A high-strength super wear-resistant flame-retardant waterproof membrane and its preparation method and application

A waterproof membrane, super wear-resistant technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, lamination, etc., can solve the problem of increasing the production cost of PVC waterproof membrane, failing to improve the strength and flame retardancy, physical Reduced performance and use time, etc., to achieve the effects of easy cleaning and maintenance, good flame retardant and anti-aging effects, and good covering function

Active Publication Date: 2022-04-05
TONGJI UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the cost of bitumen waterproofing membrane is low, its temperature stability is poor, it is easy to flow at high temperature, easy to be brittle at low temperature, and has a short service life
PVC waterproof membrane is a common thermoplastic polymer membrane. This membrane has good dimensional stability and low thermal expansion coefficient, but its physical properties will decrease rapidly with time.
[0004] Judging from the content of invention patents related to PVC waterproofing membranes in recent years, most of the patents simply compound PVC and polyester or modify the surface of PVC waterproofing membranes with asphalt and other polymer coatings. These two methods mainly contribute to improving the corrosion resistance, self-adhesiveness and antistatic properties of waterproof membranes, but fail to improve their strength and flame retardancy.
In addition, there are also some patents that have carried out more detailed research on the production process and production equipment of PVC waterproof coiled materials, but the process and equipment requirements are very complicated, which has increased the production cost of PVC waterproof coiled materials to a certain extent. Little practical significance for mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength super wear-resistant flame-retardant waterproof membrane and its preparation method and application
  • A high-strength super wear-resistant flame-retardant waterproof membrane and its preparation method and application
  • A high-strength super wear-resistant flame-retardant waterproof membrane and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] Preparation method of high strength super-resistant flame retardant waterproof coil, such as figure 1 and figure 2 , Includes the following steps:

[0048] (1) Waste epoxy resin, polyvinyl chloride recovery, heat stabilizer, light stabilizer, antioxidant, plasticizer, nano flame retardant, and amount of polyvinyl chloride recovery from 0.5-1% The agent was carried out in a high-speed mixer in the order of the first solid post-liquid, and the temperature was controlled at 130-150 ° C, the stirring time was about 3.5-4 min, the stirring speed was about 500-900 r / min, and the mixture was uniformly obtained. Waterproof layer material;

[0049] Polyester, the amount of 0.5-1% of the polyester and the thermostable agent and the heat stabilizer were added in the order of the first-solid retrorefluid, and the temperature was controlled at 130-150 ° C, the stirring time was about 3.5-4 min. , The stirring speed is about 500-900 r / min, and the inner layer of the polyester is obta...

Embodiment 1

[0067] (1) Waste epoxy resin, recovery PVC, heat stabilizer-liquid calcium / zinc composite stabilizer, light stabilizer - 2- (2'-hydroxy-5'-methylphenyl) benzotriazole , Antioxidant-four [β- (3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythritol ester, plasticizer-phthalate, nano-flame retardant- - Nano-water talc and dosage are 0.5% antistatic agent-polyether amideimide, in the order of the first solid retrofit, and the temperature is controlled at 130 ° C, stirring Time is about 3.5 min, the stirring speed is about 500 r / min, and the waterproof layer material is obtained after mixing.

[0068] The ethylene-vinyl acetate copolymer is used as an ethylene-vinyl acetate copolymer 0.5% antistatic agent-polyethylene oxide and thermally stabilizer-liquid calcium / zinc composite stabilizer, in the order of the first solid Mixing stirring was carried out in a high-speed mixer, the temperature was controlled at 130 ° C, stirring time was about 3.5 min, and the stirring ve...

Embodiment 2

[0088] As compared with Example 1, the recovery PVC, the abandoned epoxy resin, and various auxiliaries in step (1) were changed from 130 ° C to 140, and the other conditions remain unchanged.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-strength super-abrasion-resistant and flame-retardant waterproof coiled material and its preparation method and application. The high-strength super-abrasive and flame-retardant waterproof coiled material uses recycled PVC and waste epoxy resin as raw materials, and adds Appropriate ethylene-vinyl acetate copolymers, nano-flame retardants, anti-aging agents and antistatic agents and other additives are prepared by mixing, banburying and extrusion, and then co-calendering with glass fiber cloth. The anti-aging agent contains heat stabilizers, antioxidants and light stabilizers, which can weaken the intensity of ultraviolet rays and sunlight. The addition of glass fiber cloth can improve the tensile properties of the product, promote the adjustment of indoor climate, prevent moisture and mildew, and prolong the service life. , easy to construct, and has a good application prospect.

Description

Technical field [0001] The present invention relates to building solid waste recovery reuse and waterproof material, and therefore referring to a high-strength super-resistant flame retardant waterproof web and a preparation method thereof. Background technique [0002] As people improve their quality requirements, the requirements for prevent leakage of housing, tunnels and highways are also increasing. Waterproofing web is a canable curvature-shaped flexible building materials that can resist outside rainwater, groundwater leakage, is the first barrier for the entire project waterproof. [0003] Conventional waterproof web has asphalt waterproof materials and synthetic polymer waterproof coil. Although the asphalt waterproof coil is low, the temperature is poor, high temperature is easy to flow, low temperature and easy brush, and short use. PVC waterproof web is a common thermoplastic polymer web that has better dimensional stability and lower thermal expansion coefficient, bu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L63/00C08L79/08C08L23/08C08L71/02C08K5/3475C08K5/134C08K5/12C08K3/26B32B27/30B32B17/02B32B17/10B32B27/36B32B37/10B32B38/00
CPCC08L27/06C08L23/0853B32B27/304B32B27/12B32B5/02B32B27/36B32B37/10B32B38/00C08L2201/02C08L2201/04C08L2201/08B32B2038/0064B32B2262/101B32B2307/21B32B2307/3065B32B2307/554B32B2307/7265B32B2270/00B32B2272/00C08L63/00C08L79/08C08K5/3475C08K5/1345C08K5/12C08K3/26C08L71/02
Inventor 杨正龙陈羽雯姚武
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap