Polypropylene master batch and preparation method thereof

A polypropylene and masterbatch technology, applied in the field of polypropylene materials, can solve the problem of limited application fields, environmental pollution, polypropylene impact strength, melt index elongation at break, and relative tensile force that cannot meet the requirements of raw materials, etc. question

Inactive Publication Date: 2018-06-29
NINGXIA YANCHI WEST CHANGXIANG AGRI BIOTECH
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Most of the high temperature and low temperature resistant patents disclosed above are modified high temperature resistant polypropylene. It is less than the requirements for the use of raw materials, which limits the application field.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene master batch and preparation method thereof
  • Polypropylene master batch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Embodiment 1 raw material preparation

[0054] 1. Preparation of calcium fruit fiber:

[0055] The preparation method of the calcium fruit fiber comprises the following steps: uniformly mixing fresh calcium fruit stems, calcium fruit leaves and waste sawdust at a mass ratio of 7:4:1.5, placing them in an ultrasonic cleaning machine at 200W and 30KHz for cleaning for 4 minutes, draining Drying, crushing, adding water with 1 times the amount of the crushed material, ultrasonic extraction at room temperature 300W, 40KHz for 12min, and then performing high-voltage pulse electric field treatment for 12min under the conditions of electric field strength 30kV / cm, pulse time 500μs, and pulse frequency 300Hz; adjust the pH value 8. Add biological enzyme with 0.2% mass of the mixture, and enzymatically hydrolyze at 55°C for 12 minutes; the enzymolyzed solution is concentrated under reduced pressure to a solid content of 50%, and placed in a microwave dryer at 2000W and 140°C for ...

Embodiment 2

[0077] A polypropylene masterbatch, mainly prepared from the following raw materials in parts by weight:

[0078] 40 parts of polypropylene, 17 parts of calcium fruit fiber, 12 parts of modified carbon nanotubes, 3 parts of polyethylene / winter rye peptide complex, 2 parts of ultraviolet absorber, 2 parts of ethylene-methyl acrylate copolymer, anti-aging agent 2 parts, 1 part of tributyl citrate, 1 part of coupling agent, 0.8 part of polyethylene wax, 0.4 part of composite antioxidant, 0.2 part of bitter almond oil;

[0079] The ultraviolet absorber is UV-531.

[0080] The ethylene-methyl acrylate copolymer is DuPont EMA1125AC of the United States.

[0081] The composite antioxidant is uniformly mixed with antioxidant 1010, antioxidant 168 and biological antioxidant at a mass ratio of 1.5:2:3.

[0082] The preparation method comprises the following steps: first, accurately weigh each raw material according to the formula, and according to the principle of the equal-increment ...

Embodiment 3

[0084] A polypropylene masterbatch, mainly prepared from the following raw materials in parts by weight:

[0085] 30 parts of polypropylene, 16 parts of calcium fruit fiber, 10 parts of modified carbon nanotubes, 2 parts of polyethylene / winter rye peptide complex, 1 part of ultraviolet absorber, 1.5 parts of ethylene-methyl acrylate copolymer, anti-aging agent 1.2 parts, 0.8 parts of tributyl citrate, 0.8 parts of coupling agent, 0.6 parts of polyethylene wax, 0.3 parts of composite antioxidant, 0.1 part of bitter almond oil;

[0086] The ultraviolet absorber is UV-531.

[0087] The ethylene-methyl acrylate copolymer is DuPont EMA1125AC of the United States.

[0088] The composite antioxidant is uniformly mixed with antioxidant 1010, antioxidant 168 and biological antioxidant at a mass ratio of 1:1:2.

[0089] The preparation method comprises the following steps: first, accurately weigh each raw material according to the formula, and according to the principle of the equal-i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polypropylene master batch, and belongs to the technical field of polypropylene materials. The polypropylene master batch is characterized in that polypropylene is used as the base material; the types of the raw materials of the master batch and the formula are optimized; the production technology is improved; calcium fruit fibers which are capable of obviously improvingthe impact resistance of the polypropylene master batch and are easily biodegraded and are low in production cost, a modified nanotube which is capable of obviously improving the high temperature resistance, the relative stretching load, the strength, the toughness and the elastic modulus of the polypropylene master batch, a polyethylene/ fall rye peptide compound which is capable of greatly improving the low temperature resistance of the polypropylene master batch, and bitter almond oil and a composite antioxidant which are capable of effectively improving the lubricating performance and theoxidation resistance of the polypropylene master batch are scientifically compounded; and other processing additives synergize to prepare the environmentally-friendly polypropylene master batch with high physical performance.

Description

technical field [0001] The invention relates to a polypropylene material, in particular to a polypropylene masterbatch and a preparation method thereof. Background technique [0002] Polypropylene is a general-purpose plastic with good comprehensive properties, and its total output has surpassed polyvinyl chloride to become the second largest general-purpose plastic after polyethylene. Main features: non-toxic, odorless, low density, strength, stiffness, hardness and heat resistance are superior to low-pressure polyethylene, high bending fatigue resistance, can be used at about 100 degrees. It has good electrical properties and high frequency Insulation is not affected by humidity, but becomes brittle at low temperature, not wear-resistant, and easy to age. Because of its notch sensitivity, low heat distortion temperature, large molding shrinkage, poor hardness and wear resistance, its application in product packaging, automobiles, household appliances, construction and oth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L97/02C08L23/06C08L23/08C08L91/00C08K13/06C08K9/02C08K7/24C08K5/11C08K5/134C08K5/526C08H8/00C12N1/16C12P21/06C07K5/037C08J3/22C12R1/865
CPCC08L23/12C07K5/0215C08H8/00C08J3/226C08J2423/12C08K2201/011C08L2201/06C08L2201/08C08L2205/02C08L2205/035C08L2205/16C12N1/16C12P21/06C08L97/02C08L23/06C08L23/0869C08L91/00C08K13/06C08K9/02C08K7/24C08K5/11C08K5/1345C08K5/526
Inventor 李建树
Owner NINGXIA YANCHI WEST CHANGXIANG AGRI BIOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap