on the problems existing in the background technology, the present invention proposes a crack-resistant thermal insulation wall building material and a preparation method thereof. The problems of easy cracking and poor durability have realized the high performance of heat preservation, heat insulation and crack resistance in the true sense

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-cracking heat-preserving wall construction material and preparation method thereof
  • Anti-cracking heat-preserving wall construction material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An anti-cracking and thermal insulation wall building material, whose raw materials by weight include: 400 parts of cement, 70 parts of silica powder, 80 parts of gray calcium powder, 160 parts of expanded vermiculite, 60 parts of quartz sand, and 100 parts of hollow glass beads. 40 parts of rock wool silk, 80 parts of modified fly ash, 60 parts of polystyrene particles, 20 parts of wood fiber, 5 parts of polypropylene fiber, 60 parts of polyvinyl alcohol powder, 40 parts of ethylene-vinyl acetate copolymer, hydroxyethyl 20 parts of methyl cellulose;

[0021] Wherein, the method for preparing the modified fly ash includes: adding fly ash with a particle size of ≥ 20 mesh into a mixed acid solution of concentrated nitric acid and concentrated sulfuric acid with a volume ratio of 1:3, and ultrasonic treatment at 50°C for 0.5 h , The frequency of ultrasonic is 40KHz, and the sound intensity is 0.1W / cm 2 , After cooling to room temperature, suction filtration, washing, drying ...

Embodiment 2

[0024] An anti-cracking and thermal insulation wall building material, whose raw materials by weight include: 600 parts of cement, 40 parts of silica powder, 220 parts of gray calcium powder, 80 parts of expanded vermiculite, 100 parts of dolomite sand, and 60 parts of hollow glass beads , 80 parts of rock wool silk, 30 parts of modified fly ash, 120 parts of polystyrene particles, 10 parts of wood fiber, 10 parts of polypropylene fiber, 30 parts of polyvinyl alcohol powder, 80 parts of vinyl acetate-ethylene tertiary carbonate copolymer, 10 parts of carboxymethyl cellulose;

[0025] Wherein, the method for preparing the modified fly ash includes: adding fly ash with a particle size ≥ 20 mesh into a mixed acid solution of concentrated nitric acid and concentrated sulfuric acid with a volume ratio of 1:5, and ultrasonic treatment at 30°C for 3 hours, The frequency of the ultrasonic wave is 20KHz, and the sound intensity is 0.3W / cm 2 , After cooling to room temperature, suction fil...

Embodiment 3

[0028] An anti-cracking and thermal insulation wall building material, the raw materials of which by weight include: 500 parts of cement, 55 parts of silica powder, 150 parts of gray calcium powder, 120 parts of expanded vermiculite, 80 parts of sea sand, and 80 parts of hollow glass beads. 60 parts of rock wool silk, 55 parts of modified fly ash, 90 parts of polystyrene particles, 15 parts of wood fiber, 7 parts of polypropylene fiber, 45 parts of polyvinyl alcohol powder, 60 parts of ethylene-vinyl laurate-vinyl chloride copolymer Parts, 15 parts of hydroxyethyl cellulose;

[0029] Wherein, the method for preparing the modified fly ash includes: adding fly ash with a particle size ≥ 20 mesh into a mixed acid solution of concentrated nitric acid and concentrated sulfuric acid with a volume ratio of 1:4, and ultrasonic treatment at 40°C for 1.5 hours , The frequency of ultrasonic is 30KHz, and the sound intensity is 0.2W / cm 2 , After cooling to room temperature, suction filtratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-cracking heat-preserving wall construction material and a preparation method thereof. The anti-cracking heat-preserving wall construction material is prepared from, by weight, 400-600 parts of cement, 40-70 parts of silica powder, 80-220 parts of ash-calcium powder, 80-160 parts of expanded vermiculite, 60-100 parts of sand, 60-100 parts of hollow glass beads, 40-80 parts of rock wool threads, 30-80 parts of modified fly ash, 60-120 parts of polyphenyl particles, 10-20 parts of wood fiber, 5-10 parts of polypropylene fiber, 30-60 parts of polyvinyl alcohol, 40-80 parts of dispersible latex powder and 10-20 parts of cellulose ether. The anti-cracking heat-preserving wall construction material solves the problem that finishing mortar prepared from an existing outer wall heat-preserving material is prone to cracking and poor in durability, and truly achieves heat preservation, heat isolation and high anti-cracking performance.

Description

Technical field [0001] The invention relates to the technical field of building materials, in particular to a thermal insulation and crack-resistant wall building material and a preparation method thereof. Background technique [0002] The external thermal insulation system for building exterior walls can bring excellent energy-saving effects and a comfortable living environment, so people pay high attention to the long-term performance of the system. At present, the protective mortar used in the protective layer of the external wall external insulation system is mostly brittle cement-based materials with high specific gravity, high thermal conductivity, and high heat storage value; while the insulation boards are mostly organic insulation materials with low density and soft texture. Under long-term heat and cold, cold and humid cycles, repeated stresses, solar radiation, rain corrosion and other external erosion, there will be problems such as cracking, falling off, chalking, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26C04B20/02C04B111/34
CPCC04B20/023C04B28/26C04B2111/343C04B2201/20C04B2201/32C04B18/146C04B22/064C04B14/202C04B14/24C04B14/46C04B18/08C04B24/24C04B16/02C04B16/0633C04B24/2623C04B24/383C04B7/02C04B14/06C04B14/26C04B24/2688C04B14/068
Inventor 蒋子平尹万云金仁才唐翠红胡勇邱勇孙飞成刚
Owner MAANSHAN TIANJINYUN PAINT IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap