Biomass formaldehyde-free adhesive as well as preparation method and application method thereof

A technology of aldehyde adhesive and biomass, which is applied in the field of biomass aldehyde-free adhesive and its preparation and application, can solve the problems of easy mold, high cost, and easy moth, and achieve easy sizing and low production cost , good initial viscosity effect

Active Publication Date: 2021-02-05
NANNING KETIAN SHUIXING TECH LTD CO +2
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to overcome the disadvantages of the prior art that the biomass adhesive is easy to be moth-eaten, easy to mold, and high cost, and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biomass formaldehyde-free adhesive as well as preparation method and application method thereof
  • Biomass formaldehyde-free adhesive as well as preparation method and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Example 1

[0031] The preparation and application method of a kind of biomass formaldehyde-free adhesive of the present invention specifically comprises the following steps:

[0032] (1) Firstly, dry the pre-prepared papaya leaves at an ambient temperature of 25-35°C for 1-2 weeks, then place them in a high-temperature oven for 8 hours at 100-110°C, and control their moisture content at 5 % or less, then use a four-cutter high-speed pulverizer to pulverize it at a rate of 10000-15000 rpm for 10min, and filter it with a 200-mesh filter screen to obtain a coarse plant fiber powder, and use a ball mill for 25-30min to filter the coarse particle residue 1 Finally, it is taken out as plant fiber residue filling powder for later use. Mix and stir the 5 mass parts of plant fiber coarse material powder obtained above and the fiber solvent activation system according to the mass ratio of solid to liquid 0.5:5, wherein the fiber solvent activation system consists of 48 mass par...

Example Embodiment

[0039] Example 2

[0040] The preparation and application method of a kind of biomass formaldehyde-free adhesive of the present invention specifically comprises the following steps:

[0041] (1) First, dry the pre-prepared bamboo leaves at an ambient temperature of 25-35°C for 1-2 weeks, then place them in a high-temperature oven at 100-120°C for 10 hours, and control their moisture content at 5 % or less, then use a four-blade high-speed pulverizer to pulverize it at a rate of 15000-20000 rpm for 10min, and filter it with a 200-mesh filter screen to obtain the plant fiber coarse material powder, and use a ball mill for 25-30min for the coarse particle residue after filtering Finally, it is taken out as plant fiber residue filling powder for later use. Mix and stir the 5 mass parts of plant fiber coarse material powder obtained above and the fiber solvent activation system according to the mass ratio of 2:35, wherein the fiber solvent activation system consists of 135 mass pa...

Example Embodiment

[0048] Example 3

[0049] The preparation and application method of a kind of biomass formaldehyde-free adhesive of the present invention specifically comprises the following steps:

[0050] (1) First, dry the pre-prepared ramie at an ambient temperature of 25-35°C for 1-2 weeks, then place it in a high-temperature oven at 100-110°C for 8 hours, and control its moisture content at 5% Next, use a four-cutter high-speed pulverizer to pulverize it at a rate of 15000-18000 rpm for 10 minutes, and filter it with a 200-mesh filter screen to obtain a coarse plant fiber powder. Take it out and use it as plant fiber residue to fill the powder for later use. Mix and stir the 5 mass parts of plant fiber coarse material powder obtained above and the fiber solvent activation system according to the mass ratio of solid-liquid 5:100, wherein the fiber solvent activation system consists of 75 parts by mass of nitrogen methyl morpholine oxide and 5 parts by mass of dimethyl sulfoxide, 15 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of formaldehyde-free adhesive processing, in particular to a biomass formaldehyde-free adhesive based on a cellulose extracting solution as well as a preparation method and an application method thereof. Plant fibers with a natural antibacterial effect are used as main materials, a cellulose aqueous solution is prepared through physical crushing, pretreatment activation, dissolution and acetylation treatment, and compounding is performed through plant protein powder, a cross-linking agent, a curing agent and a tackifying aid. A biomass cellulose adhesive with good initial viscosity, easy gluing, water resistance and excellent natural antibacterial property of the prepared plate can be obtained, the mildewing condition of a glued layer of the glued plate is greatly improved, and the biomass formaldehyde-free adhesive prepared from the cellulose extracting solution has the advantages of wide raw material source, low preparation cost, environment friendliness, and no pollution, natural resources can be fully utilized, the dependence of the wood adhesive on petroleum resources is reduced, high-valued utilization of plant fibers with a natural antibacterial effect can be realized, and the adhesive has important significance for environmental protection.

Description

technical field [0001] The invention relates to a preparation method of a biomass-free formaldehyde adhesive, and more specifically relates to a biomass-formaldehyde-free adhesive and a preparation and application method thereof. Background technique [0002] With the enhancement of people's awareness of environmental protection and the improvement of environmental protection laws and regulations in various countries around the world, adhesives prepared from petroleum by-product polymer materials are increasingly subject to more policy restrictions, and traditional three-aldehyde adhesives are also being released due to the problem of formaldehyde. gradually eliminated by the market. In recent years, environmentally friendly formaldehyde-free adhesives made of biological materials are being favored by researchers and the market because of their advantages of no formaldehyde, non-toxicity, and low cost. As long as the biomass adhesives currently on the market are composed of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J189/00C09J101/12C09J103/02C09J177/00C09J11/08B27D1/04B27D1/08B27N1/02B27N3/10
CPCC09J189/00C09J11/08B27D1/08B27D1/04B27N3/10B27N1/02B27N1/0209C08L2205/035C08L2205/025C08L89/00C08L1/12C08L3/02C08L77/00C08L99/00C08L97/02
Inventor 闫成成朱保凌戴家兵李维虎赵曦
Owner NANNING KETIAN SHUIXING TECH LTD CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap