Sintering expansion type light ceramsite produced by using oily sludge and manufacture method of sintering expansion type light ceramsite

A technology of sintering expansion and light weight ceramsite, which is applied in the manufacture of sintering expansion type light weight ceramsite, expansion type light weight ceramsite, sintering expansion type light weight ceramsite, and can solve the problem of large volume and viscosity of oily sludge It is difficult to settle and occupy arable land, etc., to achieve good thermal insulation effect, low water absorption rate, and increase the yield of finished products.

Active Publication Date: 2013-08-14
清远绿由环保科技有限公司 +1
View PDF3 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Suspended solids and colloidal particles in the sludge form a very stable emulsification system with oil and water. The viscosity is high and it is difficult to settle. The oily sludge is huge...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] The oily sludge is the industrial wastewater of refinery, electroplating wastewater and other oily wastewater produced by petroleum mechanical processing, and the activated sludge produced after flotation, filtration, flocculation and chemical treatment, as well as the bottom sludge of crude oil grease trap, floating The combined waste of pool scum and oily sludge of crude oil tank bottom sludge is mechanically dehydrated, dried, milled, and sieved to make oily sludge powder with a particle size of less than 0.25 mm for later use;

[0065]The construction waste and soil, which is the waste slag discharged in the process of urban construction and the waste slag produced in the foundation digging and underground parking lot construction of housing construction projects, are sorted, crushed, crushed, sorted, magnetically separated, dried, and ground. powder, sieved and made into construction waste slag powder whose particle size is less than 0.25mm for subsequent use;

[0...

Embodiment 2

[0071] Get the oily sludge 58kg of embodiment 1, calcium oxide 14kg, ferrous sulfate 6kg and magnesium sulfate 12kg mix uniformly and carry out disinfection, sterilization, deodorization, dry, pulverize, sieve and make its particle diameter be less than 0.25mm after mixing Powder, then take construction waste slag powder 30kg, waste energy-saving lamp waste slag powder 20kg, boiler waste slag powder 18kg, wood processing waste slag powder 18kg, calcium sulfate 6kg, carboxymethyl cellulose 0.05kg, calcium carbonate 8kg, vulcanization 3kg of iron, 0.01kg of polycarboxylate superplasticizer and 20kg of water are mixed evenly with a double-shaft mixing mixer, and the spherical particles of 20mm are made by a disc pelletizer. After drying, they are roasted in a double-cylinder rotary kiln. The temperature should be controlled at 1180°C, and the time should be controlled at 25 minutes. After cooling out of the kiln, sieve to make oily sludge sintered and expanded lightweight ceramsit...

Embodiment 3

[0073] Get the oily sludge 46kg of embodiment 1, calcium oxide 8kg, ferrous sulfate 3kg and magnesium sulfate 8kg mix uniformly and carry out disinfection, sterilization, deodorization, dry, pulverize, sieve and make its particle diameter be less than 0.25mm after mixing Powder, then take 23kg of construction waste slag powder, 14kg of waste energy saving lamp waste slag powder, 12kg of boiler waste slag powder, 10kg of wood processing waste slag powder, 4kg of calcium sulfate, 0.03kg of carboxymethyl cellulose, 4kg of calcium carbonate, vulcanization The raw materials of iron 1.5kg, polycarboxylate superplasticizer 0.008kg and water 13kg are mixed evenly with a double-shaft mixing mixer and made into 10mm spherical particles by a disc pelletizer. After drying, they are roasted in a double-cylinder rotary kiln. , the temperature should be controlled at 1150°C, and the time should be controlled at 20 minutes. After cooling out of the kiln, sieve to make oily sludge sintered and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a sintering expansion type light ceramsite produced by using oily sludge and a manufacture method of the sintering expansion type light ceramsite. The manufacture method is characterized by comprising the following steps of: uniformly mixing raw materials including oily sludge, building waste residue, waste energy-saving lamp residue, boiler waste residue, wood material processing waste residue, calcium oxide, calcium sulfate, carboxymethylcellulose, calcium carbonate, ferric sulfide, a polycarboxylate superplasticizer, ferrous sulfate, magnesium sulfate and water by using a dual-shaft mixing and stirring machine, manufacturing into spherical particles with diameters of 5-20mm by using a disc pelletizing machine, drying, roasting by using a dual-cylinder rotary kiln, controlling the temperature to be 1,050-1,200 DEG C and the time to be 10-25 minutes, cooling and discharging from the kiln, then screening and manufacturing to be a sintering expansion type light ceramsite product. The sintering expansion type light ceramsite product has the advantages and effects of being light in weight, preserving and insulating heat, absorbing and insulating sound, comprehensively utilizing and recycling solid waste resources, and being free of pollution, low in cost and good in benefit, and accords with the requirements of saving energy, reducing emission, protecting environment and developing low-carbon economy in China.

Description

[0001] technical field [0002] The present invention relates to a kind of sintered expansion type lightweight ceramsite produced from oily sludge. Specifically, it is made of oily sludge, construction waste residue, waste energy-saving lamp waste, boiler waste residue, and wood processing waste residue, which are crushed and sorted. , crushed, and then dried, milled, and sorted powder is an expanded lightweight ceramsite produced as the main raw material, which belongs to the field of waste treatment. [0003] The invention also relates to a manufacturing method of the sintered expansion type lightweight ceramsite. Background technique [0004] Ceramsite is a lightweight particle of ceramic. Its appearance is a round or elliptical sphere, but there are also some gravel-like ceramsites in the shape of irregular gravel. The shape of ceramsite varies with different processes. Its surface is a hard shell, which is pottery or glaze, which has the function of water-proof and ai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B18/30
CPCY02A30/244Y02W30/91
Inventor 李桓宇古耀坤
Owner 清远绿由环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka