High-efficient, environmentally-friendly, anti-corrosion and waterproof coating for subway shield segment and preparation method thereof

A technology of shield segment and waterproof coating, which is used in anti-corrosion coatings, anti-fouling/underwater coatings, fire-resistant coatings, etc., can solve the problems of poor adhesion of water-based waterproof coatings, toxic and harmful to human body and the environment, and greased oil-based waterproof coatings. and other problems, to achieve the effect of anti-corrosion and waterproofing, high efficiency, environmental protection, environmental friendliness, and reducing the peak heat release rate.

Inactive Publication Date: 2018-04-27
合肥卓立雅工程材料科技有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solvent-based waterproof coatings contain organic solvents, long-term use is poisonous and harmful to the human body and the environment, and their safety is poor. Oily waterproof coatings will be fattened and cracked when they are in contact with water for a long time.
Although water-based waterproof coatings do not contain organic solvents, water-based waterproof coatings usually have poor adhesion and unstable waterproof effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A high-efficiency, environment-friendly, anti-corrosion and waterproof coating for subway shield segments is made of the following raw materials in parts by weight:

[0028] Material A: 35 parts of modified epoxy resin, 10 parts of nano-zinc oxide, 5 parts of chitosan, 20 parts of nano-light calcium carbonate, 10 parts of nano-silica, 35 parts of styrene-acrylic emulsion, 15 parts of titanium dioxide, paraffin wax 1 part, 0.5 parts of calcium stearate, 12 parts of silicone oil, 3 parts of polyacrylic acid, 8 parts of alcohol ester twelve parts, 5 parts of disodium edetate, 3 parts of sorbic acid, 10 parts of cinnamon extract, flame retardant 3 copies;

[0029] Material B: 55 parts of modified organic amines, 2 parts of carboxymethyl cellulose, 10 parts of ethylene glycol, 30 parts of cement, 1.2 parts of toner, 5 parts of mica powder, 7 parts of diethylene glycol, 15 parts of titanium dioxide , 1.5 parts of stearic acid, 2 parts of preservatives, 15 parts of water.

...

Embodiment 2

[0036] A high-efficiency, environment-friendly, anti-corrosion and waterproof coating for subway shield segments is made of the following raw materials in parts by weight:

[0037] Material A: 50 parts of modified epoxy resin, 5 parts of nano-zinc oxide, 8 parts of chitosan, 15 parts of nano-light calcium carbonate, 15 parts of nano-silica, 20 parts of styrene-acrylic emulsion, 25 parts of titanium dioxide, paraffin wax 0.5 parts, 1 part of calcium stearate, 5 parts of silicone oil, 5 parts of polyacrylic acid, 5 parts of alcohol ester twelve parts, 7 parts of disodium edetate, 5 parts of sorbic acid, 5 parts of cinnamon extract, flame retardant 8 copies;

[0038] Material B: 45 parts of modified organic amines, 4 parts of carboxymethyl cellulose, 5 parts of ethylene glycol, 50 parts of cement, 0.5 parts of toner, 10 parts of mica powder, 3 parts of diethylene glycol, 20 parts of titanium dioxide , 0.5 parts of stearic acid, 3 parts of preservatives, 10 parts of water.

[00...

Embodiment 3

[0041] A high-efficiency, environment-friendly, anti-corrosion and waterproof coating for subway shield segments is made of the following raw materials in parts by weight:

[0042] Material A: 40 parts of modified epoxy resin, 8 parts of nano-zinc oxide, 7 parts of chitosan, 17 parts of nano-light calcium carbonate, 12 parts of nano-silica, 30 parts of styrene-acrylic emulsion, 20 parts of titanium dioxide, paraffin wax 0.8 parts, 0.7 parts of calcium stearate, 9 parts of silicone oil, 4 parts of polyacrylic acid, 6 parts of alcohol ester dodecane, 6 parts of disodium edetate, 4 parts of sorbic acid, 8 parts of cinnamon extract, flame retardant 5 copies;

[0043] Material B: 50 parts of modified organic amines, 3 parts of carboxymethyl cellulose, 7 parts of ethylene glycol, 40 parts of cement, 1 part of toner, 8 parts of mica powder, 5 parts of diethylene glycol, 17 parts of titanium dioxide , 1 part of stearic acid, 2.5 parts of preservatives, and 13 parts of water.

[0044...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a high-efficient, environmentally-friendly, anti-corrosion and waterproof coating for a subway shield segment and a preparation method thereof and relates to the technical fieldof coatings. The coating is prepared from a material A: 35 to 50 parts by weight of modified epoxy resin, 5 to 10 parts by weight of nano-zinc oxide, 5 to 8 parts by weight of chitosan, 15 to 20 parts by weight of nanometer light calcium carbonate, 10 to 15 parts by weight of nano-silica, 20 to 35 parts by weight of a styrene-acrylic emulsion, 15 to 25 parts by weight of titanium dioxide, 0.5 to1 part by weight of paraffin, 0.5 to 1 part of calcium stearate, 5 to 12 parts by weight of silicone oil, 3 to 5 parts by weight of polyacrylic acid, 5 to 8 parts by weight of texanol, 5 to 7 parts byweight of disodium EDTA, 3 to 5 parts by weight of sorbic acid, 5 to 10 parts by weight of cassia bark extract and 3 to 8 parts by weight of a flame retardant. The coating has the characteristics ofstrong weather resistance and low use cost and is waterproof, efficient, anticorrosion and environmentally friendly.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a high-efficiency, environment-friendly, anti-corrosion and waterproof coating for subway shield segments and a preparation method thereof. Background technique [0002] The waterproof coating used in the construction industry is generally a viscous liquid polymer synthetic material with no fixed shape at room temperature. After coating, it will form a waterproof film on the surface of the base layer after solvent volatilization or water evaporation or reaction curing. At present, the waterproof materials used in the construction industry are generally divided into flexible waterproof materials including waterproof membranes, waterproof coatings, sealing ointments, etc., and rigid waterproof materials based on cement substrates, adding waterproofing agents and other additives. Although there are many types, they generally have disadvantages such as poor physical and mechanical p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D125/14C09D5/18C09D5/14C09D5/08C09D7/61C09D7/63C09D7/65
CPCC08K2003/2296C08K2201/003C08K2201/011C08K2201/018C08L2201/06C08L2205/035C09D5/08C09D5/14C09D5/18C09D125/14C09D163/00C08L5/08C08L25/14C08L33/00C08L1/286C08L83/04C08K13/02C08K3/22C08K5/175C08K5/092C08K5/0058C08K5/49C08K5/47C08K5/3447C08K3/36
Inventor 张健
Owner 合肥卓立雅工程材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap