Environmentally friendly thermal insulation flame retardant PBT waterproof seepage-proofing coiled material and production process thereof

A production process and coil technology, applied in the field of PBT coil and its production process, can solve the problems of easy fire, low tensile strength and elongation at break, poor flame retardancy, etc., to improve thermal insulation performance and mechanical properties The effect of high performance, impact strength and bending strength

Inactive Publication Date: 2018-11-06
NINGBO FEICHAI ROBOT TECH CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But for waterproofing membranes used in construction, we blindly pay attention to its "waterproofness", but often ignore its "fire resistance" and "heat insulation", which also caused safety incidents.
The fire at CCTV’s new site in 2009 was caused by the burning anti-aircraft gun fireworks falling on the flammable EPDM waterproofing membrane on the roof, which ignited the insulation material, which triggered the fire and caused an economic loss of 600-700 million
[0005] At present, the main problems in PBT coils are: (1) poor flame retardancy, easy to cause fire, and poor safety; (2) low tensile strength and elongation at break; (3) weak performance against external tearing ; (4) easy aging, short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmentally friendly thermal insulation flame retardant PBT waterproof seepage-proofing coiled material and production process thereof
  • Environmentally friendly thermal insulation flame retardant PBT waterproof seepage-proofing coiled material and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1 Preparation of environmental protection, heat insulation and flame retardant PBT waterproof and anti-seepage membrane

[0024] Raw material composition: PBT / Al 2 o 3 / 30 parts of glass fiber composite material, 20 parts of EVA resin, 5 parts of KH5505, 2 parts of flame retardant, 2 parts of acrylic resin film former, 1 part of dispersant, 2 parts of toughening agent, cetyl trimethyl chloride 0.005 part of ammonium and 0.005 part of fatty alcohol polyoxyethylene ether;

[0025] PBT / Al 2 o 3 / Preparation of glass fiber composites:

[0026] Will Al 2 o 3 , PBT and glass fiber are fully dried in a blast drying oven at 100°C, and the recycled PBT engineering plastics are added to the Huck Torque Rheometer, and PBT is banburyed at 300°C and 50r / min for 10 minutes until it is fully plasticized , and then add pre-mixed glass fiber, Al 2 o 3and KH550, continue to mix for 15min, the mixture is crushed, injection molded and compression molded to obtain PBT / Al ...

Embodiment 2

[0029] Example 2 Preparation of environmental protection, heat insulation and flame retardant PBT waterproof and anti-seepage membrane

[0030] Raw material composition: PBT / Al 2 o 3 / 50 parts of glass fiber composite material, 40 parts of EVA resin, 10 parts of DL17110 parts, 10 parts of nitrogen-based flame retardant, 5 parts of butadiene resin film former, 3 parts of monoglyceride stearate, 5 parts of styrene-butadiene rubber, ten parts 0.5 part of hexaalkyl pyridinium bromide and 0.5 part of fatty amine polyoxyethylene ether;

[0031] PBT / Al 2 o 3 / Preparation of glass fiber composites:

[0032] Will Al 2 o 3 , PBT and glass fiber are fully dried in a blast drying oven at 100°C, and the recycled PBT rubber head is added to the Huck torque rheometer, and the PBT is internally kneaded at 350°C and 100r / min for 20 minutes until it is fully plasticized , and then add pre-mixed glass fiber, Al 2 o 3 and isopropyl triisostearyl titanate, continue mixing for 30min, and ...

Embodiment 3

[0035] Example 3 Preparation of environmental protection, heat insulation and flame retardant PBT waterproof and anti-seepage membrane

[0036] Raw material composition: PBT / Al 2 o 3 / 42 parts of glass fiber composite material, 30 parts of EVA resin, 7 parts of KH5607, 5 parts of phosphorus flame retardant, 3 parts of nitrocellulose film former, 1.5 parts of glyceryl tristearate, styrene-butadiene thermoplastic elastomer 3 parts and 0.1 part of polyethylene glycol distearate and 0.1 part of cetyltrimethylammonium chloride;

[0037] PBT / Al 2 o 3 / Preparation of glass fiber composites:

[0038] Will Al 2 o 3 , PBT and glass fiber are fully dried in a blast drying oven at 100°C, and the PBT film fiber reclaimed material is added to the Haake torque rheometer, and PBT is banburyed at 330°C and 70r / min for 17 minutes until it is fully plasticized , and then add pre-mixed glass fiber, Al 2 o 3 and distearoyloxyisopropyl aluminate, continue to mix for 20min, and the mixtur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environmentally friendly thermal insulation flame retardant PBT (Poly Butylenes Terephthalate) waterproof seepage-proofing coiled material, the environmentally friendly thermal insulation flame retardant PBT waterproof seepage-proofing coiled material comprises a PBT / Al2O3 / glass fiber composite, an EVA resin, a coupling agent, a flame retardant, a film forming agent, a dispersing agent, a flexibilizer and a surfactant, the coupling is a silane coupling agent, the flame retardant is one or more of an aluminum magnesium based flame retardant, a phosphorus based flame retardant, a nitrogen based flame retardant, and an organosilicone flame retardant, the flexibilizer is one or more of an ethylene propylene rubber, a butyl rubber, a nitrile rubber and a butadiene styrene rubber, the film forming agent is one or more of an acrylic resin film forming agent and a nitrocellulose film forming agent, the dispersing agent is one or more of hexane based distearic amide and glycerol monostearate, and the surfactant is a compound surfactant comprising a nonionic surfactant and a cationic surfactant. The prepared environmentally friendly thermal insulation flame retardant PBT waterproof seepage-proofing coiled material is excellent in heat-insulating property and mechanical property, a PBT reclaimed material is reasonably recycled, and the purposes of saving energies and reducing consumption are fulfilled.

Description

technical field [0001] The invention relates to a plastic film manufacturing technology, in particular to a PBT coil and a production process thereof. Background technique [0002] Safety and waterproofing have always been two important issues in building waterproofing. The development and application scale of waterproofing materials can represent a country and region's emphasis on building safety in some respects. With the vigorous development of my country's construction industry, the use of waterproof membranes for construction has increased significantly year by year. But for waterproofing membranes used in construction, we blindly pay attention to its "waterproofness", but often ignore its "fire resistance" and "heat insulation", which also caused safety incidents. The fire at CCTV’s new site in 2009 was caused by the burning anti-aircraft gun fireworks falling on the flammable EPDM waterproof membrane on the roof, which ignited the insulation material, which triggered...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L23/08C08K13/04C08K7/14C08K3/22C08J5/18
CPCC08J5/18C08J2367/02C08J2423/08C08K7/14C08K13/04C08K2003/2227
Inventor 李梅
Owner NINGBO FEICHAI ROBOT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap