A kind of plastering mortar and preparation method thereof

A technology for plastering mortar and feeding materials, applied in the field of building materials, can solve the problems of poor water retention and air permeability on the wall surface, reduce the strength of the wall body, damp mold on the wall body, etc., and achieve excellent mechanical properties and adhesion, excellent thermal insulation properties, resistance to The effect of grinding is not easy to pulverize

Active Publication Date: 2021-10-22
江苏省苏安能节能建材科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in coastal areas, especially in northern coastal areas, due to special climate factors, large temperature differences, strong and changeable winds, and humid air (high concentration of potassium, sodium, and chloride ions in sea breeze and seawater), conventional plastering mortar is used for construction Finally, the water retention and air permeability of the surface of the wall is poor, and the wall is easy to crack and peel off, resulting in mildew on the inner surface of the wall, which not only pollutes the environment, endangers personal health, reduces the strength of the wall, but also affects the appearance of the interior, which brings great harm to people's lives. to great trouble

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of plastering mortar and preparation method thereof
  • A kind of plastering mortar and preparation method thereof
  • A kind of plastering mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Composition of raw materials (parts by weight): 100 parts of polyurethane / epoxy resin / diatomite composite material, 15 parts of lime paste, 10 parts of 102 glue, 30 parts of mineral admixture, 70 parts of white Portland cement, carboxymethyl fiber 7 parts of styrene, 3 parts of styrene, 3 parts of chlorine salt antifreeze, 4 parts of polycarboxylate water reducer, 5 parts of gelatin, 3 parts of sodium dodecylbenzene sulfonate, 5 parts of polyethylene glycol 4000 and 200 parts of water.

[0052] Mineral admixtures include (parts by weight): 15 parts of finely ground blast furnace slag, 5 parts of bentonite, 7 parts of heavy calcium carbonate, 3 parts of talcum powder, 10 parts of basalt, 3 parts of washed sand, 20 parts of polyethylene glycol 400, 100 parts of water.

[0053] The mineral admixture is prepared by the following method: step 1, further pulverize the ground blast furnace slag, bentonite, basalt, washed sand, and heavy calcium carbonate through the feeding s...

Embodiment 2

[0065] Raw material composition (parts by weight): 150 parts of polyurethane / epoxy resin / diatomite composite material, 20 parts of lime paste, 15 parts of 102 glue, 40 parts of mineral admixture, 120 parts of Portland cement, carboxymethyl cellulose 12 parts, 10 parts of styrene, 5 parts of chlorine salt anti-rust antifreeze, 7 parts of sulfamate-based water reducer, 10 parts of gelatin, 5 parts of sodium dodecylbenzene sulfonate, polyethylene glycol 4000 15 parts parts and 300 parts of water.

[0066] Mineral admixtures include (parts by weight): 30 parts of finely ground blast furnace slag, 10 parts of bentonite, 12 parts of heavy calcium carbonate, 10 parts of talcum powder, 15 parts of basalt, 7 parts of washed sand, 30 parts of polyethylene glycol 400, 120 parts of water.

[0067] The mineral admixture is prepared by the following method: the finely ground blast furnace slag, bentonite, basalt, washed sand, heavy calcium carbonate are further ground and pulverized throug...

Embodiment 3

[0079] Composition of raw materials (parts by weight): 125 parts of polyurethane / epoxy resin / diatomite composite material, 17 parts of lime paste, 12 parts of 102 glue, 35 parts of mineral admixture, 100 parts of composite Portland cement, carboxymethyl fiber 10 parts of styrene, 6 parts of styrene, 4 parts of chlorine-free salt antifreeze, 5 parts of melamine-based water reducer, 7 parts of gelatin, 4 parts of sodium dodecylbenzenesulfonate, 10 parts of polyethylene glycol 4000 and 250 parts of water.

[0080] Mineral admixtures include (parts by weight): 22 parts of finely ground blast furnace slag, 7 parts of bentonite, 10 parts of heavy calcium carbonate, 6 parts of talcum powder, 12 parts of basalt, 5 parts of washed sand, 25 parts of polyethylene glycol 400, 110 parts of water.

[0081] The mineral admixture is prepared by the following method: the finely ground blast furnace slag, bentonite, basalt, washed sand, heavy calcium carbonate are further ground and pulverized...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention proposes a plastering mortar, which is prepared by weight from the following raw materials: 100-150 parts of polyurethane / epoxy resin / diatomite composite material, 15-20 parts of lime paste, 10-15 parts of 102 glue, mineral 30-40 parts of admixture, 70-120 parts of Portland cement, 7-12 parts of carboxymethyl cellulose, 3-10 parts of styrene, 3-5 parts of antifreeze, 4-7 parts of water reducer, gelatin 5‑10 parts, 3‑5 parts of sodium dodecylbenzenesulfonate, 5‑15 parts of polyethylene glycol 4000 and 200‑300 parts of water. The invention has good cohesiveness, high strength, strong waterproof ability, good moisture-proof, powder-repelling and crack-proof effects, simple preparation method, low cost, easy popularization and broad application prospects.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a plastering mortar and a preparation method thereof. Background technique [0002] Mortar is a commonly used building material, generally used in masonry and plastering works. Mortar is made by mixing cementitious materials (cement, lime, clay, etc.) and fine aggregate (sand) with water. According to the composition materials, it can be divided into: ①Gypsum mortar: made of lime paste, sand and water according to a certain ratio, generally used for masonry and plastering layers that do not require high strength and are not subject to moisture; ②Cement mortar: made of Cement, sand and water are made according to a certain ratio, and are generally used for masonry, walls or floors in wet environments or in water; ③Mixed mortar: Add appropriate admixtures such as fly ash, It is made of diatomite to save the amount of cement or lime and improve the workability of mortar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/10
CPCC04B28/10C04B2111/00482C04B24/14C04B18/022C04B24/2652C04B18/023C04B7/02C04B24/383C04B24/00C04B2103/601C04B2103/302C04B24/20C04B24/32
Inventor 周锦峰
Owner 江苏省苏安能节能建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com