Rotary electric furnace and method thereof for preparing high-activity electro-plated copper oxide

Abstract

The invention discloses a rotary electric furnace and a method for preparing high-activity electro-plated copper oxide by using the rotary electric furnace. At least one percussion device is arranged on the outer wall of the furnace barrel of the rotary electric furnace, wherein the furnace barrel percussion device comprises a hollow cavity and a sphere; one end of the hollow cavity is open and the other end of the hollow cavity is closed, wherein the opening end is fixed on the outer wall of the furnace barrel; the sphere is movably arranged in the hollow cavity; the sphere moves up and down in the hollow cavity to form a clearance percussion status with the outer wall of the furnace barrel during the rotary process of the furnace barrel; the method for preparing the high-activity electro-plated copper oxide comprises the following steps of: preparing high-purity alkali type copper carbonate by adopting pure copper, liquid ammonia and high-purity carbon dioxide as materials; and obtaining the high-activity electro-plated copper oxide through roasting in the rotary electric furnace. According to the rotary electric furnace and the method for preparing the high-activity electro-plated copper oxide by using the rotary electric furnace, the defect that the low-temperature part is insufficient due to insufficient burning and the high-temperature part is burnt through during a static roasting process of the pushed slab kiln is overcome; moreover, the defects such as inactivity, a plurality of impurities, discontinuous production, long period, high energy consumption, high cost and the like are overcome, so that the activity of the product is ensured. Besides, the product quality is high, the energy consumption is less, the cost is low and the environment-friendliness is better.

Description

technical field [0001] The invention belongs to the field of copper oxide production, in particular to a rotary electric furnace and a method for preparing high-activity electroplating grade copper oxide. Background technique [0002] In the PCB manufacturing process, the traditional electroplating process uses a copper plate as the anode plate and supplements the copper source. Due to the complex shape of the electronic components, there are holes, concave-convex surfaces and other shapes. In the holes, the electroplating solution cannot penetrate, so the plating Less than copper, the protruding part has a high current density and a thick coating, while the concave part has a low current density and a thin coating, resulting in unqualified products. [0003] At present, the horizontal electroplating process is common in the PCB manufacturing industry in the market. This process overcomes the shortcomings of the traditional process, but this process must add high-purity, low...

AI Technical Summary

Problems solved by technology

Regarding the production process of copper oxide, it is also involved in some invention patents disclosed at present. The application number is 01127175.2, which uses copper sulfate and copper material as raw materials, undergoes low-temperature oxidation at 80-85°C, obtains copper sulfate through crystallization, and then mixes it with Sodium hydroxide reaction, and then through ball milling, pressure filtration, washing, drying, and pulverization to obtain active copper oxide. Waste water; Application number is the technique that 200710076208.1 discloses to produce copper oxide through distilling ammonia with alkaline etching waste liquid, owing to be to make by distilling ammonia for a long time under high temperature, strong alkali state with alkaline etching waste liquid, so copper oxide activity is relatively Low; the application number is 200710071896.2, which discloses the reaction of copper nitrate and sodium hydroxide through pressure filtration, drying, and roasting to produce copper oxide, which will produce nitrogen dioxide or nitrogen monoxide waste gas, which will cause certain pollution to the environment; application number is 200810067243.1 The production process of synthesizing basic copper chloride as a precursor, and then reacting with sodium hydroxide to produce monoclinic copper oxide, but its activity has not been verified experimentally

At present, copper oxide for horizontal electroplating is also prepared from basic copper carbonate as raw material, but first, basic copper carbonate is mostly obtained by traditional technology, and the content of impurities such as iron and lead is high. Second, most manufacturers use pusher kiln calcining equipment for calcination. Basic copper carbonate prepares electroplating-grade copper oxide. This method has the following problems: (1) Due to the uneven temperature distribution in the kiln, the physical properties of the reaction material are not uniform enough, and the low-temperature part of the basic copper carbonate has not enough fire-through content, while the high-temperature part is oxidized. The copper has been burnt to death and loses its activity; (2) The slag from the charging sagger brings impurities such as silicon, aluminum, calcium and other contaminated products into the material, making the chemical composition of the electroplating grade copper oxide unable to meet the target requirements; (3) Because the material is fixed Bed, uneven temperature distribution, long production time and high energy consumption; (4) manual operation, labor-intensive, can not be automated

Images