Long-acting sustained-release medicaments for treating and renovating osteomyelitis and preparation thereof

A carrier material and sustained-release drug technology, applied in the field of biomedical material drug carrier, long-acting sustained-release drug carrier material, and can solve the problems of inability to perform bone repair, long-acting sustained-release treatment, and short drug release time. , to achieve the effect of inhibiting the growth of osteoclasts, long drug release time, and promoting the growth of osteoblasts

Inactive Publication Date: 2009-10-14
SICHUAN UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the treatment of osteomyelitis focuses on the research of drug carrier materials on the one hand. The polymer drug carrier materials can control the time and rate of drug release, but cannot perform bone repair; on the other hand, inorganic bioceramics are also used as drug carrier materials, such as hydroxyphosphorus Limestone contains vancomycin for the treatment of osteomyelitis, but the release time of the drug is short, which cannot achieve the effect of long-acting sustained-release therapy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0024] Preparation of drug-loaded microspheres: adding chitosan to acetic acid aqueous solution to prepare a chitosan-acetic acid solution with a chitosan concentration of 2.0 wt%, adding tetracycline according to the chitosan and tetracycline mass ratio of 1: 1, completely dissolved as In the water phase of the W / O system, after the system is completely dispersed, add the crosslinking agent glutaraldehyde according to the volume ratio of the crosslinking agent and chitosan acetic acid solution at 1:10, the volume concentration of glutaraldehyde is 25%, and stir for about 3 hours. After fully reacting to form the chitosan drug-loaded microsphere core, after centrifugation, cleaning and drying, the particle size is measured with a laser particle size analyzer. Self-assembly of drug-loaded microsphere core coating layer: Prepare 1wt% sodium alginate aqueous solution and chitosan aqueous solution respectively, control the temperature at about 60°C, and 0.3M ion concentration, and di...

example 2

[0027] Preparation of drug-loaded microspheres: adding chitosan to aqueous acetic acid solution to prepare a chitosan-acetic acid solution with a chitosan concentration of 2.0 wt%, adding vancomycin according to the mass ratio of chitosan and vancomycin at 2:1 , as the water phase of the W / O system after completely dissolving, after the system is completely dispersed, add the crosslinking agent glutaraldehyde according to the volume ratio of the crosslinking agent and chitosan acetic acid solution at 1:10, the glutaraldehyde volume concentration is 25%, After fully reacting to form the chitosan drug-loaded microsphere core, after centrifugation, cleaning and drying, the particle size is measured with a laser particle size analyzer. Self-assembly of drug-loaded microsphere core coating layer: prepare 1wt% sodium alginate aqueous solution and chitosan aqueous solution respectively, control the temperature at about 60°C, and ionic concentration of about 0.3M, and disperse the prep...

example 3

[0030] Preparation of drug-loaded microspheres: adding chitosan to acetic acid aqueous solution to prepare a chitosan-acetic acid solution with a chitosan concentration of 2.0 wt%, adding gentamicin according to the mass ratio of chitosan and gentamicin at 1:1 As the water phase of the W / O system after complete dissolution, after the system is completely dispersed, add the cross-linking agent β-sodium glycerophosphate according to the volume ratio of the cross-linking agent and chitosan acetic acid solution 1:5, the mass of β-sodium glycerophosphate The concentration is 11%, stirred for about 3 hours, fully reacted to form the chitosan drug-loaded microsphere core, centrifuged, washed and dried, and measured with a laser particle size analyzer. Self-assembly of drug-loaded microsphere core coating layer: prepare 0.5wt% sodium alginate aqueous solution and chitosan aqueous solution respectively, control the temperature at about 40°C, and ionic concentration of about 0.5M, and di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a long-acting slow-release drug carrier material for osteomyelitis treatment and repair and a preparation method thereof. The drug carrier material mainly includes 4-8 parts by weight of strontium-doped calcium polyphosphate, 1-3 parts by weight of Chitosan drug-loaded microspheres and 1-3 parts by weight of chitosan. The preparation method is mainly as follows: preparing chitosan acetic acid solution, adding strontium-doped calcium polyphosphate powder into the chitosan acetic acid solution to make it evenly dispersed, then adding the prepared chitosan drug-loaded microspheres, and finally adding The cross-linking agent makes it cross-linked, and after being frozen at 2-6°C for 12-48 hours, it is heated and dried at 40-100°C to obtain a composite drug carrier material for treating bone diseases such as osteomyelitis. The long-acting slow-release drug carrier material used in the treatment and repair of osteomyelitis and other bone diseases provided by the present invention has bone repair function while releasing antibiotics for a long time, and has good biocompatibility and degradability. It has an ideal dual function of treatment and repair.

Description

a technical field [0001] The invention relates to the technical field of biomedical material drug carriers, in particular to the technical field of long-acting slow-release drug carrier materials used for the treatment of osteomyelitis and other bone diseases and the repair of bone defects. Two background technology [0002] Traditional treatment of osteomyelitis usually includes surgical removal of infected tissue, washing with antiseptic solution, and 4 to 6 weeks of gastrointestinal antibiotic treatment. In order for the drug in the bone tissue to effectively kill bacteria, it is necessary to make the drug concentration in the bone tissue reach a bactericidal level, which requires prolonging the administration time and using antibiotics with high blood concentration. Due to the high incidence of disease associated with high blood levels of antibiotics, a number of topical drug delivery systems have been extensively studied and used. Carriers for topical administration of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K47/36A61K47/02A61K9/16A61K45/08A61P19/08A61L27/20A61L27/12A61L27/54
Inventor 万昌秀史国齐余喜讯张小华李华王践云丁玉龙
Owner SICHUAN UNIV