A method for recovering zinc from smelting waste slag

A technology of waste slag and coordination, applied in the field of metallurgy, can solve the problems of increasing the steps of zinc recovery and affecting the application, so as to reduce the consumption of ammonia water and avoid the effect of dissolution

Active Publication Date: 2022-04-19
LIUPANSHUI NORMAL UNIV
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the alkaline leaching method in the prior art to prepare zinc leaching solution, while leaching zinc ions, is also accompanied by the leaching of other metal impurity ions in the smelting waste residue, such as copper, lead, iron, manganese and other ions. Therefore, for ammonia The zinc leaching solution obtained by the method leaching often requires further purification and impurity removal operations to remove the impurity ions in order to obtain high-purity zinc products. This virtually increases the steps of zinc recovery from smelting waste residues, and affects the industry. application in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Mix smelting waste residue and calcium hypochlorite, the amount of calcium hypochlorite added is 10% of the mass of smelting waste residue, place in a microwave reactor, heat up to 300°C at a heating rate of 20°C / min, and roast for 20min after taking out;

[0028] (2) Get citric acid and tartaric acid according to molar ratio 1: 1 and mix uniformly to obtain compound mixture, add water until the concentration of citric acid is 1mol / L, add ammoniacal liquor and ammonium sulfate that molar ratio is 1: 1, make the total ammoniacal concentration in the solution 5mol / L, adjust the pH value to 8 to obtain a coordination leaching agent;

[0029] (3) Mix the roasted product of step (1) and the coordination leaching agent of step (2) uniformly at a solid-to-liquid ratio of 10 g / ml, and leaching at room temperature (25° C.) under 1000 W ultrasonic power for 20 minutes to obtain a leaching solution;

[0030] (4) Zinc powder is added to the obtained leaching solution according...

Embodiment 2

[0033] Same as Example 1, the difference is that the amount of calcium hypochlorite added is 20% of the quality of smelting waste residue.

Embodiment 3

[0035] Same as Example 1, the difference is that the added amount of calcium hypochlorite is 3% of the quality of smelting waste residue.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for recovering zinc from smelting waste slag. The smelting waste slag and calcium hypochlorite are evenly mixed, and roasted at high temperature to obtain calcined sand; a complexing agent in citric acid or citrate is mixed with tartaric acid or tartaric acid A complexing agent in the salt is mixed evenly to obtain a complex mixture, add water, stir evenly, add ammonia solution and ammonium sulfate, and mix uniformly to form a coordination leaching agent; put the obtained calcined sand in the coordination leaching agent for ultrasonic reaction to obtain Zinc leaching solution; the obtained leaching solution is added with zinc powder to react for a period of time and then filtered, and the obtained filtrate is calcined at high temperature to obtain zinc oxide. The present invention prevents the leaching of impurity ions in the smelting waste slag while ensuring the leaching rate of zinc, so that the obtained zinc leaching solution can be calcined at high temperature to directly obtain high-purity zinc oxide products, which facilitates the recovery of zinc in the smelting waste slag. application.

Description

technical field [0001] The invention relates to the technical field of metallurgy, in particular to a method for recovering zinc from smelting waste residue. Background technique [0002] In addition to zinc mineral resources, zinc-containing slag dust and other metallurgical slag dust are also extremely important available resources in my country, mainly zinc-containing gas mud and gas ash produced in the blast furnace smelting process, zinc-containing smoke dust produced in the electric arc furnace smelting process, and lead smelting. Zinc-containing dust and zinc hydrometallurgy slag after slag volatilization; hydromethod zinc smelting has accounted for more than 80% of the total zinc smelting in the world, and this process produces a large amount of zinc-containing leaching slag. up to 14%), calcium (up to 19%), chlorine (up to 12%), fluorine (up to 2%) and other impurities, zinc is mainly zinc oxide, zinc iron spinel and silicon The iron element mainly exists in the form ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B19/30C22B19/20C22B19/34
CPCC22B19/30C22B19/24C22B19/26C22B19/34Y02P10/20
Inventor 马爱元郑雪梅袁杰朱山李松
Owner LIUPANSHUI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com