Ceramic coating material with characteristics of high-temperature resistance, high blackness, coking resistance and corrosion resistance

A technology of ceramic coatings and high blackness, applied in anti-corrosion coatings, coatings, etc., can solve problems such as climate warming, dissatisfaction, and high energy consumption, and achieve improved resistance, increased product production, and good adhesion Effect

Inactive Publication Date: 2018-07-20
甘肃华鑫石化科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional organic coatings, etc., have a huge impact on the environment. Not only the finished products often emit greenhouse gases and cause climate warming, but also release toxic substances in the air, causing diseases and deaths of people, animals and plants. It also consumes a lot of energy, does not meet the concept of low-carbon in my country, and produces various industrial sewage or toxic gases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A high-temperature-resistant, high-blackness, anti-coking, and corrosion-resistant ceramic coating is characterized in that the binder consists of 15% silica sol, 5% styrene-acrylic emulsion, 1% sodium oxide, 3% aluminum oxide monohydrate, The filler consists of 5% zirconia, 1% iron oxide red, 3% silicon nitride, 0.2% titanium nitride, 1% magnesium oxide, 3% chromium oxide, 1% aluminum oxide, 0.5% copper oxide by mass percentage , 5% kaolin, 2% mica powder, 0.5% sodium bentonite, 1% cerium oxide, 1% neodymium oxide, 1% lanthanum oxide, 1% yttrium oxide, 0.2% molybdenum oxide, and 1% niobium oxide. 0.3% dispersant by mass percentage, 0.2% wetting agent, 0.1% defoamer, 1% ammonia water, described filler, its zirconia, iron oxide red, silicon nitride, titanium nitride, magnesium oxide, The particle size of chromium oxide, copper oxide, kaolin, mica powder, sodium bentonite, cerium oxide, neodymium oxide, lanthanum oxide, yttrium oxide and niobium oxide is 100 nanometers, a...

Embodiment 2

[0015] A high-temperature-resistant, high-blackness, anti-coking, and corrosion-resistant ceramic coating is characterized in that the binder consists of 10% silica sol, 7% styrene-acrylic emulsion, 2% sodium oxide, 5% aluminum oxide monohydrate, The filler consists of 3% zirconia, 2% iron oxide red, 2% silicon nitride, 0.5% titanium nitride, 2% magnesium oxide, 5% chromium oxide, 1% copper oxide, 7% kaolin, 2.5% by mass percentage % mica powder, 0.7% sodium bentonite, 2% cerium oxide, 2% neodymium oxide, 2% lanthanum oxide, 2% yttrium oxide, 0.3% molybdenum oxide, 2% niobium oxide, the auxiliary agent is composed of 0.4% by mass percentage % dispersant, 0.3% wetting agent, 0.2% defoamer, 2% ammonia water, the filler, its zirconia, iron oxide red, silicon nitride, titanium nitride, magnesium oxide, chromium oxide, copper oxide, The particle size of kaolin, mica powder, sodium bentonite, cerium oxide, neodymium oxide, lanthanum oxide, yttrium oxide and niobium oxide is 100 nano...

Embodiment 3

[0017] A high-temperature-resistant, high-blackness, anti-coking, and corrosion-resistant ceramic coating is characterized in that the binder consists of 7% silica sol, 6% styrene-acrylic emulsion, 3% sodium oxide, 4% aluminum oxide monohydrate, The filler consists of 2% zirconia, 3% iron oxide red, 1% silicon nitride, 0.3% titanium nitride, 3% magnesium oxide, 6% chromium oxide, 0.75% copper oxide, 6% kaolin, 1.9% by mass percentage % mica powder, 0.6% sodium bentonite, 3% cerium oxide, 3% neodymium oxide, 3% lanthanum oxide, 3% yttrium oxide, 0.4% molybdenum oxide, 3% niobium oxide, the auxiliary agent is composed of 0.35% by mass percentage % dispersant, 0.25% wetting agent, 0.15% defoamer, 3% ammonia water, the filler, its zirconia, iron oxide red, silicon nitride, titanium nitride, magnesium oxide, chromium oxide, copper oxide, The particle size of kaolin, mica powder, sodium bentonite, cerium oxide, neodymium oxide, lanthanum oxide, yttrium oxide and niobium oxide is 100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a ceramic coating material with characteristics of high-temperature resistance, high blackness, coking resistance and corrosion resistance, wherein the ceramic coating materialcomprises a binder, a filler, an auxiliary agent and water, the binder comprises, by mass, 7-15% of silica sol, 5-7% of styrene-acrylic emulsion, 1-3% of sodium oxide, and 3-5% of alumina monohydrate, and the filler comprises, by mass, 2-5% of zirconia, 1-3% of iron oxide red, 1-3% of silicon nitride, 0.2-0.5% of titanium nitride, 1-3% of magnesium oxide, 3-6% of chromium oxide, 1% of alumina, 0.5-1% of copper oxide, 5-7% of kaolin, 1.9-2.5% of mica powder, 0.5-0.7% of sodium-based bentonite, 1-3% of cerium oxide, 1-3% of neodymium oxide, 1-3% of lanthanum oxide, 1-3% of yttrium oxide, 0.2-0.4% of molybdenum oxide, and 1-3% of niobium oxide.

Description

technical field [0001] The invention relates to the technical field of ceramic coatings, in particular to a high-temperature-resistant, high-blackness, anti-coking, and corrosion-resistant ceramic coating. Background technique [0002] Ceramic coatings belong to the field of functional coatings and are a new type of water-based inorganic coatings. It is mainly composed of nano-inorganic compounds and water as a dispersant. After coating, it is usually cured by low-temperature heating to form a coating film with properties similar to ceramics. Its raw materials are abundant, easy to mine and low in price, which makes its cost lower than traditional coatings. Some of them use silane coupling agent and aluminum hydroxide colloid to prepare ceramic coatings, which have many advantages such as high temperature resistance, high hardness, non-flammable and smoke-free, super weather resistance, environmental protection and non-toxic, rich colors, and easy coating. After various ne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/61C09D7/65C09D5/08
Inventor 刘俊刘尚鑫巩鹏
Owner 甘肃华鑫石化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap