Antibacterial latex paint and preparation method thereof
A technology of latex paint and nano antibacterial agent, applied in the field of latex paint, can solve the problems of mold growth, poor craftsmanship, blackening and peeling off the paint film, and achieve the effect of inhibiting agglomeration, wide application field and good weather resistance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0020] Example 1:
[0021] This embodiment provides an antibacterial latex paint, the latex paint comprising the following parts by weight: 100 parts of water, 9 parts of hydroxyethyl cellulose, 100 parts of modified acrylic emulsion, 27 parts of alumina modified nano titanium dioxide, ZnO w 7 parts of nano antibacterial agent, 30 parts of nano silicon dioxide, 4 parts of dispersant, 0.2 part of polydimethylsiloxane, 1 part of propylene glycol methyl ether acetate.
[0022] The modified acrylic emulsion is an organic fluorine modified acrylic emulsion, which is specifically obtained by copolymerizing the following parts by mass of monomers: 24 parts of methyl methacrylate, 42 parts of butyl acrylate, 12 parts of methacrylic acid, and methacrylic acid 6 parts of hexafluorobutyl ester;
[0023] The alumina modified nano-titania is made of TiCl 4 , Al 2 (SO 4 ) 3 As raw material, Al prepared by co-precipitation method 2 O 3 / TiO 2 Nanoparticle
[0024] The average particle size of the n...
Example Embodiment
[0033] Example 2:
[0034] This embodiment provides an antibacterial latex paint. The latex paint includes the following parts by weight: 100 parts of water, 8 parts of hydroxyethyl cellulose, 90 parts of modified acrylic emulsion, 30 parts of alumina-modified nano titanium dioxide, ZnO w 7 parts of nano antibacterial agent, 26 parts of nano silicon dioxide, 2 parts of dispersant, 0.1 part of ethylene glycol siloxane, and 1 part of propylene glycol methyl ether acetate.
[0035] The modified acrylic emulsion is an organic fluorine modified acrylic emulsion, and the specific ratio is the same as in Example 1;
[0036] The alumina-modified nano-titania is the same as in Example 1;
[0037] The average particle size of the nano-silica is 24 nm;
[0038] ZnO w The nano antibacterial agent has a four-needle whisker structure;
[0039] The dispersant is a composite of sodium lauryl sulfate and 1-butyl-3-methylimidazole tetrafluoroborate, and the mass ratio of the two is 1:0.4.
[0040] The pre...
Example Embodiment
[0041] Example 3:
[0042] This embodiment provides an antibacterial latex paint. The latex paint includes the following parts by weight: 100 parts of water, 12 parts of hydroxyethyl cellulose, 115 parts of modified acrylic emulsion, 38 parts of alumina modified nano titanium dioxide, ZnO w 8 parts of nano antibacterial agent, 36 parts of nano silicon dioxide, 5 parts of dispersant, 0.3 parts of fluorosiloxane, and 2 parts of diethylene glycol butyl ether.
[0043] The modified acrylic emulsion is an organic fluorine modified acrylic emulsion, and the specific ratio is the same as in Example 1;
[0044] The alumina-modified nano-titania is the same as in Example 1;
[0045] The average particle size of the nano-silica is 17 nm;
[0046] ZnO w The nano antibacterial agent has a four-needle whisker structure;
[0047] The dispersant is a composite of sodium lauryl sulfate and 1-butyl-3-methylimidazole tetrafluoroborate, and the mass ratio of the two is 1:0.6;
[0048] The preparation metho...
PUM
Property | Measurement | Unit |
---|---|---|
The average particle size | aaaaa | aaaaa |
The average particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap