Fireproof emulsion paint

A technology of fire-resistant latex and acrylic emulsion, applied in the field of latex paint, can solve the problems of latex paint application limitations, insufficient substrate protection, easy to fall off, etc., achieve excellent weather resistance, improve emulsification dispersion, and improve adhesion. Effect

Inactive Publication Date: 2015-11-18
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many types of latex paints on the market, and the production of fire-resistant latex paints has also reached a certain scale. However, in the latex paints produced by many fire-resistant latex paint manufacturers, there are generally insufficient flame retardancy and insufficient protection for the substrate. Disadvantages, it is easy to fall off during use, and the decoration is poor, which limits the application of latex paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of fireproof latex paint proposed by the present invention, its raw material comprises the following components by weight: 50 parts of acrylic emulsion, 40 parts of polyurethane emulsion, 10 parts of epoxy resin, 35 parts of flame retardant, 3 parts of expanded perlite, titanium dioxide 22 parts, 3 parts of nano-silica sol, 15 parts of silicon powder, 10 parts of nano-titanium dioxide, 8 parts of zinc trifluoroacetylacetonate, 2 parts of dodecafluoroheptyl methacrylate, 40 parts of film-forming aid, sorbitan monopalm 5 parts of acid ester, 10 parts of lauric acid, 1 part of defoamer, 2 parts of hydroxyethyl cellulose, 1 part of methyl ethyl ketone, 2 parts of N-phenyl-N'-cyclohexyl-p-phenylenediamine, lemon 1 part of potassium phosphate, 10 parts of dimethyl diallyl ammonium chloride, 60 parts of water;

[0022] Wherein, the flame retardant consists of 20 parts by weight of dimethyl phosphite, 25 parts by weight of methyl vinyl dichlorosilane, 3 parts by weight o...

Embodiment 2

[0025] A kind of fireproof latex paint that the present invention proposes, its raw material comprises the following components by weight: 80 parts of vinegar acrylic emulsion, 20 parts of polyurethane emulsion, 30 parts of novolac epoxy resins, 20 parts of flame retardants, 15 parts of expanded perlite, 10 parts of titanium dioxide, 10 parts of nano-silica sol, 8 parts of silicon powder, 25 parts of nano-titanium dioxide, 3 parts of zinc trifluoroacetylacetonate, 10 parts of dodecafluoroheptyl methacrylate, 3 parts of propylene glycol ether, ethylene glycol butyl ether 1 part, 2 parts of propylene glycol butyl ether, 1 part of turpentine, 0.6 parts of dipentene, 0.4 parts of decahydronaphthalene, 2 parts of benzyl alcohol, 4 parts of diisopropyl succinate, 1 part of diethylene glycol butyl ether acetate, 10 parts of sorbitan monopalmitate, 2 parts of lauric acid, 3 parts of defoamer, 1 part of hydroxyethyl cellulose, 5 parts of methyl ethyl ketone, N-phenyl-N'-cyclohexyltereph...

Embodiment 3

[0030] A kind of fireproof latex paint proposed by the present invention, its raw material comprises the following components by weight: 20 parts of pure acrylic emulsion, 30 parts of styrene-acrylic emulsion, 5 parts of silicon-acrylic emulsion, 13 parts of vinegar-acrylic emulsion, 32 parts of polyurethane emulsion, phenolic 25 parts of epoxy resin, 30 parts of flame retardant, 10 parts of expanded perlite, 20 parts of titanium dioxide, 7 parts of nano-silica sol, 12 parts of silicon powder, 20 parts of nano-titanium dioxide, 6 parts of zinc trifluoroacetylacetonate, methacrylic acid 8 parts of dodecafluoroheptyl ester, 8 parts of turpentine, 3 parts of dipentene, 3 parts of decahydronaphthalene, 4 parts of benzyl alcohol, 5 parts of diisopropyl succinate, 8 parts of sorbitan monopalmitate, lauryl 7.8 parts of acid, 2.3 parts of defoamer, 1.6 parts of hydroxyethyl cellulose, 4 parts of methyl ethyl ketone, 1.3 parts of N-phenyl-N'-cyclohexyl-p-phenylenediamine, 1.6 parts of p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention discloses fireproof emulsion paint. The fireproof emulsion paint comprises acrylic acid emulsion, polyurethane emulsion, epoxy resin, a fire retardant, expanded perlite, titanium dioxide, nanometer silica sol, silicon powder, nanometer titanium dioxide, zinc trifluoroacetylacetonate, dodecafluoroheptyl methacrylate, a film forming auxiliary agent, sorbitan monopalmitate, lauric acid, an antifoaming agent, hydroxyethyl cellulose, methyl ethyl ketone, N-phenyl-N'-cyclohexyl p-phenylenediamine, potassium citrate, dimethyldiallylammonium chloride and water. The fire retardant comprises dimethyl phosphite, methylvinyldichlorosilane, 3-aminopropyltriethoxysilane, 5-ethyl-5-butyl-2-chloro-1,3,2-dioxaphosphorinane, potassium tripolyphosphate, cetyl pyridinium bromide, decabromodiphenyl ethane, aluminum dihydrogen phosphate, calcium borate, melamine and cyanuric acid. The fireproof emulsion paint has excellent flame resistance, good fire retardancy, good adhesion to a base material and good decorative effects.

Description

technical field [0001] The invention relates to the technical field of latex paint, in particular to a fireproof latex paint. Background technique [0002] Latex paint is a water-dispersible paint. It is based on synthetic resin emulsion, and the filler is refined by adding various additives after grinding and dispersing. Latex paint has many advantages that are different from traditional wall paints, such as easy to paint, fast drying, water-resistant paint film, and good scrub resistance. At present, there are many types of latex paints on the market, and the production of fire-resistant latex paints has also reached a certain scale. However, in the latex paints produced by many fire-resistant latex paint manufacturers, there are generally insufficient flame retardancy and insufficient protection for the substrate. The disadvantage is that it is easy to fall off during use and has poor decoration, which limits the application of latex paint. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D133/04C09D125/14C09D131/04C09D175/04C09D163/04C09D5/18C09D5/02C09D5/08C09D7/12
Inventor 王和山朱建林赵欣泰
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com