Unfired hollow brick and preparation method thereof

The technology of hollow brick and fly ash is applied in the field of non-burning hollow brick and its preparation, which can solve the problems of waste, environmental pollution and high cost, and achieve the effects of energy saving, high strength and good frost resistance.

Inactive Publication Date: 2014-12-24
WUHE DINGSHUN NEW BUILDING MATERIAL
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the development of the construction industry, the demand for hollow bricks is increasing. The waste of manufacturing traditional hollow bricks will waste a lot of resources such as clay, which is costly and pollutes the environment when firing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A non-burning hollow brick made of the following raw materials in weight (kg): phosphogypsum 46, fly ash 27, quicklime 3, sludge from sewage treatment plants 46, tile slag 6, Portland cement clinker 14, Calcite powder 7, antimony slag 5, self-made concrete 9, glycerol 2.5, cetyltrimethylammonium bromide 0.2, sodium acetate 2, sodium thiosulfate 3, fatty alcohol polyoxyethylene ether sodium sulfate 2, even Azodicarbamide 0.3, carboxymethyl cellulose 0.4, appropriate amount of water,

[0015] Among them, the self-made concrete is prepared by the following methods: (1) Weigh construction waste 45, aluminum sulfate slag 13, volcanic ash 14, zeolite powder 2.5, fly ash 3.5, crop straw powder 11, sawdust 11 by weight (kg) , waste aluminum powder 1.5, tungsten powder 5, magnesium oxide 3, rosin saponified ester 2, acetic acid 14, urea 7, glycidyl methacrylate 1, methacrylate 2, ethylenediamine 4, linseed oil 0.3; (2 ), breaking the construction waste taken by weighing, then p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an unfired hollow brick which is prepared from the following raw materials in parts by weight: 40-50 parts of phosphogypsum, 20-30 parts of fly ash, 1-5 parts of quicklime, 40-50 parts of sludge generated by sewage treatment plants, 5-8 parts of tile residue, 12-15 parts of Portland cement clinker, 5-8 parts of calcite powder, 4-6 parts of antimonial dross, 8-10 parts of self-made concrete, 2-3 parts of glycerol, 0.1-0.2 part of cetyl trimethylammonium bromide, 1-2 parts of sodium acetate, 2-5 parts of sodium thiosulfate, 1-2 parts of fatty alcohol polyethenoxy ether sodium sulfate, 0.2-0.4 part of amine azodicarbonate, 0.3-0.5 part of carboxymethyl cellulose and a proper amount of water. The hollow brick has the characteristics of high strength, favorable freezing resistance and the like, can insulate heat and sound and resist moisture, can recycle industrial tailings, does not need sintering, saves the energy, utilizes the residues and wastes, can substitute for the solid clay brick with the defects of high energy consumption, field destroying and severe pollution, and can be used in various construction projects.

Description

technical field [0001] The invention relates to the field of new building materials, in particular to an unfired hollow brick and a preparation method thereof. Background technique [0002] Traditional hollow bricks are made of clay, shale, etc. as the main raw materials, after raw material processing, molding, and sintering. They are light in weight, high in strength, and have good thermal insulation and noise reduction performance. [0003] With the development of the construction industry, the demand for hollow bricks is increasing day by day. The waste of manufacturing traditional hollow bricks will waste a lot of resources such as clay, which is costly and pollutes the environment during firing. Researching new raw materials and new techniques of hollow bricks has become the development direction of hollow brick manufacturers. Contents of the invention [0004] The object of the present invention is to provide a non-fired hollow brick and its preparation method. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14
Inventor 杨喆宇
Owner WUHE DINGSHUN NEW BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap