Preparation method of ozone non-homogeneous oxidation solid catalyst

Abstract

The invention relates to a preparation method of an ozone non-homogeneous oxidation solid catalyst and belongs to the technical field of environmental protection and chemical catalysts. The preparation method comprises the following steps: taking attapulgite, diopside, bentonite, polyhalite, brucite and a serpentine porous material as carriers; adding surfactant trioctylmethylammonium chloride for surface activation treatment under the ultrasonic action after the carriers are subjected to lithium hypochlorite and bis (acetylacetone) beryllium reaming and modification; then enabling the ultrasonic surface activation carriers to perform hydrothermal reaction with compound mineralizer borax and potassium sulfate, catalytic activity auxiliary precursor tris(3-trifluoroacetyl-D-camphor) praseodymium (III), 1,1,1-trifluoroacetylacetone neodymium, holmium oxalate, a lutetium carbonate hydrate rare earth metal organic compound, catalytically-active central component precursor general transition metal organic compound ferrous fumarate, nickel citrate, zinc lactate and precious metal compound tetrachlorate potassium in a hydrothermal reactor under the action of emulsifier tri-cetylmethyl ammonium chloride; drying a reaction product, removing moisture and then firing at a certain temperature in a muffle furnace to obtain the ozone non-homogeneous oxidation solid catalyst.

Description

technical field [0001] The invention relates to a preparation method of a solid catalyst for ozone heterogeneous oxidation, which belongs to the technical fields of environmental protection and chemical catalysts. Background technique [0002] Ozone oxidation technology utilizes the strong oxidation ability of ozone, which can oxidize and decompose many organic pollutants, and is widely used in wastewater treatment. Ozone catalytic oxidation technology is divided into ozone homogeneous catalytic oxidation and ozone heterogeneous catalytic oxidation. Ozone homogeneous catalytic oxidation has catalysts that are difficult to separate, recycle and reuse, and the low utilization rate of ozone leads to high water treatment operation costs. Ozone heterogeneous catalytic oxidation technology has the advantages of easy separation and recovery of catalysts and reusable use, high ozone utilization rate, and high removal rate of organic pollutants, which reduces water treatment. The ad...

AI Technical Summary

Problems solved by technology

[0004] In view of the problems of low catalyst adsorption, poor anti-toxicity and easy loss of catalytic activity in the current preparation method of ozone heterogeneous oxidation solid catalyst, a multi-component porous carrier was developed to enhance the adsorption of the catalyst through pore expansion and surface activation. Rare earth metal organic compounds as precursors of catalytic active additives, common transition metal organic compounds and noble metal compounds as precursors of catalytic active centers and multi-component porous carriers through hydrothermal reaction and high temperature calcination to prepare ozone heterogeneous oxidation containing multiple metals The preparation method of solid catalyst to improve the anti-toxicity and catalytic activity of the catalyst is characterized in that component A and deionized water are added into a sealable reactor and stirred to prepare an aqueous solution, and the weight concentration of component A is controlled to be 2% to 6%. After the preparation is completed, add component B under stirring, raise the temperature to 35°C-50°C, continue to stir for 3h-6h, filter, and dry the reaction product at 102°C-106°C to obtain a modified carrier for pore expansion; pore expansion Put the modified carrier into the ultrasonic reactor, add the aqueous solution prepared by C component and deionized water, the weight concentration of C component is 3%~8%, stir and mix evenly, control the ultrasonic power density to 0.3~0.8W / m 3 , frequency 20kHz ~ 30kHz, 40 ℃ ~ 55 ℃, ultrasonic vibration 2h ~ 5h, the ultrasonic surface activation carrier mixture is obtained; the ultrasonic surface activation carrier mixture is transferred to the hydrothermal reaction kettle, and then add D component and deionized water to prepare The aqueous solution, the weight concentration of D component is 40% ~ 55%, by weight, the weight ratio of D component deionized aqueous solution: ultrasonic surface activation carrier mixture = 1: (1.5 ~ 2), control temperature 120 ℃ ~ 180°C, the hydrothermal reaction time is 8h~16h, and then dried to obtain fine particles; the fine particles are burned in a muffle furnace at 600°C~950°C for 3h~8h to obtain a solid catalyst for ozone heterogeneous oxidation