Antistatic reinforced polyphenylene sulfide composite material and method for making same

A technology of polyphenylene sulfide and composite materials, which is applied in the direction of chemical instruments and methods, and other chemical processes, can solve the problems of volume resistivity decline of composite materials, achieve low cost, durable antistatic properties, and improve processing performance.

Active Publication Date: 2008-03-05
GUANGDONG SILVER AGE SCI & TECH CO LTD
View PDF0 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are shared electron pairs on the ether oxygen atoms in the molecular chains of hydrophilic polymers such as polyethylene oxide, polyethylene glycol and their maleate derivatives, which have a strong tendency to form hydrogen bonds; alkali metal ions can share with The electron pairs coordinate to form an association complex and form a conductive path with the migration of the polyelectrolyte in the polyphenylene sulfide. The higher the content of alkali metal ions, the greater the probability of forming an effective conductive path, so

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1

[0020] 300 parts of polyphenylene sulfide, 5 parts of lithium chloride, 40 parts of polyethylene oxide, 550 parts of glass fiber, 90 parts of sulfonated styrene-butadiene-styrene copolymer, 9 parts of aluminate coupling agent, After 2 parts of antioxidant 1010 and 4 parts of processing aids are dispersed and mixed by a high-speed mixer, they are melted, mixed, extruded, cooled, dried, pelletized and packaged by a twin-screw extruder. The resulting composite material has a volume resistivity of 4.1×10 9 Ω.cm

[0021] The speed of the high-speed mixer is 2000r / min, and the mixing time is 5-30min. The temperature of each zone of the screw barrel of the twin-screw extruder used is kept at 280-340℃, the main engine speed is 100r / min, and the feeding speed is 40r / min. It is cooled by water and dried at 120℃ with hot air. After the extruded product is fully dried, it is injected with an injection molding machine according to the standard size to form a test standard sa...

Example Embodiment

[0022] Example 2

[0023] 300 parts of polyphenylene sulfide, 5 parts of potassium chloride, 40 parts of polyethylene glycol bismaleate, 300 parts of glass fiber, 250 parts of calcium carbonate, 90 parts of methyl methacrylate-butadiene-styrene After the copolymer, 9 parts of KH550, 2 parts of B215, and 4 parts of processing aids are dispersed and mixed by a high-speed mixer, they are melted, mixed, extruded, cooled, dried, pelletized and packaged by a twin-screw extruder. The resulting composite material has a volume resistivity of 6.5×10 9 Ω.cm

Example Embodiment

[0024] Example 3

[0025] Combine 800 parts of polyphenylene sulfide, 5 parts of sodium bromide, 40 parts of polyethylene glycol, 100 parts of glass fiber, 45 parts of styrene-butadiene-maleic anhydride copolymer, 5 parts of butyl titanate, 2 parts After B215, 3 parts of processing aids are dispersed and mixed by a high-speed mixer, they are melted, mixed, extruded, cooled, dried, pelletized and packaged by a twin-screw extruder. The resulting composite material has a volume resistivity of 3.2×10 9 Ω.cm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Volume resistivityaaaaaaaaaa
Volume resistivityaaaaaaaaaa
Volume resistivityaaaaaaaaaa
Login to view more

Abstract

The present invention discloses antistatic reinforced polyphenyl thioether composite material and its preparation process. The composite material consists of polyphenyl thioether 30-80 weight portions, glass fiber 20-60 weight portions, inorganic mineral filler 0-40 weight portions, hydrophilic polymer 3-10 weight portions, alkali metal salt 0.2-3 weight portions, interface modifier 2-10 weight portions, coupling agent 0.1-2 weight portions, antioxidant 0.1-1 weight portion, and processing aid 0.1-1 weight portion. The antistatic reinforced polyphenyl thioether composite material has excellent mechanism performance, excellent antistatic performance and high durability, and may be used in coal mine machine, business machine, fixed disk driver, etc.

Description

technical field [0001] The invention relates to an antistatic reinforced polyphenylene sulfide composite material and a preparation method thereof. Background technique [0002] Polyphenylene sulfide (PPS), also known as polyphenylene sulfide and polyphenylene sulfide, is a sulfur-containing aromatic polymer with a structural formula of , the sulfur atoms and benzene rings on the main chain of the molecule are neatly arranged alternately, which endows the molecule with highly stable chemical bond characteristics, and is easy to accumulate into a crystal lattice structure with high thermal stability, which makes it have many unique properties. The melting point is as high as 280-290 °C, the decomposition temperature is greater than 400 °C, almost insoluble in any solvent below 200 °C, the long-term continuous use temperature is 200-240 °C, low hygroscopicity, no deformation under high temperature and high humidity conditions and can maintain excellent electrical insulation, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L81/02C08K7/14C09K3/16B29C47/40B29B9/12C08L71/02C08L53/02C08K3/00C08K5/521B29C48/40
CPCB29C48/40
Inventor 谭颂斌傅轶
Owner GUANGDONG SILVER AGE SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap