Lignin/tannin composite polyurethane coating and preparation method thereof

A technology of compounding polyurethane and lignin, which is applied in the direction of coating, paper coating, non-fiber pulp addition, etc., can solve the problems of difficult to support complex and changeable application environments, moisture resistance, antibacterial, poor weather resistance, single function, etc., and achieve rich functions , Improve anti-corrosion performance and high-efficiency response effect

Active Publication Date: 2020-11-17
SOUTH CHINA UNIV OF TECH
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, today's coating materials are mostly derived from petroleum-based products, which are difficult to degrade, and will cause environmental pollution and additional carbon emissions during use (JurkkaKusipalo, Zhang Meiyun. Paper and cardboard processing. China Light Industry Press. 2017)
In recent years, people have begun to seek to use biomass raw materials to prepare new coating materials to alleviate the negative impact of petroleum-based materials. Although commonly used biomass macromolecules such as starch, gelatin, cellulose, and protein are easy to process, their functions Single, and poor moisture resistance, antibacterial, and weather resistance, it is difficult to support complex and changeable application environments (Ma Jing, Chen Liwei, Wang Heng, etc. Preparation and performance of water-resistant surface sizing agent for soybean protein isolate paper. Fine Chemical Industry, 2019, 36: 169-175.)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lignin/tannin composite polyurethane coating and preparation method thereof
  • Lignin/tannin composite polyurethane coating and preparation method thereof
  • Lignin/tannin composite polyurethane coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A lignin / tannin composite polyurethane coating and a preparation method thereof, comprising the following steps (refer to figure 1 shown):

[0034] Step 1: under nitrogen protection, be 1: 3 according to the mol ratio of total hydroxyl groups of lignin and hexamethylene diisocyanate, get 10g acetic acid lignin, the hexamethylene diisocyanate of corresponding quality, be dissolved in dimethyl methylene diisocyanate In the sulfone, a dibutyltin dilaurate catalyst with a mass of 0.02% lignin was added to make the total concentration (mass fraction) of lignin and hexamethylene diisocyanate in dimethyl sulfoxide to be 30%, and the temperature was kept at 30 °C for 0.5 h, System 1 is obtained.

[0035]Step 2: Under the protection of nitrogen, according to the molar ratio of the total hydroxyl groups of tannins and hexamethylene diisocyanate is 1:0.8, take 10g of tannins and hexamethylene diisocyanate of the corresponding quality, and dissolve them in dimethyl sulfoxide. Add...

Embodiment 2

[0041] A lignin / tannin composite polyurethane coating and a preparation method thereof, comprising the following steps (refer to figure 1 shown):

[0042] Step 1: under nitrogen protection, be 1: 1 according to the mol ratio of total hydroxyl groups of lignin and toluene diisocyanate, get 10g acetic acid lignin, the toluene diisocyanate of corresponding quality, be dissolved in dimethyl sulfoxide, add lignin The total concentration (mass fraction) of lignin and toluene diisocyanate in dimethyl sulfoxide was 10% with 0.08% mass dibutyltin dilaurate catalyst, and the system was kept at 70°C for 2h to obtain system 1.

[0043] Step 2: under nitrogen protection, according to the mol ratio of tannin total hydroxyl group and toluene diisocyanate is 1: 2.5, get 10g tannin, toluene diisocyanate of corresponding quality, dissolve in dimethyl sulfoxide, add tannin quality 0.02% dibutyltin dilaurate catalyst was used to make the total concentration (mass fraction) of tannin and toluene ...

Embodiment 3

[0049] A lignin / tannin composite polyurethane coating and a preparation method thereof, comprising the following steps (refer to figure 1 shown):

[0050] Step 1: under nitrogen protection, be 1: 2 according to the mol ratio of lignin total hydroxyl and diphenylmethane diisocyanate, get 10g acetic acid lignin, the diphenylmethane diisocyanate of corresponding quality, be dissolved in dimethyl methylene In the sulfone, a dibutyltin dilaurate catalyst with 0.05% lignin mass was added, so that the total concentration (mass fraction) of lignin and diphenylmethane diisocyanate in dimethyl sulfoxide was 30%, and the temperature was kept at 50 °C for 1.5 h, System 1 is obtained.

[0051] Step 2: Under nitrogen protection, according to the molar ratio of total tannin hydroxyl groups and diphenylmethane diisocyanate as 1:1.5, take 10g of tannin and diphenylmethane diisocyanate of the corresponding mass, and dissolve them in dimethyl sulfoxide. Add 0.02% tannin mass dibutyltin dilaura...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lignin / tannin composite polyurethane coating and a preparation method thereof. The method comprises the following steps: constructing an isocyanate prepolymer of lignin and tannin; mixing the lignin prepolymer and the tannin prepolymer, and adding polyether or polyester polyol to prepare a lignin / tannin polyurethane intermediate; adding Ag / Zn antibacterial ions with complete mixing; finally, applying the liquid coating to the substrate and performing crosslinking curing. The coating has relatively high crosslinking density, so that the coating has water resistance andoil resistance; the lignin and tannin are rich in benzene rings, so that the coating has the characteristic of ultraviolet aging resistance; the tannin catechol structure can enhance the adhesivenessof the coating to the base material; the Ag / Zn ions can be anchored at residual hydroxyl sites of tannin, so that the coating has antibacterial performance. The composite coating disclosed by the invention can be used for a paper-based material, endows the paper-based material with water resistance, oil resistance, bacteria resistance and aging resistance, and promotes the improvement of the mechanical strength of the paper-based material; the composite coating can also be used for surface treatment of medical materials or personal care products, and the antibacterial ability is improved.

Description

technical field [0001] The invention belongs to the field of polymer composite materials, in particular to a lignin / tannin composite polyurethane coating and a preparation method thereof. Background technique [0002] Coating materials are widely used in all walks of life and are indispensable and important materials in the process of social production and development. However, most of today's coating materials are derived from petroleum-based products, which are difficult to degrade and cause environmental pollution and additional carbon emissions during use (JurkkaKuusipalo, Zhang Meiyun. Paper and Cardboard Processing. China Light Industry Press. 2017). In recent years, people have begun to seek to use biomass raw materials to prepare new coating materials to alleviate the negative effects of petroleum-based materials, while commonly used biomass macromolecules such as starch, gelatin, cellulose, protein, etc. are easy to process, but functional Single, and poor moisture...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/24D21H17/57C08G18/64
CPCD21H19/24D21H17/57C08G18/6492
Inventor 张晖谢慧慧付时雨
Owner SOUTH CHINA UNIV OF TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com