Acrylic ester modifier and preparation and use in bisphenol A poly carbonate
A technology of acrylates and modifiers, applied in the field of acrylate modifiers prepared from organic-inorganic hybrid materials, can solve the problem of reducing PC heat resistance, reducing optical properties, reducing PC tensile strength and bending mold It is easy to replace the formula, the process is simple, and the performance is improved.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0032] Example 1
[0033] First, dry the nano-silica in an oven at 105°C for 2 hours. Add the silane coupling agent KH-570 and xylene to the dried nano-particles. Stir in the air for 20 minutes, protect by nitrogen, and then put it in an oil bath. Heat to 140°C in the medium, stir, and control the reaction temperature at the reflux temperature of xylene at 140°C. After reacting for 10 hours, leave the product to stand. After layering, vacuum dry the lower layer to obtain alkylated nano-silica. The weight ratio between each material is:
[0034] Nano silica: KH-570: xylene = 10: 2: 250;
[0035] Then add the alkylated nanoparticles and emulsifier to the deionized water, pass nitrogen protection, start stirring, when the temperature rises to 70 ℃, add ammonium persulfate, butyl acrylate and methyl methacrylate step by step. After the reaction is completed, it is cooled to room temperature, and the emulsion is spray-dried to obtain a white powder. The weight ratio between the materia...
Example Embodiment
[0038] Example 2
[0039] First, dry the nano-silica in an oven at 105°C for 2 hours. Add the silane coupling agent KH-570 and xylene to the dried nano-particles. Stir in the air for 20 minutes, protect by nitrogen, and then put it in an oil bath. Heat to 140°C in the medium, stir, and control the reaction temperature at the reflux temperature of xylene at 140°C. After reacting for 10 hours, leave the product to stand. After layering, vacuum dry the lower layer to obtain alkylated nano-silica. The weight ratio between each material is:
[0040] Nano silica: KH-570: xylene = 10: 2: 250;
[0041] Then add the alkylated nano silica and emulsifier to the deionized water, pass nitrogen protection, start stirring, when the temperature rises to 70 ℃, add ammonium persulfate and methyl methacrylate step by step, the reaction is complete After cooling to room temperature, the emulsion was spray-dried to obtain a white powder,
[0042] The weight ratio between the materials is: alkylated na...
Example Embodiment
[0044] Example 3
[0045] First, the nano-zinc oxide was dried in an oven at 105°C for 2 hours, then KH-570 and xylene were added to the dried nanoparticles, stirred in the air for 20 minutes, protected by nitrogen, and then heated to 140°C in an oil bath , Stirring, the reaction temperature is controlled at the reflux temperature of xylene at 140 ℃, after 10 hours of reaction, the product is allowed to stand, after stratification, the lower layer material is vacuum-dried to obtain alkylated nano zinc oxide, wherein the weight of each material Than:
[0046] Nano zinc oxide: KH-570: xylene = 10: 2: 250;
[0047] Then add the alkylated nanoparticles and emulsifier to the deionized water, pass nitrogen protection, start stirring, when the temperature rises to 70 ℃, dropwise add ammonium persulfate, 2-ethylhexyl acrylate and methyl After the reaction is complete, the methyl acrylate is cooled to room temperature, and the emulsion is spray-dried to obtain a white powder. The weight ra...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap