A kind of bead-shaped ultra-high viscosity water-soluble cationic polymer and its preparation method

A water-soluble cation and polymer technology, applied in the field of polymer compound preparation, can solve the problems of unadjustable cation degree, affecting product quality, low intrinsic viscosity, etc., and achieve controllable reaction temperature, fast heat transfer, and intrinsic viscosity big effect

Active Publication Date: 2018-10-19
山东聚发生物科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the problems of its production process and formula, there will be a large amount of insoluble matter after it dissolves, which will affect the product quality
[0004] Existing bead polymers belong to the homopolymer of polydimethyldiallyl ammonium chloride. Due to the dispersant used and the operation problems of the production process, the product made has a large amount of insoluble matter and the viscosity is not enough. The product will seriously affect the printing and dyeing, daily chemical industry, etc.
[0005] The existing bead polymer belongs to the homopolymer of dimethyl diallyl ammonium chloride, the cationic degree cannot be adjusted, the intrinsic viscosity is low, and the application range is relatively narrow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Add 3 g of dimethylaminoethyl methacrylate: butyl methacrylate copolymer in a mass ratio of 3:5 into the reactor, and add 300 g of organic hydrocarbon solvent aviation kerosene at the same time, and then put it at room temperature ( 25°C) in a water bath, stir with a frequency conversion agitator, and at the same time fill the reaction system with nitrogen protection under the liquid surface;

[0027] (2) Add 150g of 65% dimethyl diallyl ammonium chloride solution to the water phase tank; 0.15g of chelating agent EDTA; 1.5g of initiator ammonium persulfate, 1.5g of sodium bisulfite; chain transfer agent phosphorous acid Sodium hydrogen 0.15g; stir evenly to obtain monomer phase.

[0028] (3) Control the temperature of the reactor at about 25°C, add the monomer phase prepared in the step, stir for 10 minutes, the stirring speed is 250r / min, adjust the nitrogen to the liquid surface and fill with nitrogen protection;

[0029] (4) Slowly raise the temperature to 60°C ...

Embodiment 2

[0033] (1) Add 5g of dispersant acrylic acid and methyl methacrylate copolymer into the reaction kettle, and add 500g of organic hydrocarbon solvent aviation kerosene at the same time, then put it in a water bath at room temperature (25°C), and use a frequency conversion agitator to Stir while filling the reaction system with nitrogen protection under the liquid surface;

[0034] (2) Add 142.5g of 65% dimethyl diallyl ammonium chloride solution, 7.5g of acrylamide, 0.25g of chelating agent EDTA, 2.5g of initiator ammonium persulfate, and 1g of sodium bisulfite into the water tank; Chain transfer agent sodium formate 0.25g; Stir evenly to obtain the monomer phase;

[0035] (3) Control the temperature of the reactor at about 30°C, add the monomer phase prepared in the step, stir for 15 minutes, the stirring speed is 250r / min, adjust the nitrogen to the liquid surface and fill with nitrogen protection;

[0036] (4) Slowly raise the temperature to 60°C and react for 5 hours. Afte...

Embodiment 3

[0040] (1) Add 1g of dispersant acrylic acid and butyl methacrylate copolymer into the reaction kettle, and add 200g of organic hydrocarbon solvent aviation kerosene at the same time, then put it in a water bath at room temperature (25°C), and use a frequency conversion agitator to Stir while filling the reaction system with nitrogen protection under the liquid surface;

[0041] (2) Add 135g of 65% dimethyl diallyl ammonium chloride solution, 15g of acrylamide; 0.05g of chelating agent EDTA; 1g of initiator ammonium persulfate, 1g of sodium bisulfite; Sodium hydrogen phosphite 0.05g; stir evenly to obtain monomer phase;

[0042] (3) Control the temperature of the reaction kettle at about 25°C, add the monomer phase prepared in the step, stir for 20 minutes, the stirring speed is 250r / min, adjust the nitrogen to the liquid surface and fill with nitrogen protection;

[0043] (4) Slowly raise the temperature to 65°C and react for 5 hours. After the reaction, stop filling nitroge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of preparation of high-molecular compounds, and particularly relates to a bead-shaped hyperviscosity water-soluble cationic polymer and a preparation method thereof. The preparation method of the bead-shaped hyperviscosity water-soluble cationic polymer adopts the technical scheme that the preparation method comprises the following steps of according to parts by mass, adding 1 to 5 parts of dispersant into a reaction kettle, adding 200 to 500 parts of organic hydrocarbon solvent of aviation kerosene, putting into a water bath pot at room temperature, stirring, and filling a nitrogen protection reaction system under liquid level. The bead-shaped hyperviscosity water-soluble cationic polymer has the advantages that the dissolving speed is high, the viscosity is high, the cationic degree can be adjusted, and the like; the bead-shaped hyperviscosity water-soluble cationic polymer is widely applied into water treatment, papermaking, petroleum production, textile printing and dyeing, daily chemical engineering, and the like.

Description

technical field [0001] The invention belongs to the technical field of preparation of macromolecular compounds, and in particular relates to a bead-like ultra-high viscosity water-soluble cationic polymer and a preparation method thereof. Background technique [0002] The existing industrial products of polydimethyldiallylammonium chloride and its cationic copolymers are mainly aqueous solution polymers and a small amount of powder polymer products. Aqueous solution polymer is mainly a product in which monomers are polymerized to a certain molecular weight and then diluted with water to a certain concentration. Because the product contains a large amount of water, it not only increases the packaging cost, but also increases the transportation cost; the powder polymer is mainly polymerized through the solution bulk. The product is processed in a pulverizing dryer, which is difficult to produce, high in cost, and cannot be mass-produced. The product is powdery and difficult to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F126/02C08F226/02C08F220/56C08F2/08
CPCC08F2/08C08F126/02C08F220/56C08F226/02
Inventor 彭程刘培宝刘洪楼
Owner 山东聚发生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap