A nano-graphene and fiber bundle technology, applied in the field of building materials, can solve the problems of not being able to effectively guarantee the private car environment, ignore, forget, etc., and achieve the effects of shortening the post-processing process, improving dispersion, and improving casting efficiency
Inactive Publication Date: 2016-12-07
SUZHOU RUI TE JIE CHEM PROD CO LTD
View PDF7 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Therefore, it is necessary to maintain frequent ventilation and put adsorption materials in the car, such as activated carbon or a composite product of melt-blown material and large-particle activated carbon, to absorb harmful gases and purify the air in private cars, but such products often have a certain lifespan. It needs to be replaced frequently, and it is generally easy to be forgotten or ignored without marking or reminding, and cannot effectively guarantee the environment in the private car
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] A dust-absorbing polymer nanographene-loaded fiber bundle, made of the following weight raw materials: 25kg of cellulose acetate bundle, 20kg of alginic acid, 5kg of hydrochloric acid, 30kg of coal gangue, 20kg of ethylene-vinyl acetate copolymer, and 8kg of high polyethylene , nano active agent 5kg, glyceryl triacetate 5 kg, conductive mica powder 0.3kg, nano conductive graphite powder 0.2kg, polyisocyanate trimer 0.8kg, polytetrafluoroethylene fiber 1kg, porous aluminum titanate 2 kg, poly Lactic acid chitosan 15 kg, nano-graphene 10 kg, modified nano-titanium dioxide 10 kg, fly ash 20 kg, slaked lime 6 kg, silica lime 6 kg, diethyl terephthalate 15 kg, 3-aminocrotonic acid 10 kg of methyl ester, 15 kg of tetrabromophthalic anhydride, 15 kg of polyethylene resin, 2 kg of nano-alumina, 10 kg of mesh soil, 8 kg of sea mud, 5 kg of polyvinyl acetate, 4 kg of tung oil, 3 kg of waste syrup, lauroyl sarcosine 1kg of sodium, 3kg of fir glue, 4kg of asbestos wool, 6kg of addi...
Embodiment 2
[0032] Acetate bundle 30kg, alginic acid 25kg, hydrochloric acid 10kg, coal gangue 35kg, ethylene-vinyl acetate copolymer 25kg, high polyethylene 10kg, nano active agent 8kg, triacetin 8 kg, conductive mica powder 0.5kg, nano conductive 0.4kg of graphite powder, 1kg of polyisocyanate trimer, 2kg of polytetrafluoroethylene fiber, 3 kg of porous aluminum titanate, 20kg of polylactic chitosan, 15 kg of nano-graphene, 25 kg of modified nano-titanium dioxide, and 25 kg of fly ash kg, 7 kg of slaked lime, 8 kg of silica lime, 25 kg of diethyl terephthalate, 15 kg of methyl 3-aminocrotonate, 20 kg of tetrabromophthalic anhydride, 21 kg of polyethylene resin, 4 kg of nano-alumina, and clay 12kg, sea mud 810kg, polyvinyl acetate 8kg, tung oil 5kg, waste syrup 4.5kg, sodium lauroyl sarcosinate 1.5kg, fir gum 4kg, asbestos velvet 6kg, additive 7kg, appropriate amount of water;
[0033] The preparation method of the modified nano-titanium dioxide is: mix completely substituted N-trimethyl...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a dust-collecting type macromolecule nanometer graphene-loaded fiber bundle and a production method thereof. The dust-collecting type macromolecule nanometer graphene-loaded fiber bundle is prepared by adopting the following raw materials in parts by weight: 20-25 parts of coal gangue, 2-4 parts of nanometer aluminum oxide, 10-15 parts of mesh soil, 8-12 parts of sea mud, 5-10 parts of polyvinyl acetate, 4-6 parts of tung oil, 3-6 parts of waste syrup, 1-2 parts of sodium lauroyl sarcosine, 3-5 parts of abienic balsam, 4-8 parts of asbestos wool, 6-8 parts of additives and a defined amount of water. A sintered brick provided by the invention takes coal gangue as the main raw material, so that the clay resource is saved, the production cost is lowered, the problem of processing of coal gangue is solved and the environmental pollution is avoided. Besides, the sintered brick provided by the invention has the advantages of being high in strength, high in loading capacity, low in density, and low in heat conductivity coefficient, and meeting the requirement of people, wide application scope and wide market prospect.
Description
technical field [0001] The invention relates to the technical field of building materials, in particular to a dust-absorbing polymer nano-graphene-loaded fiber bundle and a production method thereof. Background technique [0002] At present, most bricks are prepared by sintering clay. However, with the increase of clay mining, clay resources are increasingly scarce, which not only increases the mining cost, but also has a serious impact on the ecological environment. Therefore, it is urgent to optimize and improve the existing bricks. There are brick-making methods to change the status quo. [0003] Decomposing zircon sand with sodium hydroxide is the main production process for producing zirconium oxychloride and zirconium dioxide in my country. my country's annual production capacity of zirconium oxychloride reached 150,000 tons in 2007, ranking first in the world. The demand for zirconia as a functional material and structural material is also increasing, and its produc...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more