All-solid-state battery and preparation method thereof

A technology of all-solid-state batteries and solid-state electrolytes, which is applied in the manufacture of electrolyte batteries, battery electrodes, secondary batteries, etc., and can solve problems such as large interface resistance, poor thermal stability, and obstacles to the development of solid-state battery technology

Active Publication Date: 2020-12-04
SOUNDON NEW ENERGY TECH CO LTD
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Since Bellcore successfully prepared polymer lithium-ion batteries with conductive polymer materials as solid electrolytes in 1994, polymer lithium-ion batteries have developed rapidly. Although polymer materials are simple to prepare, have strong plasticity, good safety performance, and lithium ion migration numbers High, but its low ionic conductivity and poor thermal stability seriously affect its application in lithium-ion batteries
The inorganic ionic conductors developed later have good thermal stability and high ionic conductivity. Introducing the inorganic ionic conductors into the polymer electrolyte can improve the mechanical properties and ionic conductivity of the electrolyte. There is a serious interface incompatibility between them, and the interface resistance is large, which hinders the development of solid-state battery technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • All-solid-state battery and preparation method thereof
  • All-solid-state battery and preparation method thereof
  • All-solid-state battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0078] The preparation method of the positive electrode material with the above-mentioned three-layer core-shell structure is to dissolve a certain quality of soluble lithium source, soluble titanium source, soluble aluminum source, and soluble phosphate in water or a mixed solvent of water and an organic solvent, and add a certain amount of glue Coagulant, adjust the pH to close to neutral to form a sol; add Al(OH) under constant stirring 3 Coated ternary cathode material precursor or Al 2 o 3 The coated ternary cathode material is heated to the sol solution, and coagulation occurs to obtain a gel, so that Al(OH) 3 The coated ternary cathode material precursor is coated with Li, Ti, Al and phosphate, and some lithium ions in the solution will penetrate into the inner layer and be embedded on the ternary cathode material precursor. The gel is calcined in an oxygen-containing atmosphere to obtain a three-layer core-shell structure cathode material, that is, the core changes f...

Embodiment 1

[0087] 1. Preparation of positive electrode active material:

[0088] (1) Lithium nickel cobalt manganese oxide LiNi 0.6 co 0.2 mn 0.2 o 2 Preparation of the precursor of the ternary cathode material:

[0089] 109.620g nickel nitrate Ni(NO 3 ) 2 , 58.211g cobalt nitrate Co(NO 3 ) 2 ·6H 2O, 35.790g manganese nitrate Mn(NO 3 ) 2 Add it to 700ml of isopropanol, and then add 1mol / L ammonium bicarbonate solution dropwise thereto until the pH of the solution is 10-12. Then put it in a polytetrafluoroethylene reactor for solvothermal reaction at 150° C. for 12 hours, and then filter and wash to obtain a ternary cathode material precursor.

[0090] (2) Preparation of aluminum hydroxide-coated ternary cathode material precursor:

[0091] Add the above-mentioned ternary cathode material precursor to 42.0ml of 0.01mol / L aluminum sulfate solution and stir to form a uniform dispersion, then slowly add sodium bicarbonate solution dropwise to it while stirring until no more gas i...

Embodiment 2

[0110] Embodiment 2 is the same as step 2-step 4 of embodiment 1, the difference is only that the preparation process of the positive electrode active material in step 1 is as follows:

[0111] (1) Lithium nickel cobalt manganese oxide LiNi 0.8 co 0.1 mn 0.1 o 2 Preparation of the precursor of the ternary cathode material:

[0112] 146.16 (0.8mol) nickel nitrate Ni (NO 3 ) 2 , 29.10g (0.1mol) cobalt nitrate Co(NO 3 ) 2 ·6H 2 O, 17.90g (0.1mol) manganese nitrate Mn (NO 3 ) 2Add it to 700ml of ethanol, and then dropwise add 1mol / L ammonium bicarbonate solution therein until the pH of the solution is 10-12. Then place it in a polytetrafluoroethylene reactor for solvothermal reaction at 150° C. for 12 hours, and then filter and wash to obtain a positive electrode material precursor.

[0113] (2) Preparation of alumina-coated ternary cathode material precursor:

[0114] Add the above-mentioned spherical precursor to 42.0ml of 0.01mol / L aluminum nitrate solution and stir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical conductivityaaaaaaaaaa
electrical conductivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to an all-solid-state battery, which comprises a positive pole and a solid electrolyte, the positive active material on the surface of the positive pole is in contact with the solid electrolyte, and the positive active material and the solid electrolyte contain the same substance. Preferably, the same material composition is the fast ion conductor Li 1+x Al x Ti 2‑x (PO 4 ) 3 (0<x≤0.5). Thus, the composition of the solid electrolyte and the composition of the positive electrode active material contain the same substance, thereby improving the homogeneous compatibility between the positive electrode of the battery and the solid electrolyte, and reducing the interface resistance. The invention also relates to a preparation method of the all-solid-state battery.

Description

technical field [0001] The invention belongs to the field of new energy materials and electrochemistry, and in particular relates to an all-solid-state battery and a preparation method thereof. Background technique [0002] Lithium-ion batteries have the characteristics of high energy density, long cycle life, no memory effect, and no pollution to the environment. They have been widely used in portable electronic devices and power vehicles. Therefore, lithium-ion batteries and their related materials have become a hot research topic at present. [0003] Traditional lithium-ion batteries generally use organic electrolytes and separators, which are prone to serious safety hazards such as flammability, explosion, and night leakage during use. In order to solve safety problems, the development of all-solid-state batteries has become a future development trend. Compared with traditional liquid lithium-ion batteries, solid-state batteries have obvious advantages: (1) solid-state...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/056H01M10/058H01M10/0525H01M4/36H01M4/485H01M4/62
CPCH01M4/366H01M4/485H01M4/624H01M10/0525H01M10/056H01M10/058H01M2300/0065H01M2300/0091Y02E60/10Y02P70/50
Inventor 靳岩娄忠良胡泽林
Owner SOUNDON NEW ENERGY TECH CO LTD